Effect of isothermal holding treatment in the solidification process on the microstructure of Ti-6Al-4V alloy was studied by temperature controlled induced melting apparatus. The result shows that with isothermal hold...Effect of isothermal holding treatment in the solidification process on the microstructure of Ti-6Al-4V alloy was studied by temperature controlled induced melting apparatus. The result shows that with isothermal holding treatment above the β transus temperature during solidification, the colony structure consisting of parallel lamellae was obtained. While the isothermal holding treatment was set at 960 °C, a unique bi-modal microstructure consisting of coarse primary α and fine secondary lamellar α was obtained. The primary lamellar α tended to break into several pieces, globularize and present equiaxed morphology. The formation mechanism of the equiaxed α can be explained with the atom immigration, high density dislocations, combined action with the interface tension of formed α phase during the isothermal holding treatment. After the isothermal holding, the retained β matrix transformed into fine lamellar α, thus, bi-modal microstructure was acquired. Compared with the lamellar structure, the grain boundary α presented discontinuously and cannot be distinguished from the primary α lamellae easily. The size of colonies α was greatly decreased. The microstructure tended to be much more homogeneous in the whole section of the samples.展开更多
基金Project(3102014JCQ01026)supported by the Fundamental Research Fund for the Central Universities,ChinaProject(B08040)supported by the Program of Introducing Talents of Discipline to Universities,China
文摘Effect of isothermal holding treatment in the solidification process on the microstructure of Ti-6Al-4V alloy was studied by temperature controlled induced melting apparatus. The result shows that with isothermal holding treatment above the β transus temperature during solidification, the colony structure consisting of parallel lamellae was obtained. While the isothermal holding treatment was set at 960 °C, a unique bi-modal microstructure consisting of coarse primary α and fine secondary lamellar α was obtained. The primary lamellar α tended to break into several pieces, globularize and present equiaxed morphology. The formation mechanism of the equiaxed α can be explained with the atom immigration, high density dislocations, combined action with the interface tension of formed α phase during the isothermal holding treatment. After the isothermal holding, the retained β matrix transformed into fine lamellar α, thus, bi-modal microstructure was acquired. Compared with the lamellar structure, the grain boundary α presented discontinuously and cannot be distinguished from the primary α lamellae easily. The size of colonies α was greatly decreased. The microstructure tended to be much more homogeneous in the whole section of the samples.