A NiTi@Mg interpenetrating phase composite with high strength and lightweight was prepared by additive manufacturing(AM)and infiltration technology,and the interface bonding,three-point bending properties and cyclic c...A NiTi@Mg interpenetrating phase composite with high strength and lightweight was prepared by additive manufacturing(AM)and infiltration technology,and the interface bonding,three-point bending properties and cyclic compressive properties of NiTi@Mg composites were investigated.The results show that the metallurgically bonded interface is formed at the NiTi/Mg interfaces.The bending strength and compressive strength of the NiTi@Mg composite are 2.5 and 1.7 times higher than those of the NiTi scaffold,respectively.During the bending deformation process,a large number of dislocations are observed to accumulate in the soft Mg area at the interface.Furthermore,the finite element model showed that the stress accumulation area,where the bending crack is initiated,is located at the interface of NiTi and Mg.The strengthening mechanism of NiTi@Mg composites is attributed to the twinning strengthening of Mg and heterogeneous structure strengthening.展开更多
基金supported by the National Natural Science Foundation of China (Nos.52001030,51803200,52105356,52003104)the Natural Science Foundation of Hunan Province,China (Nos.2021JJ40590,2021JJ40600)+6 种基金the Natural Science Foundation of Hunan Province Youth Fund,China (No.2021JJ20011)the Major Research Plan of the National Natural Science Foundation of China (No.92166112)the Project of MOE Key Lab of Disaster Forecast and Control in Engineering in Jinan University,China (No.20200904006)the Guangdong Province Basic and Applied Basic Research Foundation,China (No.2020B1515420004)the Guangxi Key Laboratory of Information Materials,China (No.211003-K)the Open Project Program of the State Key Laboratory of Mechanical Transmissions in Chongqing University,China (No.SKLMT-MSKFKT-202102)the Fundamental Research Funds for the Central Universities,China (No.21622110)。
文摘A NiTi@Mg interpenetrating phase composite with high strength and lightweight was prepared by additive manufacturing(AM)and infiltration technology,and the interface bonding,three-point bending properties and cyclic compressive properties of NiTi@Mg composites were investigated.The results show that the metallurgically bonded interface is formed at the NiTi/Mg interfaces.The bending strength and compressive strength of the NiTi@Mg composite are 2.5 and 1.7 times higher than those of the NiTi scaffold,respectively.During the bending deformation process,a large number of dislocations are observed to accumulate in the soft Mg area at the interface.Furthermore,the finite element model showed that the stress accumulation area,where the bending crack is initiated,is located at the interface of NiTi and Mg.The strengthening mechanism of NiTi@Mg composites is attributed to the twinning strengthening of Mg and heterogeneous structure strengthening.