Ferritic steel with a nominal composition of Fe-14Cr-3W-0.42Ti-0.32Y was prepared by mixing gas-atomized prealloyed powder and mechanically alloyed powder. The microstructure is much different fxom other ferritic stee...Ferritic steel with a nominal composition of Fe-14Cr-3W-0.42Ti-0.32Y was prepared by mixing gas-atomized prealloyed powder and mechanically alloyed powder. The microstructure is much different fxom other ferritic steels with the same composition and prepared via only mechanically alloyed powder. A bi-modal structure, which consists of pure ferritic grains and martensitic grains, was obtained after hot forging and air cooling. A phase transformation of αbcc→γfcc→α＇bcc was also discovered in microstructural observation. The bi-modal microstructure shows a good combination of high strength and high ductility.展开更多
基金Projects (50634060,50721003) supported by the National Natural Science Foundation of ChinaProject (2009AA03Z526) supported by the High-tech Research and Development Program of ChinaProject supported by the Open-End Fund for Valuable and Precision Instruments of Central South University
文摘Ferritic steel with a nominal composition of Fe-14Cr-3W-0.42Ti-0.32Y was prepared by mixing gas-atomized prealloyed powder and mechanically alloyed powder. The microstructure is much different fxom other ferritic steels with the same composition and prepared via only mechanically alloyed powder. A bi-modal structure, which consists of pure ferritic grains and martensitic grains, was obtained after hot forging and air cooling. A phase transformation of αbcc→γfcc→α＇bcc was also discovered in microstructural observation. The bi-modal microstructure shows a good combination of high strength and high ductility.