碳化钨、钨及其复合物料中痕量砷的测定

对碳化钨样品中的痕量砷进行了分析测定,试样以硝酸、氢氟酸低温溶解,硫—磷混酸冒烟驱除硝酸和氢氟酸,用预还原剂还原高价砷(Ⅴ)为低价砷(Ⅲ),进行氢化物原子吸收光谱测定,测得结果与摄谱法及分光光度法结果一致。

复合物料片材

库尔兹新推出的复合物材料片材——IML片材是一种连续性的木纹箔，亦可以是连续性的金属拉丝箔。IML片材可通过真空吸塑及模切手段完成预成型工序，预成型后的嵌片可在相匹配的注塑模具中完成注塑工序。

复配乳液聚合物水泥防水涂料防护效果研究

本文以丙烯酸酯乳液和氯丁橡胶乳液复配的方法制备聚合物水泥防水涂料,以解决单一聚合物乳液水泥防水涂料在应用过程中易开裂、柔性不足等问题。将其涂覆于水泥砂浆试块表面,探讨了涂层对氯盐侵蚀、硫酸盐侵蚀、冻融循环、自然环境侵蚀下水泥砂浆试块质量、抗压强度的影响,分析了涂层对试块的防护效果。结果显示涂层水泥砂浆试块均无开裂、剥落现象,试块的质量损失率、抗压强度损失率均较小。采用复配乳液并添加外加剂制得涂层对水泥砂浆试块的防护效果最优,试块在氯盐、硫酸盐侵蚀180天、冻融循环100次后的抗压强度损失率分别为9.45%、10.84%、12.16%,自然环境侵蚀120天后,试块抗压强度可保持为29.80MPa远高于无涂层试块。还以其中防护效果最优配方制备聚合物水泥防水涂料,探讨了涂层涂覆方法对自然环境侵蚀下涂层水泥砂浆试块抗压强度的影响。结果显示固定涂层厚度,分多次涂覆制得涂层更致密,交叉涂覆方法制得涂层厚度更均匀,沿十字交叉方向分三次涂覆制得涂层对水泥砂浆试块的防护效果更优。

Preparation and Anti⁃arc Erosion Property of Ag Matrix Electrical Contact Material Reinforced by Novel Ti_(2)Cd

Due to their outstanding electrical contact properties,Cd-containing silver-matrix electrical contact materials can meet the requirements of high stability and long life for military defense and aerospace applications.In order to further reduce the Cd content under the premise of meeting the high-performance requirements,in this study,high-purity intermediate Ti_(2)Cd powder of MAX phase(Ti_(2)CdC)was synthesized with a pressureless technique and then applied to reinforce the Ag matrix.The Cd content of the as-prepared Ag/Ti_(2)Cd composites was actually reduced by 38.31%compared with conventional Ag/CdO material.Based on the systematic study of the effect of heat treatment temperature on the physical phase,morphology,interface and comprehensive physical properties of Ag/Ti_(2)Cd composites,the preferred samples(heat treated at 400°C for 1 h)showed high density(97.77%),low resistivity(2.34μΩ·cm),moderate hardness(90.8HV),high tensile strength(189.9 MPa),and exhibited good electrical contact performance after 40000 cycles of arc discharging under severe conditions(DC 28 V/20 A).The results of microscopic morphological evolution,phase change and elemental distribution of the electrical contact surface show that the combination of high stability of Ti_(2)Cd reinforcing phase,good interfacial bonding with Ag matrix and improved melt pool viscosity in the primary stage of arc erosion,results in low and stable contact resistance(average value 13.20 mΩ)and welding force(average value 0.6 N),low fluctuation of static force(2.2-2.5 N).The decomposition and absorption energy of Ti_(2)Cd and the arc extinguishing effect of Cd vapor are the main reasons for the stable arcing energy and arcing time of electric contacts in the late stage of arc erosion.

汽车车身材料革命颠覆汽车生产工艺

全身主要由复合材料制作的波音787飞机，完成了大型民用飞机由传统的铝合金向碳纤维增强塑料复合材料的转变。新飞机所用材料按体积计算，复合材料占到80％。按重量计算则为：50％复合物料，20％铝，10％钢和20％的其他材料。

Microstructure and wear resistance of laser clad TiB-TiC/TiNi-Ti_2Ni intermetallic coating on titanium alloy

A wear resistant TiB-TiC reinforced TiNi-Ti2Ni intermetallic matrix composite coating（TiB-TiC/TiNi-Ti2Ni） was prepared on Ti-6.5Al-2Zr-1Mo-1V titanium alloy by the laser cladding process using Ti＋Ni＋B4C powder blends as the precursor materials.Microstructure and worn surface morphologies of the coating were characterized by optical microscopy（OM）,scan electron microscopy（SEM）,X-ray diffraction（XRD）,energy dispersive X-ray analysis（EDS） and atomic force microscopy（AFM）.Wear resistance of the coating was evaluated under dry sliding wear test condition at room temperature.The results indicate that the laser clad coating has a unique microstructure composed of flower-like TiB-TiC eutectic ceramics uniformly distributed in the TiNi-Ti2Ni dual-phase intermetallic matrix.The coating exhibits an excellent wear resistance because of combined action of hard TiB-TiC eutectic ceramic reinforcements and ductile TiNi-Ti2Ni dual-phase intermetallic matrix.

EFFECT OF COMPOSITE MINERAL ADMIXTURES ON RESTRAINING ALKALI-SILICA REACTION

The expansion and micro-cracks of the mortar with composite mineral admixtures （fly ash, zeolite and slag） due to the alkali-silica reaction （ASR） are studied. Results show that composite mineral admixtures cannot absolutely diminish the ASR of mortar bars with the low-alkali cement and a highly reactive aggregate. But the expansion rate and the deleterious expansion of the mortar bar are mostly reduced with increasing composite mineral admixture. The influence of mineral admixtures on the fluidity of the paste and the strength of the mortar is also studied.

Characterisation of wear particles from biomedical carbon/carbon composites with different preforms in hip joint simulator

A hip joint simulator was employed to predict the clinical wear behaviour of carbon/carbon （C/C） composites with needled carbon cloth preform and carbon felt preform. Wear particles generated from the two kinds of C/C composites were isolated and characterised by the size distribution and morphology. The evolvement of wear particles in the hip joint simulator was proposed. The results show that the wear particles from two kinds of C/C composites have a size ranging from submicron to tens of micrometers. The wear particles have various morphologies including broken fiber, fragment fiber, slice pyrolytic carbon and spherical pyrolytic carbon. C/C composites with needled carbon cloth preforms have larger size range and more broken fiber particles and slice pyrolytic carbon particles in comparison with C/C composites with carbon felt preforms. The evolvement of pyrolytic carbon particles is caused by surface regularization, whereas, the evolvement of carbon fiber particles is related to stress direction in the hip joint simulator.

WC-Ni_3Al-B composites prepared through Ni+Al elemental powder route

In order to develop the liquid phase sintering process of WC-Ni3Al-B composites,the preparation process of WC＋Ni3Al prealloyed powder by reaction synthesis of carbonyl Ni,analytical purity Al and coarse WC powders was investigated.DSC and XRD were adopted to study the procedure of phase transformation for the 3Ni＋Al and 70%WC＋（3Ni＋Al） mixed powders in temperature ranges of 550-1200 °C and 25-1400 °C,respectively.The results demonstrate that the formation mechanism of Ni3Al depends on the reaction temperature.Besides WC phase,there exist Ni2Al3,NiAl and Ni3Al intermetallics in the powder mixture after heat treatment at 200-660 °C,while only NiAl and Ni3Al exist at 660-1100 °C.Homogeneous WC＋Ni3Al powder mixture can be obtained in the temperature range of 1100-1200 °C.The WC-30%（Ni3Al-B） composites prepared from the mixed powders by conventional powder metallurgy technology show nearly full density and the shape of WC is round.WC-30%（Ni3Al-B） composites exhibit higher hardness of 9.7 GPa,inferior bending strength of 1800 MPa and similar fracture toughness of 18 MPa-m1/2 compared with commercial cemented carbides YGR45（WC-30%（Co-Ni-Cr））.

Effects of chitosan coating on biocompatibility of Mg-6%Zn-10%Ca_3(PO_4)_2 implant

A Mg?6%Zn?10%Ca3(PO4)2 composite with a chitosan coating was prepared to study its in vivo biodegradation properties. The chitosan dissolved in a 0.2% acetic acid solution was applied on the surface of Mg?6%Zn?10%Ca3(PO4)2 composite specimens and solidified at 60 °C for 30 min to form the coating. The cytotoxicity evaluation of chitosan coated specimens is at level 0, which indicates that such coating is safe for cellular applications. The in vivotests of chitosan coated composite show that the concentration of metal ions from the composite measured in the venous blood of Zelanian rabbits is less than that from the uncoated composite specimens. The chitosan coating impedes the in vivo degradation of the composite after surgery. The in vivo testing also indicates that the chitosan coated composite is harmless to important visceral organs, including the heart, kidneys and liver of the rabbits. The new bone formation surrounding the chitosan coated composite implant shows that the composite improves the concrescence of the bone tissues. And the chitosan coating is an effective corrosion resistant layer that reduces the hydrogen release of the implant composite, thereby decreasing the subcutaneous gas bubbles formed.

Multilayered Ti-Al intermetallic sheets fabricated by cold rolling and annealing of titanium and aluminum foils

Multilayered Ti-Al based intermetallic sheets were fabricated by sintering alternately layered titanium and aluminum foils.The microstructure and phase formation of the obtained sheets under different sintering conditions were evaluated by various techniques.The results reveal that when the sintering temperature is above the melting point of aluminum,the self-propagating high-temperature synthesis reaction occurs between Ti and Al,and forms various phases of Ti-based solid solutions including α-Ti Ti3Al,TiAl,TiAl2 and α-Ti including TiAl3,etc.When the sintering time increased,Ti-based solid solution,TiAl2 and TiAl3 disappeared gradually,and the sheet containing Ti3Al and TiAl phases in a multilayered structure formed finally.A lot of voids were also observed in the sintered structures,which were caused by the melting Al,Kirkendall effect and the difference of molar volumes between reactants and products.The voids were eliminated and a dense sample was obtained by the following hot press.

Photocatalytic Degradation of Water-Soluble Dyes by LaCoO_3

Pervoskite type oxides LaCoO 3 was prepared by citrate method with the granula of 20 nm-30 nm. With a fluorescent Hg lamp or sunlight as irradiator, the degradation experiments of various water soluble dyes were carried out in the suspension system of LaCoO 3 . The results show that the pervoskite type oxide LaCoO 3 has good photocatalytic activity.Studied by X ray photoelectron spectroscopy and photoacoustic spectra, its photocatalytic activity is found to be related with factors such as the d electron structure of ion Co 3+ ,Co—O binding energy and adsorbed oxygen on the surface etc.

Prediction of the thermo-elastic properties of knitted structural composites using FEM

It is a very important and complex task to estimate the thermo-elasticproperties of a textile structural composite. In this paper, the finite element method (FEM) wasused for the prediction of the orthotropic thermo-elastic properties of a composite reinforced byglass fiber knitted fabric. In order to define the final 3-D configuration of the loop reinforcingstructure, the interactions between the adjacent loops, the large displacement and the contactelements without friction were considered. The values predicted were compared with the experimentalresults.

Laser-weldable Si_p-SiC_p/Al hybrid composites with bilayer structure for electronic packaging

Laser-weldable Sip-SiCp/Al hybrid composites with high volume fraction （60%-65%） of SiC reinforcement were fabricated by compression moulding and vacuum gas pressure infiltration technology. Microscopic observation displayed that the Sip-SiCp/Al hybrid composites with bilayer structure were compact without gas pores and the intergradation between Sip/Al layer and SiCp/Al layer was homogeneous and continuous. Further investigation revealed that the Sip-SiCp/Al hybrid composites possessed low density （2.96 g/cm^3）, high gas tightness （1.0 mPa·cm^3）/s）, excellent thermal management function as a result of high thermal conductivity （194 W/（m·K） and low coefficient of thermal expansion （7.0×10^-6 K-1）. Additionally, Sip-SiCp/Al hybrid composites had outstanding laser welding adaptability, which is significantly important for electronic packaging applications. The gas tightness of components after laser welding （48 mPa·cm^3）/s） can well match the requirement of advanced electronic packaging. Several kinds of these precision components passed tests and were put into production.

Solid-state bonding between Al and Cu by vacuum hot pressing

Diffusion bonding between aluminum and copper was performed by vacuum hot pressing at temperatures between 623 and 923 K through two thermal processes： hot compression under the deformation rate of 0.2 mrrdmin for 10 rain at pre-set temperatures, and additional pressing at 0.2 mm/min for 20 rain during furnace cooling. After analyzing interface, the feasible diffusion bonding temperature was suggested as 823 K. The three major intermetallic layers generated during diffusion bonding process were identified as AIECu, AlCu＋AlaCu4 and Al4Cu9. Furthermore, local hardness values ofAlECU, AlCu＋AlaCu4 and Al4Cu9 layers average at （4.97±0.05）, （6.33±0.00） and （6.06±0.18） GPa, respectively.

Surface modification of calcium carbonate:A review of theories,methods and applications

Calcium carbonate,which is widely employed as a filler added into the polymer matrix,has large numbers of applications owing to the excellent properties such as low cost,non-toxicity,high natural reserves and biocompatibility.Nevertheless,in order to obtain the good filling effect,calcium carbonate needs to be surface modified by organic molecules so as to enhance the dispersion and compatibility within the composites.This review paper systematically introduces the theory,methods,and applications progress of calcium carbonate with surface modification.Additionally,the key factors that affect the properties of the composites as well as the current difficulties and challenges are highlighted.The current research progress and potential application prospects of calcium carbonate in the fields of plastics,rubber,paper,medicine and environmental protection are discussed as well.Generally,this review can provide valuable reference for the modification and comprehensive utilization of calcium carbonate.

In vitro degradation and cytotoxicity of Mg-5Zn-0.3Ca/n HA biocomposites prepared by powder metallurgy

Mg-5Zn-0.3Ca/nHA biocomposites were prepared from pure Mg,Zn,Ca and nano-hydroxyapatite(nHA)powders by powder metallurgy method.The effect of various mass fractions of nHA(1%,2.5%,5%)as reinforcement on the corrosion properties of Mg-5Zn-0.3Ca alloy was investigated.The corrosion resistance of biocomposite samples was investigated by immersion tests and electrochemical techniques in SBF solution.The results showed that the corrosion resistance of Mg alloy was improved by adding 1%and 2.5%nHA.Bioactive nHA motivated the formation of stable phosphate and carbonate layers on surface and improved corrosion resistance of nanocomposites.However,addition of large contents of nHA in Mg alloy as reinforcement increased the density of this precipitated layer,so gases produced from localized corrosion were accumulated underneath this layer and decreased its adhesiveness and lowered its corrosion resistance.Indirect cytotoxicity evaluation for Mg alloy and its nanocomposites also showed that their extraction was not toxic and nanocomposite with 1%nHA indicated almost similar behavior as negative control.

Research advances of light-driven hydrogen evolution using polyoxometalate-based catalysts

With the increasing concerns to energy shortage and environmental problems in modern society,the development of cheap,clean,and sustainable energy alternatives has been attracting tremendous attention globally.Among various strategies of renewable energy exploration,solar-driven water splitting into its compositional elements H2 and O2 is an ideal approach to convert and store renewable solar energy into chemical bonds.In recent few decades,as an emerging new type of catalysts,polyoxometalates(POMs)have been widely utilized for water splitting due to their versatile synthetic methodology and highly tunable physicochemical and photochemical properties.This critical review addresses the research advances of light-driven hydrogen evolution using polyoxometalate-based catalysts,including plenary POMs,transition-metal-substituted POMs,POM@MOF composites,and POM-semiconductor hybrids,under UV,near UV and visible light irradiation.In addition,the catalytic mechanism for each reaction system has been thoroughly discussed and summarized.Finally,a comprehensive outlook of this research area is also prospected.

Morphology and conductivity of in-situ PEO-LiClO_4-TiO_2 composite polymer electrolyte

PEO-LiClO4-TiO2 composite polymer electrolyte films were prepared. TiO2 was formed directly in matrix by hydrolysis and condensation reaction of tetrabutyl titanate. The crystallinity, morphology and ionic conductivity of composite polymer electrolyte films were examined by differential scanning calorimetry, scanning electron microscopy, atom force microscopy and alternating current impedance spectroscopy, respectively. The glass transition temperature and the crystallinity of composite polymer electrolytes are decreased compared with those of PEO-LiClO4 polymer electrolyte film. The results show that TiO2 particles are uniformly dispersed in PEO-LiClO4-5%TiO2 composite polymer electrolyte film. The maximal conductivity of 5.5×10、5 Scm at 20 ℃ of PEO-LiClO4-TiO2 film is obtained at 5% mass fraction of TiO2.