The solid solutions Ce 1- x Eu x O 2- δ ( x =0\^10—0\^50) were synthesized by high temperature and high pressure. The XRD measurement showed that the solid solution was crystallized in cubic fluorite type structure ...The solid solutions Ce 1- x Eu x O 2- δ ( x =0\^10—0\^50) were synthesized by high temperature and high pressure. The XRD measurement showed that the solid solution was crystallized in cubic fluorite type structure and the lattice parameter increased with the content of Eu increasing up to x =0.4. The solution limit was \%ca.\% 0.4 under the condition of 3.6 GPa, 840—1 020 ℃. The XPS data showed that the Eu ions are Eu 3+ and trace of Ce 4+ ions were reduced to Ce 3+ ions during synthesis of high temperature and high pressure. The ionic conduction for Ce 0.8 Eu 0.2 O 2- δ was measured by impedance spectroscopy and it was found that the activation energy was 1.07 eV and the conductivity was 3.43×10 -5 S·cm -1 at 550 ℃.展开更多
The structure and catalytic desulfurization characteristics of CeO2-TiO2 mixed oxides were investigated by means ofX-ray diffraction （XRD）, X-ray photoelectron spectroscopy （XPS） and catalytic activity tests. Acco...The structure and catalytic desulfurization characteristics of CeO2-TiO2 mixed oxides were investigated by means ofX-ray diffraction （XRD）, X-ray photoelectron spectroscopy （XPS） and catalytic activity tests. According to the results, a CeO2-TiO2solid solution is formed when the mole ratio of cerium to titanium n（Ce）：n（Ti） is 5：5 or greater, and the most suitable n（Ce）：n（Ti） isdetermined as 7：3, over which the conversion rate of SO2 and the yield of sulfur at 500℃ reach 93% and 99%, respectively.According to the activity testing curve, Ce0.7Ti0.3O2 （n（Ce）：n（Ti）=7：3） without any pretreatment can be gradually activated by reagentgas after about 10 min, and reaches a steady activation status 60 min later. The XPS results of Ce0.7Ti0.3O2 after different time ofSO2＋CO reaction show that CeO2 is the active component that offers the redox couple Ce4＋/Ce3＋ and the labile oxygen vacancies, andTiO2 only functions as a catalyst structure stabilizer during the catalytic reaction process. After 48 h of catalytic reaction at 500℃,Ce0.7Ti0.3O2 still maintains a stable structure without being vulcanized, demonstrating its good anti-sulfur poisoning performance.展开更多
Three La-doped CeO2-ZrO2-Al2O3(CZA)composite oxide samples,namely,CZA-I,CZA-II and CZA-III,were prepared following a co-precipitation method in the presence of La2O3,La(NO3)3-6H2O and H[La(EDTA)]-16H2O precursors,resp...Three La-doped CeO2-ZrO2-Al2O3(CZA)composite oxide samples,namely,CZA-I,CZA-II and CZA-III,were prepared following a co-precipitation method in the presence of La2O3,La(NO3)3-6H2O and H[La(EDTA)]-16H2O precursors,respectively.When the precursor samples are sintered at 1000°C,the as-prepared composite oxides mainly exhibit the CeO2-ZrO2 cubic fluorite phase,while theγ-Al2O3 andδ-Al2O3 phases appear when the precursor samples are subjected to sintering at 1100 and 1200°C.CZA-III exhibits improved redox properties after high-temperature treatment compared with CZA-I and CZA-II.CZA-III presents the largest surface area of 97.46 m2/g among the three CZAs when the CZA-III precursor sample is sintered at 1000°C.Furthermore,the corresponding oxygen storage capacity(OSC)is the largest with value of 400.27μmol/g when CZA-III precursor sample is sintered at 1000°C.Additionally,CZA-III exhibits the best thermal stability and the highest reduction temperature.However,by increasing the sintering temperature to 1200°C,there is a dramatic decline in the properties of surface area and OSC.And a decrease for CZA-III in surface area by 58.94%and a decrease of the OSC value by 74.56%are observed.展开更多
文摘The solid solutions Ce 1- x Eu x O 2- δ ( x =0\^10—0\^50) were synthesized by high temperature and high pressure. The XRD measurement showed that the solid solution was crystallized in cubic fluorite type structure and the lattice parameter increased with the content of Eu increasing up to x =0.4. The solution limit was \%ca.\% 0.4 under the condition of 3.6 GPa, 840—1 020 ℃. The XPS data showed that the Eu ions are Eu 3+ and trace of Ce 4+ ions were reduced to Ce 3+ ions during synthesis of high temperature and high pressure. The ionic conduction for Ce 0.8 Eu 0.2 O 2- δ was measured by impedance spectroscopy and it was found that the activation energy was 1.07 eV and the conductivity was 3.43×10 -5 S·cm -1 at 550 ℃.
文摘The structure and catalytic desulfurization characteristics of CeO2-TiO2 mixed oxides were investigated by means ofX-ray diffraction （XRD）, X-ray photoelectron spectroscopy （XPS） and catalytic activity tests. According to the results, a CeO2-TiO2solid solution is formed when the mole ratio of cerium to titanium n（Ce）：n（Ti） is 5：5 or greater, and the most suitable n（Ce）：n（Ti） isdetermined as 7：3, over which the conversion rate of SO2 and the yield of sulfur at 500℃ reach 93% and 99%, respectively.According to the activity testing curve, Ce0.7Ti0.3O2 （n（Ce）：n（Ti）=7：3） without any pretreatment can be gradually activated by reagentgas after about 10 min, and reaches a steady activation status 60 min later. The XPS results of Ce0.7Ti0.3O2 after different time ofSO2＋CO reaction show that CeO2 is the active component that offers the redox couple Ce4＋/Ce3＋ and the labile oxygen vacancies, andTiO2 only functions as a catalyst structure stabilizer during the catalytic reaction process. After 48 h of catalytic reaction at 500℃,Ce0.7Ti0.3O2 still maintains a stable structure without being vulcanized, demonstrating its good anti-sulfur poisoning performance.
基金Project(14JJ4043)supported by the Natural Science Foundation of Hunan Province,China
文摘Three La-doped CeO2-ZrO2-Al2O3(CZA)composite oxide samples,namely,CZA-I,CZA-II and CZA-III,were prepared following a co-precipitation method in the presence of La2O3,La(NO3)3-6H2O and H[La(EDTA)]-16H2O precursors,respectively.When the precursor samples are sintered at 1000°C,the as-prepared composite oxides mainly exhibit the CeO2-ZrO2 cubic fluorite phase,while theγ-Al2O3 andδ-Al2O3 phases appear when the precursor samples are subjected to sintering at 1100 and 1200°C.CZA-III exhibits improved redox properties after high-temperature treatment compared with CZA-I and CZA-II.CZA-III presents the largest surface area of 97.46 m2/g among the three CZAs when the CZA-III precursor sample is sintered at 1000°C.Furthermore,the corresponding oxygen storage capacity(OSC)is the largest with value of 400.27μmol/g when CZA-III precursor sample is sintered at 1000°C.Additionally,CZA-III exhibits the best thermal stability and the highest reduction temperature.However,by increasing the sintering temperature to 1200°C,there is a dramatic decline in the properties of surface area and OSC.And a decrease for CZA-III in surface area by 58.94%and a decrease of the OSC value by 74.56%are observed.