The effects of Sr addition on microstructures and tensile properties of the as-cast and hot-extruded AZ80 alloys were studied by OM, SEM, EDS, XRD, DSC and Instron tester. The results show that the microstructures of ...The effects of Sr addition on microstructures and tensile properties of the as-cast and hot-extruded AZ80 alloys were studied by OM, SEM, EDS, XRD, DSC and Instron tester. The results show that the microstructures of as-cast alloys consist of α-Mg and β-Mg17Al12 phase. Sr gathers on the boundaries, and dissolves into β-Mg17Al12 phase or forms Mg17Sr2 phase. The grains of as-cast alloys are refined and discontinuous net-shaped structure is formed. The compound phases on the boundaries become thicker with increasing Sr content. The ultimate tensile stress(UTS) and elongation are improved compared with the corresponding Sr-free alloy. After preliminary hot-extruding, the UTS is up to 308?320 MPa and elongation reaches 8.0%?13.5%. After double hot-extrusion, the dynamic recrystallization completes totally, and the UTS is up to 310?355 MPa, but the elongation does not change apparently. The alloy with 0.02%Sr (mass fraction) obtains the best comprehensive performance with the UTS of 355 MPa and elongation of 13.2%. The SEM morphology of fracture surface shows that the alloys with Sr present good ductility after double hot-extrusion.展开更多
基金Project(50571092) supported by the National Natural Science Foundation of China
文摘The effects of Sr addition on microstructures and tensile properties of the as-cast and hot-extruded AZ80 alloys were studied by OM, SEM, EDS, XRD, DSC and Instron tester. The results show that the microstructures of as-cast alloys consist of α-Mg and β-Mg17Al12 phase. Sr gathers on the boundaries, and dissolves into β-Mg17Al12 phase or forms Mg17Sr2 phase. The grains of as-cast alloys are refined and discontinuous net-shaped structure is formed. The compound phases on the boundaries become thicker with increasing Sr content. The ultimate tensile stress(UTS) and elongation are improved compared with the corresponding Sr-free alloy. After preliminary hot-extruding, the UTS is up to 308?320 MPa and elongation reaches 8.0%?13.5%. After double hot-extrusion, the dynamic recrystallization completes totally, and the UTS is up to 310?355 MPa, but the elongation does not change apparently. The alloy with 0.02%Sr (mass fraction) obtains the best comprehensive performance with the UTS of 355 MPa and elongation of 13.2%. The SEM morphology of fracture surface shows that the alloys with Sr present good ductility after double hot-extrusion.