CuI thin films with nano-scale grains of about 35nm were deposited via spraying method with using acetonitrile as solvent. The influence of iodine doping concentration in acetonitrile solution on the structure, topogr...CuI thin films with nano-scale grains of about 35nm were deposited via spraying method with using acetonitrile as solvent. The influence of iodine doping concentration in acetonitrile solution on the structure, topographic and optical properties of CuI thin films was investigated. X-ray diffraction results showed that CuI iodine-doped films doped CuI：I2 were in γ-phase of zinc blende structure with （111） preferential plane. Scanning electron microscopy revealed that the microstructure of CuI films depended on the relative amount of doping iodine in the solution. When the iodine doping amount in acetonitrile solution was 0.025 g, the film was uniform and compact, the optical transmittance was 75.4% in the part of visible region and the energy band gap was close to 2.96 eV.展开更多
Sputtering deposition is one of the most important processes in the vacuum coating, it is widely used in microeletronics industries, optical films, and metallurgical coatings industry et al. Sputtering deposition is, ...Sputtering deposition is one of the most important processes in the vacuum coating, it is widely used in microeletronics industries, optical films, and metallurgical coatings industry et al. Sputtering deposition is, in the vacuum conditions, sputtered particles from the target material deposit on the substrate using energetic ions to bombard surface of target to form a film.展开更多
基金Project (2091003) supported by Beijing Natural Science Foundation, China
文摘CuI thin films with nano-scale grains of about 35nm were deposited via spraying method with using acetonitrile as solvent. The influence of iodine doping concentration in acetonitrile solution on the structure, topographic and optical properties of CuI thin films was investigated. X-ray diffraction results showed that CuI iodine-doped films doped CuI：I2 were in γ-phase of zinc blende structure with （111） preferential plane. Scanning electron microscopy revealed that the microstructure of CuI films depended on the relative amount of doping iodine in the solution. When the iodine doping amount in acetonitrile solution was 0.025 g, the film was uniform and compact, the optical transmittance was 75.4% in the part of visible region and the energy band gap was close to 2.96 eV.
文摘Sputtering deposition is one of the most important processes in the vacuum coating, it is widely used in microeletronics industries, optical films, and metallurgical coatings industry et al. Sputtering deposition is, in the vacuum conditions, sputtered particles from the target material deposit on the substrate using energetic ions to bombard surface of target to form a film.