The phase morphology evolution during the solid solution treatment and then artificial aging of the La-modified ZL107 Al alloy was studied. The results show that when the solid solution was held at 560 ℃ for 6 h, onl...The phase morphology evolution during the solid solution treatment and then artificial aging of the La-modified ZL107 Al alloy was studied. The results show that when the solid solution was held at 560 ℃ for 6 h, only partial Si phase dissolved into the matrix; however, the precipitation also occurred during the artificial aging process. The precipitation process in Al-Si alloys with or without La-modification was compared. After modification and heat treatment, the mechanical properties of the alloy were greatly enhanced, due to the modification and uniform distribution of Si phase.展开更多
Vacuum sintering and ball milling methods were employed in the preparation process of Ti-C grain refine- ment and the ability of refiners with varying ratios of Ti and C to refine ZL111 crystal grains was tested. The ...Vacuum sintering and ball milling methods were employed in the preparation process of Ti-C grain refine- ment and the ability of refiners with varying ratios of Ti and C to refine ZL111 crystal grains was tested. The refinement effect of the Ti-C ratios on tensile strength, elongation percentage, Brinell hardness, pro-eutectoid αAl and the size of the Si phase of ZL111, after modification by rare-earth and strontium nitrate, were studied by means of metallographic examination, SEM and mechanical property tests. The results show that there is an obvious increase in the tensile strength and elongation percentage of refined ZL111 with these new Ti and C refiner compounding powders, while Brinell hardness remained more or less constant. The pro-eutectoid αAl is considerably reduced in size and the Si phase shows a finer and rounder structure. The refiner exhibits a good grain refining performance when the Ti-C ratio is 25:1, for Al crystals can favorably easily form nuclei and grow up along the TiC surface thanks to the TiAl3 generated by sur- plus Ti and Al. The mechanical properties have clearly been improved by the addition of strontium nitrate to ZL111. The effective factors in the modification of mechanical properties of ZL111 are in order of importance: strontium nitrate, Ti-C ratio and rare earth.展开更多
The solidification microstructure,fracture morphologies,and mechanical properties of an Al-18Si alloy and alloys modified with Al-5Ti and Al-3P master alloys were investigated using an optical microscope,scanning elec...The solidification microstructure,fracture morphologies,and mechanical properties of an Al-18Si alloy and alloys modified with Al-5Ti and Al-3P master alloys were investigated using an optical microscope,scanning electron microscope,and an electronic universal testing machine.The results show that additions of Al-5Ti and Al-3P have significant effects on the size and area fraction of the primary Si and the mechanical properties of the Al-18Si alloy.Compared to the Al-18Si alloy modified with 0.6 wt%Al-5Ti at 850°C,when the Al-18Si alloy was modified with 0.3 wt%Al-5Ti and 0.5 wt%Al-3P at the same temperature,the average size of the primary Si decreased from 39 to 14μm and the area fraction increased from 9.5%to 11.6%.The biggest influencing factor on the tensile strength and elongation of the Al-18Si alloy is the addition of Al-3P,followed by the modification temperature and the addition of Al-5Ti.At a modification temperature of 850°C,the tensile strength and elongation of the Al-18Si alloy modified with 0.3 wt%Al-5Ti+0.5 wt%Al-3P increased by 19.6%and 88.6%,respectively compared to that of the Al-18Si alloy modified with 0.6 wt%Al-5Ti.展开更多
基金Project (50671083) supported by the National Natural Science Foundation of ChinaProject (09102008) supported by Key Laboratory of Ministry of Education for Conveyance and Equipment (East China Jiaotong University)Project (20114BAB216015) supported by the Natural Science Foundation of Jiangxi Province, China
文摘The phase morphology evolution during the solid solution treatment and then artificial aging of the La-modified ZL107 Al alloy was studied. The results show that when the solid solution was held at 560 ℃ for 6 h, only partial Si phase dissolved into the matrix; however, the precipitation also occurred during the artificial aging process. The precipitation process in Al-Si alloys with or without La-modification was compared. After modification and heat treatment, the mechanical properties of the alloy were greatly enhanced, due to the modification and uniform distribution of Si phase.
文摘Vacuum sintering and ball milling methods were employed in the preparation process of Ti-C grain refine- ment and the ability of refiners with varying ratios of Ti and C to refine ZL111 crystal grains was tested. The refinement effect of the Ti-C ratios on tensile strength, elongation percentage, Brinell hardness, pro-eutectoid αAl and the size of the Si phase of ZL111, after modification by rare-earth and strontium nitrate, were studied by means of metallographic examination, SEM and mechanical property tests. The results show that there is an obvious increase in the tensile strength and elongation percentage of refined ZL111 with these new Ti and C refiner compounding powders, while Brinell hardness remained more or less constant. The pro-eutectoid αAl is considerably reduced in size and the Si phase shows a finer and rounder structure. The refiner exhibits a good grain refining performance when the Ti-C ratio is 25:1, for Al crystals can favorably easily form nuclei and grow up along the TiC surface thanks to the TiAl3 generated by sur- plus Ti and Al. The mechanical properties have clearly been improved by the addition of strontium nitrate to ZL111. The effective factors in the modification of mechanical properties of ZL111 are in order of importance: strontium nitrate, Ti-C ratio and rare earth.
基金Project(51571039) supported by the National Natural Science Foundation of China
文摘The solidification microstructure,fracture morphologies,and mechanical properties of an Al-18Si alloy and alloys modified with Al-5Ti and Al-3P master alloys were investigated using an optical microscope,scanning electron microscope,and an electronic universal testing machine.The results show that additions of Al-5Ti and Al-3P have significant effects on the size and area fraction of the primary Si and the mechanical properties of the Al-18Si alloy.Compared to the Al-18Si alloy modified with 0.6 wt%Al-5Ti at 850°C,when the Al-18Si alloy was modified with 0.3 wt%Al-5Ti and 0.5 wt%Al-3P at the same temperature,the average size of the primary Si decreased from 39 to 14μm and the area fraction increased from 9.5%to 11.6%.The biggest influencing factor on the tensile strength and elongation of the Al-18Si alloy is the addition of Al-3P,followed by the modification temperature and the addition of Al-5Ti.At a modification temperature of 850°C,the tensile strength and elongation of the Al-18Si alloy modified with 0.3 wt%Al-5Ti+0.5 wt%Al-3P increased by 19.6%and 88.6%,respectively compared to that of the Al-18Si alloy modified with 0.6 wt%Al-5Ti.