In situ TiB2/Cu composites were fabricated by both solid-liquid(S-L)and liquid-liquid(L-L)reactive spray deposition in combination with cold rolling and annealing.The microstructure and properties of the fabricated Ti...In situ TiB2/Cu composites were fabricated by both solid-liquid(S-L)and liquid-liquid(L-L)reactive spray deposition in combination with cold rolling and annealing.The microstructure and properties of the fabricated TiB2/Cu composites were investigated.The results show that the reactive mode and rolling treatment are the main factors affecting the microstructure and properties of the TiB2/Cu composite.The in situ reaction in the L-L reaction can be carried out more completely.By controlling the rolling and annealing process,the relative density and the properties of the as-deposited composites are optimized.The comprehensive performance of the deformed TiB2/Cu composite prepared by L-L reactive spray deposition(401 MPa and 83.5%IACS)is better than that by S-L reactive spray deposition(520 MPa and 20.2%IACS).展开更多
A novel surface cladding technique was developed to prepare the FeCrNiMn alloy and high carbon steel cladding layers,and the microhardness,bonding strength,abrasion wear and corrosion resistance were investigated.The ...A novel surface cladding technique was developed to prepare the FeCrNiMn alloy and high carbon steel cladding layers,and the microhardness,bonding strength,abrasion wear and corrosion resistance were investigated.The microstructures of the cladding layers were analyzed by using X-ray diffraction(XRD),scanning electron microscopy(SEM),and energy dispersive spectrometry(EDS).The results show that the bonding strength between the substrate and the two cladding layers were(432.6±21)and(438.3±12)MPa,respectively.Vickers hardness values of the two cladding layers were HV418.5and HV329.6,respectively.The corrosion current densities of the two coatings were2.926×10–6and6.858×10–6A/cm2after electrochemical corrosion test in3.5%NaCl solution,and the wear rate were1.78×10–7and1.46×10–6mm3/mN after sliding wear test,respectively.This indicates that a well metallurgical bonding between the coating and the substrate was achieved,the abrasion wear and corrosion resistance of both coatings had been greatly improved compared with the substrate.The novel cladding technology is promising for preparing wear-and-corrosion resistant coatings.展开更多
基金Projects(U1502274,51834009)supported by the National Natural Science Foundation of ChinaProject(2017ZDXM-GY-028)supported by the Key Research and Development Program of Shaanxi,China。
文摘In situ TiB2/Cu composites were fabricated by both solid-liquid(S-L)and liquid-liquid(L-L)reactive spray deposition in combination with cold rolling and annealing.The microstructure and properties of the fabricated TiB2/Cu composites were investigated.The results show that the reactive mode and rolling treatment are the main factors affecting the microstructure and properties of the TiB2/Cu composite.The in situ reaction in the L-L reaction can be carried out more completely.By controlling the rolling and annealing process,the relative density and the properties of the as-deposited composites are optimized.The comprehensive performance of the deformed TiB2/Cu composite prepared by L-L reactive spray deposition(401 MPa and 83.5%IACS)is better than that by S-L reactive spray deposition(520 MPa and 20.2%IACS).
基金Project(2016JJ2025)supported by the Natural Science Foundation of Hunan Province,ChinaProject(U1560105)supported by the National Natural Science Foundation of China
文摘A novel surface cladding technique was developed to prepare the FeCrNiMn alloy and high carbon steel cladding layers,and the microhardness,bonding strength,abrasion wear and corrosion resistance were investigated.The microstructures of the cladding layers were analyzed by using X-ray diffraction(XRD),scanning electron microscopy(SEM),and energy dispersive spectrometry(EDS).The results show that the bonding strength between the substrate and the two cladding layers were(432.6±21)and(438.3±12)MPa,respectively.Vickers hardness values of the two cladding layers were HV418.5and HV329.6,respectively.The corrosion current densities of the two coatings were2.926×10–6and6.858×10–6A/cm2after electrochemical corrosion test in3.5%NaCl solution,and the wear rate were1.78×10–7and1.46×10–6mm3/mN after sliding wear test,respectively.This indicates that a well metallurgical bonding between the coating and the substrate was achieved,the abrasion wear and corrosion resistance of both coatings had been greatly improved compared with the substrate.The novel cladding technology is promising for preparing wear-and-corrosion resistant coatings.