We have successfully employed metal-organic chemical vapor deposition （MOCVD） technique to simultaneously deposit double-sided YBa2Cu3O7-δ （YBCO） films on both sides of YzO3/yttria-stabilized zirconia （YSZ）/Ce...We have successfully employed metal-organic chemical vapor deposition （MOCVD） technique to simultaneously deposit double-sided YBa2Cu3O7-δ （YBCO） films on both sides of YzO3/yttria-stabilized zirconia （YSZ）/CeO2 （YYC） buffered biaxially textured Ni-5 at.% W substrates, which is of great prospect to cut the production cost of YBCO coated conductors. X-ray diffraction analysis revealed that both sides of YBCO film were purely c-axis oriented and highly textured. The co-scan of （005） YBCO and Ф-scan of （103） YBCO yielded full width at half maximum （FWHM） values of 4.9° and 6.6° for one side of double-sided YBCO film, respectively, as well as 4.4° and 6.4° for the other side. The current transportation measurements performed on such double-sided 500 nm-thickness YBCO films showed the self-field critical current density （Jc） at 77 K of 0.6 MA/cm^2 and 1.2 MA/cm^2, respectively. Further research is in the process of exploring new solution to improve the Jc in practice.展开更多
基金supported by the National Natural Science Foundation of China(Grant No.51002024)Sichuan Youth Science and Technology Innovation Research Team Funding(Grant No.2011JTD0006)Fundamental Research Funds for the Central Universities(Grant Nos.ZYGX2012J039 and ZYGX2011Z002)
文摘We have successfully employed metal-organic chemical vapor deposition （MOCVD） technique to simultaneously deposit double-sided YBa2Cu3O7-δ （YBCO） films on both sides of YzO3/yttria-stabilized zirconia （YSZ）/CeO2 （YYC） buffered biaxially textured Ni-5 at.% W substrates, which is of great prospect to cut the production cost of YBCO coated conductors. X-ray diffraction analysis revealed that both sides of YBCO film were purely c-axis oriented and highly textured. The co-scan of （005） YBCO and Ф-scan of （103） YBCO yielded full width at half maximum （FWHM） values of 4.9° and 6.6° for one side of double-sided YBCO film, respectively, as well as 4.4° and 6.4° for the other side. The current transportation measurements performed on such double-sided 500 nm-thickness YBCO films showed the self-field critical current density （Jc） at 77 K of 0.6 MA/cm^2 and 1.2 MA/cm^2, respectively. Further research is in the process of exploring new solution to improve the Jc in practice.