The effects of sub-transus(α+β)annealing treatment(ST),followed by single aging(SA)or duplex aging(DA)on the microstructural evolution and mechanical properties of near-βTi-4Al-1Sn-2Zr-5Mo-8V-2.5Cr(mass fraction,%)...The effects of sub-transus(α+β)annealing treatment(ST),followed by single aging(SA)or duplex aging(DA)on the microstructural evolution and mechanical properties of near-βTi-4Al-1Sn-2Zr-5Mo-8V-2.5Cr(mass fraction,%)alloy were investigated using optical microscopy,scanning electron microscopy,and transmission electron microscopy.The results show that the finer secondaryαphase precipitates in the alloy after DA than SA(e.g.,149 nm for SA and 69 nm for DA,both after ST at 720℃).The main reason is that the pre-aging step(300℃)in the DA process leads to the formation of intermediateωphase nanoparticles,which assist in the nucleation of the acicular secondaryαphase precipitates.In addition,the strength of the alloy after DA is higher than that of SA at the specific ST temperature.A good combination is achieved in the alloy subjected to ST at 750℃,followed by DA(UTS:1450 MPa,EL:3.87%),which is due to the precipitation of nanoscale secondaryαphase by DA.In conclusion,DA is a feasible process for this new near-βtitanium alloy.展开更多
基金supported by the SJTU-GM Collaborative Research Laboratory Jointly Established by General Motors Global Research and Development(GM R&D)Research was Supported by National Key Research and Development Program of China(2016YFB0301000)+2 种基金Shanghai Rising-Star Program(15QB1402700)National Natural Science Foundation of China(NSFC)(51671128&51771113)Special Fund of Jiangsu Province(BA2016039).
基金the financial supports from the Key Research and Development Program of Shanxi Province,China(Nos.201903D421084,201903D121056)the National Natural Science Foundation of China(Nos.52171122,52071228,51901151)。
文摘The effects of sub-transus(α+β)annealing treatment(ST),followed by single aging(SA)or duplex aging(DA)on the microstructural evolution and mechanical properties of near-βTi-4Al-1Sn-2Zr-5Mo-8V-2.5Cr(mass fraction,%)alloy were investigated using optical microscopy,scanning electron microscopy,and transmission electron microscopy.The results show that the finer secondaryαphase precipitates in the alloy after DA than SA(e.g.,149 nm for SA and 69 nm for DA,both after ST at 720℃).The main reason is that the pre-aging step(300℃)in the DA process leads to the formation of intermediateωphase nanoparticles,which assist in the nucleation of the acicular secondaryαphase precipitates.In addition,the strength of the alloy after DA is higher than that of SA at the specific ST temperature.A good combination is achieved in the alloy subjected to ST at 750℃,followed by DA(UTS:1450 MPa,EL:3.87%),which is due to the precipitation of nanoscale secondaryαphase by DA.In conclusion,DA is a feasible process for this new near-βtitanium alloy.