The oxidation induration and reduction swelling behavior of the chromium-bearing vanadium titanomagnetite pellets (CVTP) with B2O3 addition were investigated. Besides, the reduction swelling index (RSI) and compressiv...The oxidation induration and reduction swelling behavior of the chromium-bearing vanadium titanomagnetite pellets (CVTP) with B2O3 addition were investigated. Besides, the reduction swelling index (RSI) and compressive strength (CS) of the reduced CVTP were also examined using the simulated coke oven gas (COG). The results suggested that the CS of CVTP was increased from 2448 to 3819.2 N, while the porosity of CVTP was decreased from 14.86% to 10.03% with the increase in B2O3 addition amounts. Moreover, the B2O3 mainly existed in the forms of TiB0.024O2 and Fe3BO5 in both CVTP and the reduced CVTP. Specifically, the CS of the reduced CVTP was elevated from 901 to 956.2 N, while the RSI was reduced from 5.87% to 3.81% as the B2O3 addition amounts were increased. Taken together, B2O3 addition would facilitate the aggregation and diffusion of metallic iron particles, which contributed to reducing the formation of metal iron whiskers and weakening the reduction swelling behavior.展开更多
The effect of nickel oxide additive on the smelting behaviors of chromium-bearing vanadium titanomagnetite pellets(CVTP)was investigated while analyzing the transfer behavior of nickel in iron and slag.The results sho...The effect of nickel oxide additive on the smelting behaviors of chromium-bearing vanadium titanomagnetite pellets(CVTP)was investigated while analyzing the transfer behavior of nickel in iron and slag.The results show that when NiO added to CVTP increases from 0 to 6 wt.%,softening start temperature increases from 1148 to 1212℃,and the softening end temperature increases from 1280 to 1334℃;the melting start temperature increases from 1318 to 1377℃,and the dripping temperature decreases from 1558 to 1521℃.The pig iron comprises a compound of Fe-Ni-C.The slag structure depolymerizes with increasing nickel addition.The softening-melting behaviors of CVTP,the reduction of nickel into pig iron,and the depolymerization of slag structure indicate the feasibility of producing nickel-iron alloy through the blast furnace process.展开更多
基金Projects(51674084,51174051,51574082)supported by the National Natural Science Foundation of China
文摘The oxidation induration and reduction swelling behavior of the chromium-bearing vanadium titanomagnetite pellets (CVTP) with B2O3 addition were investigated. Besides, the reduction swelling index (RSI) and compressive strength (CS) of the reduced CVTP were also examined using the simulated coke oven gas (COG). The results suggested that the CS of CVTP was increased from 2448 to 3819.2 N, while the porosity of CVTP was decreased from 14.86% to 10.03% with the increase in B2O3 addition amounts. Moreover, the B2O3 mainly existed in the forms of TiB0.024O2 and Fe3BO5 in both CVTP and the reduced CVTP. Specifically, the CS of the reduced CVTP was elevated from 901 to 956.2 N, while the RSI was reduced from 5.87% to 3.81% as the B2O3 addition amounts were increased. Taken together, B2O3 addition would facilitate the aggregation and diffusion of metallic iron particles, which contributed to reducing the formation of metal iron whiskers and weakening the reduction swelling behavior.
基金financial supports from the National Natural Science Foundation of China(Nos.21908020,U1908226)。
文摘The effect of nickel oxide additive on the smelting behaviors of chromium-bearing vanadium titanomagnetite pellets(CVTP)was investigated while analyzing the transfer behavior of nickel in iron and slag.The results show that when NiO added to CVTP increases from 0 to 6 wt.%,softening start temperature increases from 1148 to 1212℃,and the softening end temperature increases from 1280 to 1334℃;the melting start temperature increases from 1318 to 1377℃,and the dripping temperature decreases from 1558 to 1521℃.The pig iron comprises a compound of Fe-Ni-C.The slag structure depolymerizes with increasing nickel addition.The softening-melting behaviors of CVTP,the reduction of nickel into pig iron,and the depolymerization of slag structure indicate the feasibility of producing nickel-iron alloy through the blast furnace process.