Coarse grained WC-9Co cemented carbides with 0-1.0% TaC(mass fraction) were fabricated by HIP-sintering and gas quenching. The effects of TaC on the microstructures and mechanical properties were investigated using sc...Coarse grained WC-9Co cemented carbides with 0-1.0% TaC(mass fraction) were fabricated by HIP-sintering and gas quenching. The effects of TaC on the microstructures and mechanical properties were investigated using scanning electron microscopy(SEM), energy dispersive X-ray analysis(EDS), X-ray diffractometry(XRD) and mechanical properties tests. The results show that the maximum values of hardness and strength are HV 1124 and 2466 MPa respectively when 0.4% TaC is added. When the content of TaC is more than 0.6%, the grain size of WC is no longer affected by the amount of TaC, and(W,Ta)C occurs as well. Moreover, the strength and fracture toughness increase and the(Ta+W) content decreases with the increase of TaC content. The dependence of(Ta+W) content on the mechanical properties indicates that(Ta+W) content in Co should be decreased as low as possible to improve the mechanical properties of coarse grained WC-TaC-9Co cemented carbides with the microstructure of WC+γ two phase regions.展开更多
Cemented tungsten carbide with ultra fine grains was prepared via microwave sintering.η phase（W3Co3C） was formed on the surface of the samples during the preparation process.Extra carbon black was premixed and the ...Cemented tungsten carbide with ultra fine grains was prepared via microwave sintering.η phase（W3Co3C） was formed on the surface of the samples during the preparation process.Extra carbon black was premixed and the influence of carbon content on mechanical properties was studied.The results show that the maximum value of hardness and transverse rupture strength are HRA 93.2 and 3396 MPa respectively when the carbon black content is 0.45%.The microstructure investigated by SEM show that the WC grains growth mainly occurs during the early stage of microwave sintering by the coalescence of grains.展开更多
In order to study the wear behavior of different kinds of contact wires,the dry sliding wear behaviors of Cu-Sn,Cu-Ag and Cu-Mg alloys prepared by up-drawn continuous casting and followed continuous extrusion were stu...In order to study the wear behavior of different kinds of contact wires,the dry sliding wear behaviors of Cu-Sn,Cu-Ag and Cu-Mg alloys prepared by up-drawn continuous casting and followed continuous extrusion were studied.The research was tested on a block-on-ring wear tester.The results indicate that the friction coefficient is remarkably influenced by the formation of a continuous tribofilm,which consists of oxidation film.The abrasion,adhesion,oxidation and plastic deformation are observed.Oxidation and abrasion wear mechanisms dominate at the lower sliding velocity and load.The combination of oxidation and adhesion play leading roles with the increasing load and velocity.Plastic deformation is detected under higher applied load and sliding velocities.展开更多
Diffusion bonding of TC21 titanium alloy was carried out at temperature ranging from 780 ℃ to 980 ℃ for 5-90 min.The interfacial bonding ratio,deformation ratio,microstructures and microhardness of the diffusion bon...Diffusion bonding of TC21 titanium alloy was carried out at temperature ranging from 780 ℃ to 980 ℃ for 5-90 min.The interfacial bonding ratio,deformation ratio,microstructures and microhardness of the diffusion bonded joints were investigated.Results show that joints with high bonding quality can be obtained when bonded at 880 ℃ for 15？30 min.The microhardness increases with increasing the bonding temperature,while it has a peak value（HV367） when bonding time is prolonged up to 90 min.Fully equiaxed microstructures,bi-modal microstructures and fully lamellar microstructures were observed when bonded in temperature range of 780-880 ℃,at 930 ℃ or 980 ℃,respectively.The volume fraction of α phase first increases and achieves the maximum when bonded at 880 ℃ for 60 min,and then descended.展开更多
The forming quality of high-strength TA18 titanium alloy tube during numerical control bending in changing bending angle β, relative bending radius R/D and tube sizes such as diameter D and wall thickness t was clari...The forming quality of high-strength TA18 titanium alloy tube during numerical control bending in changing bending angle β, relative bending radius R/D and tube sizes such as diameter D and wall thickness t was clarified by finite element simulation. The results show that the distribution of wall thickness change ratio Δt and cross section deformation ratio ΔD are very similar under different β; the Δt and ΔD decrease with the increase of R/D, and to obtain the qualified bent tube, the R/D must be greater than 2.0; the wall thinning ratio Δto slightly increases with larger D and t, while the wall thickening ratio Δti and ΔD increase with the larger D and smaller t; the Δto and ΔD firstly decrease and then increase, while the Δti increases, for the same D/t with the increase of D and t.展开更多
基金Project(2013zzts025)supported by the Fundamental Research Funds for the Central Universities of China
文摘Coarse grained WC-9Co cemented carbides with 0-1.0% TaC(mass fraction) were fabricated by HIP-sintering and gas quenching. The effects of TaC on the microstructures and mechanical properties were investigated using scanning electron microscopy(SEM), energy dispersive X-ray analysis(EDS), X-ray diffractometry(XRD) and mechanical properties tests. The results show that the maximum values of hardness and strength are HV 1124 and 2466 MPa respectively when 0.4% TaC is added. When the content of TaC is more than 0.6%, the grain size of WC is no longer affected by the amount of TaC, and(W,Ta)C occurs as well. Moreover, the strength and fracture toughness increase and the(Ta+W) content decreases with the increase of TaC content. The dependence of(Ta+W) content on the mechanical properties indicates that(Ta+W) content in Co should be decreased as low as possible to improve the mechanical properties of coarse grained WC-TaC-9Co cemented carbides with the microstructure of WC+γ two phase regions.
基金Project (2008890) supported by the Scientific Research Foundation for the Returned Overseas Chinese Scholars,China
文摘Cemented tungsten carbide with ultra fine grains was prepared via microwave sintering.η phase（W3Co3C） was formed on the surface of the samples during the preparation process.Extra carbon black was premixed and the influence of carbon content on mechanical properties was studied.The results show that the maximum value of hardness and transverse rupture strength are HRA 93.2 and 3396 MPa respectively when the carbon black content is 0.45%.The microstructure investigated by SEM show that the WC grains growth mainly occurs during the early stage of microwave sintering by the coalescence of grains.
基金Projects(51134013,51074031,51274054)supported by the National Natural Science Foundation of China
文摘In order to study the wear behavior of different kinds of contact wires,the dry sliding wear behaviors of Cu-Sn,Cu-Ag and Cu-Mg alloys prepared by up-drawn continuous casting and followed continuous extrusion were studied.The research was tested on a block-on-ring wear tester.The results indicate that the friction coefficient is remarkably influenced by the formation of a continuous tribofilm,which consists of oxidation film.The abrasion,adhesion,oxidation and plastic deformation are observed.Oxidation and abrasion wear mechanisms dominate at the lower sliding velocity and load.The combination of oxidation and adhesion play leading roles with the increasing load and velocity.Plastic deformation is detected under higher applied load and sliding velocities.
基金Project(2010CB731704)supported by the National Basic Research Program of Chinathe Northwest Institute for Non-ferrous Metal Research of China for the support
文摘Diffusion bonding of TC21 titanium alloy was carried out at temperature ranging from 780 ℃ to 980 ℃ for 5-90 min.The interfacial bonding ratio,deformation ratio,microstructures and microhardness of the diffusion bonded joints were investigated.Results show that joints with high bonding quality can be obtained when bonded at 880 ℃ for 15？30 min.The microhardness increases with increasing the bonding temperature,while it has a peak value（HV367） when bonding time is prolonged up to 90 min.Fully equiaxed microstructures,bi-modal microstructures and fully lamellar microstructures were observed when bonded in temperature range of 780-880 ℃,at 930 ℃ or 980 ℃,respectively.The volume fraction of α phase first increases and achieves the maximum when bonded at 880 ℃ for 60 min,and then descended.
基金Project(GJJ150810)supported by the Research Project of Science and Technology for Jiangxi Province Department of Education,ChinaProject(gf201501001)supported by National Defense Key Discipline Laboratory of Light Alloy Processing Science and Technology,Nanchang Hangkong University,ChinaProject(BSJJ2015015)supported by Doctor Start-up Fund of Jiangxi Science&Technology Normal University,China
文摘The forming quality of high-strength TA18 titanium alloy tube during numerical control bending in changing bending angle β, relative bending radius R/D and tube sizes such as diameter D and wall thickness t was clarified by finite element simulation. The results show that the distribution of wall thickness change ratio Δt and cross section deformation ratio ΔD are very similar under different β; the Δt and ΔD decrease with the increase of R/D, and to obtain the qualified bent tube, the R/D must be greater than 2.0; the wall thinning ratio Δto slightly increases with larger D and t, while the wall thickening ratio Δti and ΔD increase with the larger D and smaller t; the Δto and ΔD firstly decrease and then increase, while the Δti increases, for the same D/t with the increase of D and t.