The SiC/A356/FeNi50 composite was fabricated by gas pressure infiltration. The interfacial region of the SiC/A356/FeNi50 composite consisted of FeNi50 reaction layer, A1 reaction layer and A1 alloy matrix. The main in...The SiC/A356/FeNi50 composite was fabricated by gas pressure infiltration. The interfacial region of the SiC/A356/FeNi50 composite consisted of FeNi50 reaction layer, A1 reaction layer and A1 alloy matrix. The main intermetallic compounds were （Fe,Ni）a（A1,Sih3 and （Fe,Ni）2（A1,Si）5 at the A1 reaction layer and FeNi50 reaction layer, respectively. The bending behavior versus different infiltration temperatures and holding times was also investigated. The bending strength at 670 ~C was the highest and close to the bending strength of A1 alloy （223 MPa）, and 46% of SIC/A356. The brittle intermetallic compounds existing at the interface induced the decreasing of the bending strength. The pores were reduced by adequate heating time due to the homogeneous temperature of preform, which was beneficial to improve the bending strength of the composite.展开更多
The B4C/Mg composites fabricated by metal-assisted pressureless infiltration technique were used as experimental material, and the wear behavior and mechanism of this material were studied. A pin-on-disc apparatus was...The B4C/Mg composites fabricated by metal-assisted pressureless infiltration technique were used as experimental material, and the wear behavior and mechanism of this material were studied. A pin-on-disc apparatus was used to evaluate the wear behavior where loads of 20, 40, 60 and 80 N, and a sliding velocity of 250 r/min were exerted. The results show that B4C/Mg composites possess superior wear resistance than pure Mg under various applied loads, and the content of Ti, as infiltration inducer, has an influence on the wear resistance of B4C/Mg composites. The dominant wear mechanism for pure Mg is abrasion, while that for B4C/Mg composites under low loads is adhesion and delamination. Under high loads, the wear mechanism of B4C/Mg composites can be attributed to thermal softening and melting or plastic deformation.展开更多
Thermal properties of AlN-Si-Al composites produced by pressureless melt infiltration of Al/Al alloys into porous a-Si3N4 preforms were investigated in a temperature range of 50-300 °C. SEM and TEM investigations...Thermal properties of AlN-Si-Al composites produced by pressureless melt infiltration of Al/Al alloys into porous a-Si3N4 preforms were investigated in a temperature range of 50-300 °C. SEM and TEM investigations revealed that the grain size of AlN particles was less than 1 μm. In spite of sub-micron grain size, composites showed relatively high thermal conductivity （TC）, 55-107 W/（m·K）. The thermal expansion coefficient （CTE） of the composite produced with commercial Al source, which has the highest TC of 107 W/（m·K）, was 6.5×10-6 K-1. Despite the high CTE of Al （23.6×10-6 K-1）, composites revealed significantly low CTE through the formation of Si and AlN phases during the infiltration process.展开更多
Cu47Ti33Zr11Ni6Sn2Si1-based bulk metallic glass matrix composites reinforced with tungsten wires were fabricated by infiltration process at different temperatures （850, 900, 950 and 1000 °C） and time （10, 20 a...Cu47Ti33Zr11Ni6Sn2Si1-based bulk metallic glass matrix composites reinforced with tungsten wires were fabricated by infiltration process at different temperatures （850, 900, 950 and 1000 °C） and time （10, 20 and 30 min） in a quartz or a steel tube. The mechanical tests were carried out by scanning electron microscopy （SEM） and X-ray diffraction （XRD）. The results show that the maximum strength and total strain of the composite are 1778 MPa and 2.8% fabricated in steel tube at 900 °C for 10 min, and 1582 MPa and 3.6% fabricated in quartz tube at 850 °C for 10 min, respectively.展开更多
A new method for determining two key parameters(threshold pressure and permeability)for fabricating metal matrix composites was proposed based on the equation-solving method.An infiltration experimental device was dev...A new method for determining two key parameters(threshold pressure and permeability)for fabricating metal matrix composites was proposed based on the equation-solving method.An infiltration experimental device was devised to measure the infiltration behavior precisely with controllable infiltration velocity.Two experiments with alloy Pb-Sn infiltrating into Al2O3 preform were conducted independently under two different pressures so as to get two different infiltration curves.Two sets of coefficients which are functions of threshold pressure and permeability can be obtained through curve fitting method.By solving the two-variable equation set,two unknown variables were determined.It is shown that the determined threshold pressure and permeability are very close to the calculated ones and are also verified by another independent infiltration experiment.The proposed method is also feasible to determine the key infiltration parameters for other metal matrix composite systems.展开更多
基金Project (60776019) supported by the National Natural Science Foundation of ChinaProject (61-TP-2010) supported by Research Fund of the State Key Laboratory of Solidification Processing(NWPU),China
文摘The SiC/A356/FeNi50 composite was fabricated by gas pressure infiltration. The interfacial region of the SiC/A356/FeNi50 composite consisted of FeNi50 reaction layer, A1 reaction layer and A1 alloy matrix. The main intermetallic compounds were （Fe,Ni）a（A1,Sih3 and （Fe,Ni）2（A1,Si）5 at the A1 reaction layer and FeNi50 reaction layer, respectively. The bending behavior versus different infiltration temperatures and holding times was also investigated. The bending strength at 670 ~C was the highest and close to the bending strength of A1 alloy （223 MPa）, and 46% of SIC/A356. The brittle intermetallic compounds existing at the interface induced the decreasing of the bending strength. The pores were reduced by adequate heating time due to the homogeneous temperature of preform, which was beneficial to improve the bending strength of the composite.
基金Project(51271051)supported by the National Natural Sciecne Foundation of China
文摘The B4C/Mg composites fabricated by metal-assisted pressureless infiltration technique were used as experimental material, and the wear behavior and mechanism of this material were studied. A pin-on-disc apparatus was used to evaluate the wear behavior where loads of 20, 40, 60 and 80 N, and a sliding velocity of 250 r/min were exerted. The results show that B4C/Mg composites possess superior wear resistance than pure Mg under various applied loads, and the content of Ti, as infiltration inducer, has an influence on the wear resistance of B4C/Mg composites. The dominant wear mechanism for pure Mg is abrasion, while that for B4C/Mg composites under low loads is adhesion and delamination. Under high loads, the wear mechanism of B4C/Mg composites can be attributed to thermal softening and melting or plastic deformation.
基金The Foundation for Scientific Research Projects of Mugla Sitki Kocman University(Project No.10/30)The Scientific&Technological Research Council of Turkey(TUBITAK,Project No:108M194)for funding the present work
文摘Thermal properties of AlN-Si-Al composites produced by pressureless melt infiltration of Al/Al alloys into porous a-Si3N4 preforms were investigated in a temperature range of 50-300 °C. SEM and TEM investigations revealed that the grain size of AlN particles was less than 1 μm. In spite of sub-micron grain size, composites showed relatively high thermal conductivity （TC）, 55-107 W/（m·K）. The thermal expansion coefficient （CTE） of the composite produced with commercial Al source, which has the highest TC of 107 W/（m·K）, was 6.5×10-6 K-1. Despite the high CTE of Al （23.6×10-6 K-1）, composites revealed significantly low CTE through the formation of Si and AlN phases during the infiltration process.
文摘Cu47Ti33Zr11Ni6Sn2Si1-based bulk metallic glass matrix composites reinforced with tungsten wires were fabricated by infiltration process at different temperatures （850, 900, 950 and 1000 °C） and time （10, 20 and 30 min） in a quartz or a steel tube. The mechanical tests were carried out by scanning electron microscopy （SEM） and X-ray diffraction （XRD）. The results show that the maximum strength and total strain of the composite are 1778 MPa and 2.8% fabricated in steel tube at 900 °C for 10 min, and 1582 MPa and 3.6% fabricated in quartz tube at 850 °C for 10 min, respectively.
基金Project(51575447) supported by the National Natural Science Foundation of ChinaProject supported by Top University around World Visiting Plan for Young Teacher’s Cultivating in NWPU,China
文摘A new method for determining two key parameters(threshold pressure and permeability)for fabricating metal matrix composites was proposed based on the equation-solving method.An infiltration experimental device was devised to measure the infiltration behavior precisely with controllable infiltration velocity.Two experiments with alloy Pb-Sn infiltrating into Al2O3 preform were conducted independently under two different pressures so as to get two different infiltration curves.Two sets of coefficients which are functions of threshold pressure and permeability can be obtained through curve fitting method.By solving the two-variable equation set,two unknown variables were determined.It is shown that the determined threshold pressure and permeability are very close to the calculated ones and are also verified by another independent infiltration experiment.The proposed method is also feasible to determine the key infiltration parameters for other metal matrix composite systems.