A modified horizontal continuous casting process under the electromagnetic field was proposed for preparing AA3003/ AA4045 clad composite hollow billets. To investigate the effect of electromagnetic field on this proc...A modified horizontal continuous casting process under the electromagnetic field was proposed for preparing AA3003/ AA4045 clad composite hollow billets. To investigate the effect of electromagnetic field on this process, a comprehensive three-dimensional model was developed. Two cases with and without electromagnetic field were compared using the simulations. When rotating electromagnetic stirring is applied, the flow pattern of fluid melt is greatly modified; the mushy zone becomes much wider, the temperature profile becomes more uniform, and the solid fraction decreases for both the external and internal alloy melt layers. These modifications are beneficial for the formation of a bimetal interface and fine and uniform grain structure of the clad composite hollow billet. Experiments conducted using the same electrical and casting parameters as the simulations verify that under the electromagnetic field the microstructure of the clad composite hollow billet becomes fine and the diffusion of the elements at the interface is promoted.展开更多
6009/7050 alloy bimetal slab was prepared by a direct-chill (DC) casting process. Homogenizing annealing, hot rolling and T6 treatment were successively performed and their effects on microstructure and properties of ...6009/7050 alloy bimetal slab was prepared by a direct-chill (DC) casting process. Homogenizing annealing, hot rolling and T6 treatment were successively performed and their effects on microstructure and properties of the slab were studied. The results reveal that the average diffusion layer thickness of as-cast slab, determined by interdiffusion of elements Zn, Cu, Mg and Si, was about 400 μm. Excellent metallurgical bonding was achieved because all tensile samples fractured on the softer 6009 alloy side after homogenizing annealing. After homogenizing annealing plus rolling, the average diffusion layer thickness decreased to 100 μm, while the network structure of 7050 alloy side transformed to dispersive nubby structure. Furthermore, subsequent T6 treatment resulted in diffusion layer thickness up to 200 μm and an obvious increase of the Vickers hardness for both 7050 and 6009 sides. The layered structure of the as-cast 6009/7050 bimetal is retained after hot rolling and T6 treatment.展开更多
Three-layer6009/7050/6009aluminum alloy clad slab was fabricated by an innovative direct-chill casting process.To study the response of the clad slab to plastic deformation and heat treatments,homogenization annealing...Three-layer6009/7050/6009aluminum alloy clad slab was fabricated by an innovative direct-chill casting process.To study the response of the clad slab to plastic deformation and heat treatments,homogenization annealing,hot rolling,solution and aging were successively performed on the as-cast6009/7050/6009clad samples.The results revealed that excellent metallurgical bonding between7050alloy layer and6009alloy layer was achieved under optimal parameters.The clad ratio obviously decreased when the annealed sample was rolled to55%hot reduction level,and then changed slightly with further rolling.Furthermore,the content of rodlike Zn-rich phases increased significantly in7050alloy layer in the homogenized clad samples after rolling at55%,65%and75%hot reduction levels,and the higher level of hot reduction resulted in narrower diffusion layer.Subsequent solution and aging significantly improved the hardness in7050alloy layer,interfaces and6009alloy layers of the rolled samples except for the thin side for the75%hot reduction sample.展开更多
基金Projects(51274054,U1332115,51271042,51375070,51401044)supported by the National Natural Science Foundation of ChinaProject(313011)supported by the Key Grant Project of Ministry of Education of China+4 种基金Project(2013A16GX110)supported by the Science and Technology Planning Project of Dalian,ChinaProject(2014M551075)supported by the China Postdoctoral Science FoundationProject supported by the Fundamental Research Funds for the Central Universities,China
文摘A modified horizontal continuous casting process under the electromagnetic field was proposed for preparing AA3003/ AA4045 clad composite hollow billets. To investigate the effect of electromagnetic field on this process, a comprehensive three-dimensional model was developed. Two cases with and without electromagnetic field were compared using the simulations. When rotating electromagnetic stirring is applied, the flow pattern of fluid melt is greatly modified; the mushy zone becomes much wider, the temperature profile becomes more uniform, and the solid fraction decreases for both the external and internal alloy melt layers. These modifications are beneficial for the formation of a bimetal interface and fine and uniform grain structure of the clad composite hollow billet. Experiments conducted using the same electrical and casting parameters as the simulations verify that under the electromagnetic field the microstructure of the clad composite hollow billet becomes fine and the diffusion of the elements at the interface is promoted.
基金Project (51375070) supported by the National Natural Science Foundation of China
文摘6009/7050 alloy bimetal slab was prepared by a direct-chill (DC) casting process. Homogenizing annealing, hot rolling and T6 treatment were successively performed and their effects on microstructure and properties of the slab were studied. The results reveal that the average diffusion layer thickness of as-cast slab, determined by interdiffusion of elements Zn, Cu, Mg and Si, was about 400 μm. Excellent metallurgical bonding was achieved because all tensile samples fractured on the softer 6009 alloy side after homogenizing annealing. After homogenizing annealing plus rolling, the average diffusion layer thickness decreased to 100 μm, while the network structure of 7050 alloy side transformed to dispersive nubby structure. Furthermore, subsequent T6 treatment resulted in diffusion layer thickness up to 200 μm and an obvious increase of the Vickers hardness for both 7050 and 6009 sides. The layered structure of the as-cast 6009/7050 bimetal is retained after hot rolling and T6 treatment.
基金Projects(51375070,51574058) supported by the National Natural Science Foundation of China
文摘Three-layer6009/7050/6009aluminum alloy clad slab was fabricated by an innovative direct-chill casting process.To study the response of the clad slab to plastic deformation and heat treatments,homogenization annealing,hot rolling,solution and aging were successively performed on the as-cast6009/7050/6009clad samples.The results revealed that excellent metallurgical bonding between7050alloy layer and6009alloy layer was achieved under optimal parameters.The clad ratio obviously decreased when the annealed sample was rolled to55%hot reduction level,and then changed slightly with further rolling.Furthermore,the content of rodlike Zn-rich phases increased significantly in7050alloy layer in the homogenized clad samples after rolling at55%,65%and75%hot reduction levels,and the higher level of hot reduction resulted in narrower diffusion layer.Subsequent solution and aging significantly improved the hardness in7050alloy layer,interfaces and6009alloy layers of the rolled samples except for the thin side for the75%hot reduction sample.