The removal of phosphorus in metallurgical grade silicon （MG-Si） by water vapor carried with high purity argon was examined. The effect of the nozzle types, refining time, refining temperature, refining gas temperat...The removal of phosphorus in metallurgical grade silicon （MG-Si） by water vapor carried with high purity argon was examined. The effect of the nozzle types, refining time, refining temperature, refining gas temperature and refining gas flow rate on the phosphorus removed was investigated by the self-designed gas blowing device. The optimal refining conditions are nozzle type of holes at bottom and side, refining time of 3 h, refining temperature of 1793 K, refining gas temperature of 373 K, refining gas flow rate of 2 L/min. Under these optimal conditions, the phosphorus content in MG-Si is reduced from 94×10^-6 initially to 11×10-6 （mass fraction）, which indicates that gas blowing refining is very effective to remove phosphorus in MG-Si.展开更多
Gas blowing is a valid method to remove the impurities from metallurgical grade silicon（MG-Si） melt.The thermodynamic behavior of impurities Fe,Al,Ca,Ti,Cu,C,B and P in MG-Si was studied in the process of O2 blowing...Gas blowing is a valid method to remove the impurities from metallurgical grade silicon（MG-Si） melt.The thermodynamic behavior of impurities Fe,Al,Ca,Ti,Cu,C,B and P in MG-Si was studied in the process of O2 blowing.The removal efficiencies of impurities in MG-Si were investigated using O2 blowing in ladle.It is found that the removal efficiencies are higher than 90% for Ca and Al and nearly 50% for B and Ti.The morphology of inclusions was analyzed and the phases Al3Ni,NiSi2 and Al3Ni were confirmed in MG-Si by X-ray diffraction.It was found that SiB4 exists in Si？B binary system.The chemical composition of inclusions in MG-Si before and after refining was analyzed by SEM-EDS.It is found that the amount of white inclusion reduces for the removal of most Al and Ca in the forms of molten slag inclusion and the contents of Fe,Ni and Mn in inclusion increase for their inertia in silicon melt with O2 blowing.展开更多
A new method about purification of metallurgical grade silicon （MG-Si） by a combination of Si-Al solvent refining andgas blowing treatment was proposed. The morphologies and transformation of impurity phases, especi...A new method about purification of metallurgical grade silicon （MG-Si） by a combination of Si-Al solvent refining andgas blowing treatment was proposed. The morphologies and transformation of impurity phases, especially for boron and iron in Si-Al melt were investigated during Ar-H2 gas blowing treatment. The mechanism of boron removal was discussed. The resultsindicate that gas blowing can refine grain size and increase nucleation of the primary Si. Boron can be effectively removed fromMG-Si using the Ar-H2 gas blowing technique during the Si-Al solvent refining. Compared with the sample without gas blowing,the removal efficiency of boron increases from 45.83% to 74.73% after 2.5 h gas blowing. The main impurity phases containingboron are in the form of TiB2, AlB2 and VB compounds and iron-containing one is in the form of β-Al5FeSi intermetallic compound.Part of boron combines [H] to transform into gas BxHy （BH, BH2） and diffuses towards the surface of the melt and is volatilized byAr-H2 gas blowing treatment under electromagnetic stirring.展开更多
基金Project(51074043)supported by the National Natural Science Foundation of ChinaProject(2011BAE03B01)supported by the National Key Technology R&D Program of China
文摘The removal of phosphorus in metallurgical grade silicon （MG-Si） by water vapor carried with high purity argon was examined. The effect of the nozzle types, refining time, refining temperature, refining gas temperature and refining gas flow rate on the phosphorus removed was investigated by the self-designed gas blowing device. The optimal refining conditions are nozzle type of holes at bottom and side, refining time of 3 h, refining temperature of 1793 K, refining gas temperature of 373 K, refining gas flow rate of 2 L/min. Under these optimal conditions, the phosphorus content in MG-Si is reduced from 94×10^-6 initially to 11×10-6 （mass fraction）, which indicates that gas blowing refining is very effective to remove phosphorus in MG-Si.
基金Projects(51104080,u1137601) supported by the National Natural Science Foundation of ChinaProject(2009CD027) supported by the Natural Science Foundation of Yunnan Province,ChinaProject(14118557) supported by the Personnel Training Foundation of Kunming University of Science and Technology,China
文摘Gas blowing is a valid method to remove the impurities from metallurgical grade silicon（MG-Si） melt.The thermodynamic behavior of impurities Fe,Al,Ca,Ti,Cu,C,B and P in MG-Si was studied in the process of O2 blowing.The removal efficiencies of impurities in MG-Si were investigated using O2 blowing in ladle.It is found that the removal efficiencies are higher than 90% for Ca and Al and nearly 50% for B and Ti.The morphology of inclusions was analyzed and the phases Al3Ni,NiSi2 and Al3Ni were confirmed in MG-Si by X-ray diffraction.It was found that SiB4 exists in Si？B binary system.The chemical composition of inclusions in MG-Si before and after refining was analyzed by SEM-EDS.It is found that the amount of white inclusion reduces for the removal of most Al and Ca in the forms of molten slag inclusion and the contents of Fe,Ni and Mn in inclusion increase for their inertia in silicon melt with O2 blowing.
基金Projects(51404231,51474201)supported by the National Natural Science Foundation of ChinaProject(1508085QE81)supported by Anhui Provincial Natural Science Foundation,China+1 种基金Project(2014M561846)supported by China Postdoctoral Science FoundationProject(2012065)supported by 100 Talent Program of Chinese Academy of Sciences
文摘A new method about purification of metallurgical grade silicon （MG-Si） by a combination of Si-Al solvent refining andgas blowing treatment was proposed. The morphologies and transformation of impurity phases, especially for boron and iron in Si-Al melt were investigated during Ar-H2 gas blowing treatment. The mechanism of boron removal was discussed. The resultsindicate that gas blowing can refine grain size and increase nucleation of the primary Si. Boron can be effectively removed fromMG-Si using the Ar-H2 gas blowing technique during the Si-Al solvent refining. Compared with the sample without gas blowing,the removal efficiency of boron increases from 45.83% to 74.73% after 2.5 h gas blowing. The main impurity phases containingboron are in the form of TiB2, AlB2 and VB compounds and iron-containing one is in the form of β-Al5FeSi intermetallic compound.Part of boron combines [H] to transform into gas BxHy （BH, BH2） and diffuses towards the surface of the melt and is volatilized byAr-H2 gas blowing treatment under electromagnetic stirring.