SiC granule films were fabricated onto porous glass substrate by RF-magnetron sputtering. Photoluminescence （PL） measurements show that there are light emissions at three different wavelengths. Ultraviolet emission ...SiC granule films were fabricated onto porous glass substrate by RF-magnetron sputtering. Photoluminescence （PL） measurements show that there are light emissions at three different wavelengths. Ultraviolet emission peaked at 360 nm originated from the band-band transmission of SiC nanoparticles with relatively small size. The 370 nm light emission was due to the luminescence of the nano-skeletons of porous glass that was formed during the etching of the glass substrate. The blue emission at about 460 nm was associated with the recombination of the excited electron and O-deficient defects appeared at the interface between SiC nanoparticles and the porous glass. Furthermore, the optimal PL performance was obtained when SiC deposited time was I h and the glass substrate was etched for 20 min in the annealing sample （450 ℃）.展开更多
基金National Science Foundation of China (10774037)Natural Science Foundation of Hebei Province (E2007000280)Foundation of Hebei Educational Committee (2006123)
文摘SiC granule films were fabricated onto porous glass substrate by RF-magnetron sputtering. Photoluminescence （PL） measurements show that there are light emissions at three different wavelengths. Ultraviolet emission peaked at 360 nm originated from the band-band transmission of SiC nanoparticles with relatively small size. The 370 nm light emission was due to the luminescence of the nano-skeletons of porous glass that was formed during the etching of the glass substrate. The blue emission at about 460 nm was associated with the recombination of the excited electron and O-deficient defects appeared at the interface between SiC nanoparticles and the porous glass. Furthermore, the optimal PL performance was obtained when SiC deposited time was I h and the glass substrate was etched for 20 min in the annealing sample （450 ℃）.