LaFeO3 perovskite supported Ni and Ni-Fe catalysts were prepared and applied to methanation reaction of syngas. Two preparation methods were employed. One was one-step citrate complexing method, and the other was a tw...LaFeO3 perovskite supported Ni and Ni-Fe catalysts were prepared and applied to methanation reaction of syngas. Two preparation methods were employed. One was one-step citrate complexing method, and the other was a two step method using citrate complexing method to produce LaFeO3 and followed by loading nickel oxide on it with impregnation. The structure evolution of the sample as prepared was investigated by XRD, TPR and TEM techniques. For the former, the chemical composites of the calcined sample are NiO-Fe2O3/LaFe1-xNixO3. After reduction and reaction of CO methanation, its composites convert to Fe-Ni@Ni/LaFeO3-La2O2CO3, in which Fe-Ni@Ni is metal particles in nano-size composed of nickel core and Fe-Ni alloy shell. For the latter, the chemical composites of the calcined sample are NiO/LaFeO3; and after reduction and reaction of CO methanation, its chemical composites change to Ni/LaFeO3. Ni/LaFeO3 catalyst is a little more active, while Fe-Ni@Ni/LaFeO3-La2O2CO3 is much more stable and shows very good resistance to carbon deposition. In this work it is aimed to show that the structure and composites of the catalysts can be tailored using perovskite-type oxide as precursor with different preparing method or preparing condition. Therefore, it is a promising route to prepare supported bi-metal catalysts in nano-size for a lot of metals with desired catalytic performances.展开更多
The preparation process of amorphous nanometer boron powders through combustion synthesis was investigated, and the effects of the reactant ratio, the heating agent and the milling rate on the activity and particle si...The preparation process of amorphous nanometer boron powders through combustion synthesis was investigated, and the effects of the reactant ratio, the heating agent and the milling rate on the activity and particle size of amorphous boron powders were studied. The results show that the boron powders exist in the form of an amorphous phase which has the crystallinity lower than 30.4%, and the panicle size of boron powder decreases with an increase of the high-energy ball milling rate. The purity of amorphous boron powder is 94.8% and panicle sizes are much smaller than 100 nm when the mass ratio of B2O3/Mg/KClO3 is 100：105：17 and the ball milling time is 20 min with the milling rate of 300 r/min. At the same time, the amorphous boron nano-fibers appear in the boron powders.展开更多
基金supported by the Financial support from the NSF of China(21066007)the NSF of Tianjin China(10JCZDJC23800)the NSF of Mongolia China(2009BS0203)
文摘LaFeO3 perovskite supported Ni and Ni-Fe catalysts were prepared and applied to methanation reaction of syngas. Two preparation methods were employed. One was one-step citrate complexing method, and the other was a two step method using citrate complexing method to produce LaFeO3 and followed by loading nickel oxide on it with impregnation. The structure evolution of the sample as prepared was investigated by XRD, TPR and TEM techniques. For the former, the chemical composites of the calcined sample are NiO-Fe2O3/LaFe1-xNixO3. After reduction and reaction of CO methanation, its composites convert to Fe-Ni@Ni/LaFeO3-La2O2CO3, in which Fe-Ni@Ni is metal particles in nano-size composed of nickel core and Fe-Ni alloy shell. For the latter, the chemical composites of the calcined sample are NiO/LaFeO3; and after reduction and reaction of CO methanation, its chemical composites change to Ni/LaFeO3. Ni/LaFeO3 catalyst is a little more active, while Fe-Ni@Ni/LaFeO3-La2O2CO3 is much more stable and shows very good resistance to carbon deposition. In this work it is aimed to show that the structure and composites of the catalysts can be tailored using perovskite-type oxide as precursor with different preparing method or preparing condition. Therefore, it is a promising route to prepare supported bi-metal catalysts in nano-size for a lot of metals with desired catalytic performances.
基金Project(51002025) supported by the National Natural Science Foundation of China
文摘The preparation process of amorphous nanometer boron powders through combustion synthesis was investigated, and the effects of the reactant ratio, the heating agent and the milling rate on the activity and particle size of amorphous boron powders were studied. The results show that the boron powders exist in the form of an amorphous phase which has the crystallinity lower than 30.4%, and the panicle size of boron powder decreases with an increase of the high-energy ball milling rate. The purity of amorphous boron powder is 94.8% and panicle sizes are much smaller than 100 nm when the mass ratio of B2O3/Mg/KClO3 is 100：105：17 and the ball milling time is 20 min with the milling rate of 300 r/min. At the same time, the amorphous boron nano-fibers appear in the boron powders.