The high-temperature oxidation behaviour of the Inconel 625 alloy at 950℃ was investigated after different ageing treatments.The effect of heat treatment on the oxidation behaviour of the alloy was analysed by charac...The high-temperature oxidation behaviour of the Inconel 625 alloy at 950℃ was investigated after different ageing treatments.The effect of heat treatment on the oxidation behaviour of the alloy was analysed by characterizing the structure and elemental distribution before and after oxidation.The results reveal that the two ageing treatments at 650℃ for 500 h and at 750℃ for 400 h both reduced the oxidation mass gain.After oxidation at 950℃,an outer Cr_(2)O_(3) layer and inner Al_(2)O_(3) are identified as the main oxidation products.Moreover,Nb_(2)O_(5) andδ(Ni_(3)Nb)phases precipitated after oxidation.The ageing treatments cause the rapid generation of a dense Cr_(2)O_(3) layer on the surface,which prevents the diffusion of oxygen into the matrix,reduce the Al_(2)O_(3) inward growth depth,and improve the oxidation resistance of the alloy.展开更多
基金financially supported by the National Science and Technology Major Project of China (Nos.MJ-2018-G-48,J2019-Ⅵ-0023-0140)the Research Fund of the State Key Laboratory of Solidification Processing (NPU),China (No.2022-TS-04)。
文摘The high-temperature oxidation behaviour of the Inconel 625 alloy at 950℃ was investigated after different ageing treatments.The effect of heat treatment on the oxidation behaviour of the alloy was analysed by characterizing the structure and elemental distribution before and after oxidation.The results reveal that the two ageing treatments at 650℃ for 500 h and at 750℃ for 400 h both reduced the oxidation mass gain.After oxidation at 950℃,an outer Cr_(2)O_(3) layer and inner Al_(2)O_(3) are identified as the main oxidation products.Moreover,Nb_(2)O_(5) andδ(Ni_(3)Nb)phases precipitated after oxidation.The ageing treatments cause the rapid generation of a dense Cr_(2)O_(3) layer on the surface,which prevents the diffusion of oxygen into the matrix,reduce the Al_(2)O_(3) inward growth depth,and improve the oxidation resistance of the alloy.