The effect of current on the morphology of Al alloy T-joint in double-pulsed metal inert gas（DP-MIG） welding process was investigated by simulation and experiment.A three-dimensional finite element model and the DP-...The effect of current on the morphology of Al alloy T-joint in double-pulsed metal inert gas（DP-MIG） welding process was investigated by simulation and experiment.A three-dimensional finite element model and the DP-MIG heat source of double-ellipsoidal volumetric model were developed to simulate the temperature and stress fields under different welding conditions.The macro-morphology and microstructure of welding joints at the corresponding currents were observed in the experiment.The results show that the best condition is at an average current of 90 A and current difference of 40 A,when the maximum temperature is 200 °C higher than the fusion points,with the temperature difference of about 100 °C and stress change of 10 MPa between thermal pulse and thermal base.Under these conditions,Al alloy T-joint with proper fusion condition has smooth fish-scale welding appearance and finer microstructure.Furthermore,the thermal curves and stress distribution in the experiment are consistent with those in the simulation,verifying the precision of the welding simulation.展开更多
The T-joints of Ti?6Al?4V alloy were manufactured by double-sided synchronized laser beam welding with the homologous filler wire. The formation, microstructure and mechanical properties of welded joints as well as th...The T-joints of Ti?6Al?4V alloy were manufactured by double-sided synchronized laser beam welding with the homologous filler wire. The formation, microstructure and mechanical properties of welded joints as well as the correlations of each other were investigated. The results indicate that the quality of weld seams is good without defects such as discontinuity, beading, visible cracks or porosity, which is linked to the steady molten pool behavior and droplet transition. The morphologies of the heat affected zone (HAZ) located on the skin and stringer are disparate. The microstructure of the HAZ and fusion zone (FZ) is mainly comprised of acicular martensiticα′ phases. The microhardness of the HAZ and FZ is higher than that of the base metal (BM) and reaches a maximum value at the HAZ near FZ on the stringer. The tensile specimens along the skin and stringer fractured at the BM with ductile fracture surfaces.展开更多
基金Project(51475156)supported by the National Natural Science Foundation of China
文摘The effect of current on the morphology of Al alloy T-joint in double-pulsed metal inert gas（DP-MIG） welding process was investigated by simulation and experiment.A three-dimensional finite element model and the DP-MIG heat source of double-ellipsoidal volumetric model were developed to simulate the temperature and stress fields under different welding conditions.The macro-morphology and microstructure of welding joints at the corresponding currents were observed in the experiment.The results show that the best condition is at an average current of 90 A and current difference of 40 A,when the maximum temperature is 200 °C higher than the fusion points,with the temperature difference of about 100 °C and stress change of 10 MPa between thermal pulse and thermal base.Under these conditions,Al alloy T-joint with proper fusion condition has smooth fish-scale welding appearance and finer microstructure.Furthermore,the thermal curves and stress distribution in the experiment are consistent with those in the simulation,verifying the precision of the welding simulation.
基金Project supported by Science and Technology on Power Beam Processes Laboratory at Beijing Aeronautical Manufacturing Technology Research Institute,China
文摘The T-joints of Ti?6Al?4V alloy were manufactured by double-sided synchronized laser beam welding with the homologous filler wire. The formation, microstructure and mechanical properties of welded joints as well as the correlations of each other were investigated. The results indicate that the quality of weld seams is good without defects such as discontinuity, beading, visible cracks or porosity, which is linked to the steady molten pool behavior and droplet transition. The morphologies of the heat affected zone (HAZ) located on the skin and stringer are disparate. The microstructure of the HAZ and fusion zone (FZ) is mainly comprised of acicular martensiticα′ phases. The microhardness of the HAZ and FZ is higher than that of the base metal (BM) and reaches a maximum value at the HAZ near FZ on the stringer. The tensile specimens along the skin and stringer fractured at the BM with ductile fracture surfaces.