Microstructural evolution of AZ91 magnesium alloy was investigated during homogenizing annealing treatment, hot extrusion and ageing treatment, respectively. The results exhibited that both the divorced eutectic β-Mg...Microstructural evolution of AZ91 magnesium alloy was investigated during homogenizing annealing treatment, hot extrusion and ageing treatment, respectively. The results exhibited that both the divorced eutectic β-Mg17Al12 and the precipitated β-Mg17Al12 phases appeared in the as-cast alloy. The β-Mg17Al12 phase dissolved into α-Mg matrix mostly and the structure kept fine after the optimized homogenization treatment at 380 °C for 15 h. Dynamic recrystallization and consequent grain refinement occurred during extrusion. The banded β-Mg17Al12 precipitates paralleled to the extrusion direction were observed after ageing treatment. The banded precipitation should be attributed to the solidification segregation which was elongated during the subsequent extrusion. Furthermore, the effects of temperature, holding time of homogenization and ageing treatment, and extrusion processing parameters on the microstructural evolution of AZ91 alloy were also discussed in details according to the experimental results.展开更多
Pre-compression and heat treatment were performed on an extruded AZ31 Mg alloy,and their effects on subsequent deformation behavior were investigated.The results show that at low temperature annealing(170 ℃ for 4 h),...Pre-compression and heat treatment were performed on an extruded AZ31 Mg alloy,and their effects on subsequent deformation behavior were investigated.The results show that at low temperature annealing(170 ℃ for 4 h),the extruded samples with and without annealing exhibit a nearly equivalent yield stress(~148 MPa) because their microstructures are nearly unchanged.However,under the same annealing condition,the yield stress of sample with pre-twinning and subsequent annealing(~225 MPa) is higher than that of the pre-twinned one(~200 MPa).The former sample presents a hardening effect because the solute atoms segregated on twin boundaries lead to a strengthening effect.The pre-twinned sample annealed at 400 ℃ for 1 h shows a higher ultimate elongation(~28%) than the pre-twinned one(~15%),but its yield stress(~125 MPa) is much lower than that of the pre-twinned one(~200 MPa).展开更多
基金Project (2011A090200104) supported by Guangdong Science and Technology Special Projects, China
文摘Microstructural evolution of AZ91 magnesium alloy was investigated during homogenizing annealing treatment, hot extrusion and ageing treatment, respectively. The results exhibited that both the divorced eutectic β-Mg17Al12 and the precipitated β-Mg17Al12 phases appeared in the as-cast alloy. The β-Mg17Al12 phase dissolved into α-Mg matrix mostly and the structure kept fine after the optimized homogenization treatment at 380 °C for 15 h. Dynamic recrystallization and consequent grain refinement occurred during extrusion. The banded β-Mg17Al12 precipitates paralleled to the extrusion direction were observed after ageing treatment. The banded precipitation should be attributed to the solidification segregation which was elongated during the subsequent extrusion. Furthermore, the effects of temperature, holding time of homogenization and ageing treatment, and extrusion processing parameters on the microstructural evolution of AZ91 alloy were also discussed in details according to the experimental results.
基金Project(XDJK2013C106)supported by the Fundamental Research Funds for the Central Universities of ChinaProject(51201140)supported by the National Natural Science Foundation of China
文摘Pre-compression and heat treatment were performed on an extruded AZ31 Mg alloy,and their effects on subsequent deformation behavior were investigated.The results show that at low temperature annealing(170 ℃ for 4 h),the extruded samples with and without annealing exhibit a nearly equivalent yield stress(~148 MPa) because their microstructures are nearly unchanged.However,under the same annealing condition,the yield stress of sample with pre-twinning and subsequent annealing(~225 MPa) is higher than that of the pre-twinned one(~200 MPa).The former sample presents a hardening effect because the solute atoms segregated on twin boundaries lead to a strengthening effect.The pre-twinned sample annealed at 400 ℃ for 1 h shows a higher ultimate elongation(~28%) than the pre-twinned one(~15%),but its yield stress(~125 MPa) is much lower than that of the pre-twinned one(~200 MPa).