聚硅氧烷增容母料的制备及应用

The increasing-compatibility-matrix-stuff with properties of compellent compatibility was prepared through the seed emulsion grafting co-polymerization methods. The structures of the increasing-compatible-matrix-stuff was analyzed by fourier transform infrared spectroscopy(FTIR) and nuclear magnetic resonate(NMR). The compellent damping materials was prepared using different ratio of the increasing-compatible-matrix-stuff, and the properties was tested with dynamic mechanic analysis(DMA) methods. The results show that the increasing-compatible-matrix-stuff has the special characteristics of compellent compatibility, and enhance the glass transformation temperature of the damping materials, and markedly develop the using-temperature-extent and the loss tangent of the damping materials.

酸酐化LLDPE/PS增容母料对LLDPE/PS/PA6三元共混物结构及性能的影响

结合聚烯烃与聚苯乙烯间的Friedel-Crafts烷基化反应和聚烯烃熔融接枝马来酸酐(MAH)技术,制备了酸酐化线性低密度聚乙烯(LLDPE)/聚苯乙烯(PS)(70/30,质量比)增容母料。以该母料作为多相相容剂,考察了其对LLDPE/PS/尼龙6(PA6)(60/20/20,质量比)三元共混物微观结构、力学性能和流变性能的影响。红外测试结果表明,酸酐化LLDPE/PS增容母料中含有(LLDPE/LLDPE-g-PS)-g-MAH;三元共混物加入母料后有接枝物(LLDPE/LLDPE-g-PS)-gPA6生成。扫描电镜及力学性能测试结果显示,三元共混物加入质量分数为10%母料后两分散相粒径显著减小,三相之间从互相分离转变为互相连接;力学性能明显提高。动态流变测试结果表明,加入母料后三元共混物的储能模量(G')、损耗模量(G″)和复数黏度(η*)上升,损耗因子(tanδ)减小;三元简单共混物出现2个内耗峰,母料的增容作用可使2个内耗峰均消失。

增容剂流动性对PE-LLD/PS/PET三元共混物性能的影响

通过Friedel-Crafts烷基化反应,制备了线型低密度聚乙烯(PE-LLD)/聚苯乙烯(PS)(质量比50/50)增容母料,并将其与甲基丙烯酸缩水甘油酯(GMA)熔融接枝,制成接枝改性母料。在等质量的接枝改性母料中,添加不同用量的高熔体流动速率(MFR)的PE-LLD(HFPE-LLD),同时添加PS,使HFPE-LLD与PS的质量比始终保持在50/50,制成流动性不同的三元增容母料。将有效组分含量相同的上述三元增容母料,添加到PE-LLD/PS/聚对苯二甲酸乙二酯(PET)三元共混物中,考察了三元增容母料的流动性对共混物力学性能、动态流变性能及微观结构的影响。结果表明,随着三元增容母料流动性的增大,共混物的力学性能逐渐上升。相比未增容的共混物,添加了MFR为10.1 g/10 min的三元增容母料的共混物,力学性能达到最佳,其拉伸强度由8.2 MPa增至17.5 MPa,增幅为113.4%,断裂伸长率由2.3%增至23.5%,增幅为921.7%;在高频区,随着三元增容母料流动性的增大,共混物的储能模量、损耗模量、复数黏度逐渐上升,损耗因子逐渐下降。扫描电子显微镜照片显示,三元增容母料的流动性增大后,分散相粒径明显减小,相界面逐渐模糊。

动态硫化法制备结构性耐候聚苯乙烯/乙烯-辛烯共聚物高韧合金

利用Friedel-Crafts烷基化反应制备50/50(质量比,下同)聚苯乙烯/乙烯-辛烯共聚物(PS/POE)增容母料,研究了POE-PS增容母料用量和动态硫化对PS/POE(70/30)性能的影响。结果表明,在增容母料中,PS接枝率为29.2%,凝胶含量为0%;当添加40 phr增容母料取代PS/POE(70/30)共混物中部分PS和POE,共混物的冲击强度比纯PS和相同配比简单共混物分别提高了300%和91.2%;在此基础上,添加过氧化二异丙苯(DCP)和三烯丙基异氰脲酸酯(TAIC)各0.2 phr进行动态硫化,其冲击强度和拉伸强度较未动态硫化的PS/POE/PS-POE增容母料(50/10/40)提高了12.4%和6.5%;扫描电镜、动态流变性能和动态力学热分析的测试结果表明,采用增容母料和动态硫化有助于提高POE与PS两相之间的相容性。