The influence of calcination temperature on TiO2 nanotubes＇ catalysis for TiO2/UV/03 was investigated. TiO2 nanotubes （TNTs） were prepared via the sol-gel method and calcined at 300--700 ℃, which were labeled as T...The influence of calcination temperature on TiO2 nanotubes＇ catalysis for TiO2/UV/03 was investigated. TiO2 nanotubes （TNTs） were prepared via the sol-gel method and calcined at 300--700 ℃, which were labeled as TNTs-300, TNTs-400, TNTs-500, TNTs-600 and TNTs-700, respectively. TNTs were characterized by transmission electron microscopy （TEM） and X-ray diffraction （XRD）. It is found that TNTs calcined at 400 ℃ showed the best thermal stability. When the calcination temperature increased from 400 ℃ to 700 ℃, the special structure of tubes was destroyed and gradually converted into nanorods and/or particles. The transformation from anatase to rutile occurred at 600 ℃, and the rutile phase was enhanced when the calcination temperature was increased to over 600 ℃. The calcina- tion temperature＇s influence on TNTs＇ adsorption activity for for TiO2/UV/O3 was investigated in landfill leachate solution chemical oxygen demand （COD） and catalytic activity In landfill leachate solution, the adsorption activity of COD decreased in the reduced order of TNTs-300, TNTs-400, TNTs-500, TNTs-600 and TNTs-700. In photocatalytic ozonation, TNTs-400 showed the best catalytic activity while TNTs-700 exhibited the worst. In other three processes, the COD removal of TNTs-300/UV/O3 was higher than those of TNTs-500/UV/O3 and TNTs-600/UV/O3 in the first 20 rain, and then became close to those of the latter two in the following 40 rain. Compared with TNTs-300 and TNTs- 400, TNTs-600 had the best anti-fouling activity, while TNTs-500 and TNTs-700 had lower anti-fouling activity than the former three. In photocatalytic ozonation, the calcination temperature of 400 ℃ was appropriate when TNTs were obtained at the synthesis temperature of 105 ℃.展开更多
基金Supported by Tianjin Science and Technology Development Plan Project (No.06YFGZSH06700)
文摘The influence of calcination temperature on TiO2 nanotubes＇ catalysis for TiO2/UV/03 was investigated. TiO2 nanotubes （TNTs） were prepared via the sol-gel method and calcined at 300--700 ℃, which were labeled as TNTs-300, TNTs-400, TNTs-500, TNTs-600 and TNTs-700, respectively. TNTs were characterized by transmission electron microscopy （TEM） and X-ray diffraction （XRD）. It is found that TNTs calcined at 400 ℃ showed the best thermal stability. When the calcination temperature increased from 400 ℃ to 700 ℃, the special structure of tubes was destroyed and gradually converted into nanorods and/or particles. The transformation from anatase to rutile occurred at 600 ℃, and the rutile phase was enhanced when the calcination temperature was increased to over 600 ℃. The calcina- tion temperature＇s influence on TNTs＇ adsorption activity for for TiO2/UV/O3 was investigated in landfill leachate solution chemical oxygen demand （COD） and catalytic activity In landfill leachate solution, the adsorption activity of COD decreased in the reduced order of TNTs-300, TNTs-400, TNTs-500, TNTs-600 and TNTs-700. In photocatalytic ozonation, TNTs-400 showed the best catalytic activity while TNTs-700 exhibited the worst. In other three processes, the COD removal of TNTs-300/UV/O3 was higher than those of TNTs-500/UV/O3 and TNTs-600/UV/O3 in the first 20 rain, and then became close to those of the latter two in the following 40 rain. Compared with TNTs-300 and TNTs- 400, TNTs-600 had the best anti-fouling activity, while TNTs-500 and TNTs-700 had lower anti-fouling activity than the former three. In photocatalytic ozonation, the calcination temperature of 400 ℃ was appropriate when TNTs were obtained at the synthesis temperature of 105 ℃.
