Al-Cu-Mg合金单晶应力时效析出相取向分布效应

基于实验室自制的Al-1.2Cu-0.5Mg合金单晶材料,开展了不同应力水平下的应力时效试验和相应的透射电镜组织分析(TEM),并结合3种不同理论模型模拟研究了Al-1.2Cu-0.5Mg单晶经压缩应力时效和人工时效后析出相的分布规律与析出相取向分布作用机制。结果表明:在压应力作用下,Al-1.2Cu-0.5Mg合金单晶的时效析出相出现了显著的取向分布规律,且具有不同晶体取向的单晶在同样的压应力作用下时效后析出相分布取向程度差别明显;3种理论模型中,同时考虑应力与位错耦合作用的模型预测结果与实测结果相符,证明析出相的取向效应既有析出相-应力弹性交互作用促进机制,也有促进析出相均匀形核的位错抑制机制。

Effect of normalizing cooling process on microstructure and precipitates in low-temperature silicon steel

Microstructure, precipitate and magnetic characteristic of fmal products with different normalizing cooling processes for Fe-3.2%Si low-temperature hot-rolled grain-oriented silicon steel were analyzed and compared with the hot-rolled plate by optical microscopy （OM）, transmission electron microscopy （TEM）, and energy dispersive spectrometry （EDS）. The results show that, the surface microstructure is uniform, the proportion of recrystallization in matrix increases, and the banding textures are narrowed; the precipitates, whose quantity in normalized plate is more than that in hot-rolled plate greatly, are mainly A1N, MnS, composite precipitates （Cu,Mn）S and so on. Normalizing technology with a temperature of 1120 ℃, holding for 3 min, and a two-stage cooling is a most advantaged method to obtain oriented silicon steel with sharper Goss texture and higher magnetic properties, owing to the uniform surface microstructures and the obvious inhomogeneity of microstructures along the thickness. The normalizing technology with the two-stage cooling is the optimum process, which can generate more fine precipitates dispersed over the matrix, and be beneficial for finished products to get higher magnetic properties.

Effect of crystal orientations and precipitates on corrosion behavior of Al-Cu-Li single crystals

The effect of the crystal orientations and precipitates on the corrosion behavior of Al-Cu-Li single crystals was studied by scanning electron microscopy, transmission electron microscopy, optical microscopy, immersion testing in exfoliation corrosion solution, and electrochemical testing. The results show that the corrosion rates of different orientations of the aged Al-Cu-Li alloy increase in the order of (001) 1 phase deteriorated the corrosion resistance of the Al-Cu-Li alloy, and the degree of deterioration differed in different crystal plane orientations. The severe localized corrosion of the aged alloy propagates along the crystallography and extends along the {111}Alplane in the form of corrosion bands.

Synergistic effect of orientation and temperature on slip behavior and precipitation behavior of Al−Cu−Li single crystals

The slip behavior and precipitation behavior of four Al−Cu−Li single crystals with varying orientations at different temperatures were investigated using electron backscattering diffraction(EBSD)and transmission electron microscopy(TEM).The maximum differences in yield strength and ductility of the single crystals at room temperature are 41.6%and 14.7%,respectively.This indicates that the mechanical properties are strongly influenced by the crystal orientation.Moreover,grains with varying orientations exhibit distinct slip characteristics,including slip homogenization,slip localization,and multiple slip.In single crystal SC1,slip localization primarily contributes to its inferior ductility compared to other grains.Nevertheless,during deformation at 250℃,the distinct morphology and distribution of precipitates in the crystals are also correlated with orientation,which causes the increase in the maximum elongation difference to 20.8%in all selected single crystals.Notably,SC1,with a precipitate volume fraction of 2.65%,exhibits more severe slip localization compared to room temperature conditions,while SC2,with a precipitate volume fraction of 4.79%,demonstrates cross-slip characteristics,significantly enhancing the plastic deformation capacity of the Al−Cu−Li alloy.