A procedure of low temperature solid-phase sintering（LTSS） was carried out to fabricate sintered metal fibrous media（SMFM） with high specific surface area.Stainless steel fibers which were produced by cutting proc...A procedure of low temperature solid-phase sintering（LTSS） was carried out to fabricate sintered metal fibrous media（SMFM） with high specific surface area.Stainless steel fibers which were produced by cutting process were first plated with a coarse copper coating layer by electroless plating process.A low-temperature sintering process was then completed at about 800 °C for 1 h under the protection of hydrogen atmosphere.The results show that a novel SMFM with complex surface morphology and high specific surface area（0.2 m2/g） can be obtained in this way.The effect of sintering temperature on the surface morphology and specific surface area of SMFM was studied by means of scanning electron microscopy and Brunauer-Emmett-Teller.The damage of micro-structure during the sintering process mainly contributed to the loss of specific surface area of SMFM and the optimal sintering temperature was 800 °C.展开更多
Copper porous materials have been manufactured by the method of powder metallurgy.Electrolytic copper powders and atomized copper powders are used as matrix material.Methylcellulose and paraffin are used as porogen.Th...Copper porous materials have been manufactured by the method of powder metallurgy.Electrolytic copper powders and atomized copper powders are used as matrix material.Methylcellulose and paraffin are used as porogen.The influence of porogen type and copper powder morphology on the property of copper porous materials is investigated as well.The results show that copper porous materials with paraffin as porogen have lower porosity and permeability compared with materials using methylcellulose as porogen,due to the different pore-forming mechanisms.The pore forming mechanism of methylcellulose is thermal decomposition,while the pore forming mechanism of paraffin is melting–evaporation.The morphology of copper powders affects the contact state between adjacent powders,which further influence the sintering shrinkage.The porous materials using arborescent copper powders as matrix have lower porosity,smaller pore size and lower permeability,compared with materials with atomized copper powders as matrix.展开更多
This paper introduces the classification, properties and application of porous ceramic materials, reviewed preparation of porous ceramics. Taking fly ash and red mud as the main raw material to generate porous ceramic...This paper introduces the classification, properties and application of porous ceramic materials, reviewed preparation of porous ceramics. Taking fly ash and red mud as the main raw material to generate porous ceramics, the paper study the influence of different proportions of raw materials, sintering temperature, porosity of porous ceramic sample rate, bending strength, and microstructure. The results show that, fly ash and red mud proportioning and sintering temperature are the main factors that influence the structure and properties of samples. The4#sample is a kind of high porosity and high strength quality of porous ceramics.展开更多
基金Project (50930005) supported by the National Natural Science Foundation of ChinaProject (U0834002) supported by the Key Programof NSFC-Guangdong Joint Funds of China+1 种基金Project (LYM09024) supported by Training Program for Excellent Young Teachers withInnovation of Guangdong University, ChinaProject (2009ZM0121) supported by the Fundamental Research Funds for the CentralUniversities of South China University of Technology,China
文摘A procedure of low temperature solid-phase sintering（LTSS） was carried out to fabricate sintered metal fibrous media（SMFM） with high specific surface area.Stainless steel fibers which were produced by cutting process were first plated with a coarse copper coating layer by electroless plating process.A low-temperature sintering process was then completed at about 800 °C for 1 h under the protection of hydrogen atmosphere.The results show that a novel SMFM with complex surface morphology and high specific surface area（0.2 m2/g） can be obtained in this way.The effect of sintering temperature on the surface morphology and specific surface area of SMFM was studied by means of scanning electron microscopy and Brunauer-Emmett-Teller.The damage of micro-structure during the sintering process mainly contributed to the loss of specific surface area of SMFM and the optimal sintering temperature was 800 °C.
基金Project(2015DFR50580)supported by International S&T Cooperation Program of ChinaProject(51505503)supported by the National Natural Science Foundation of China
文摘Copper porous materials have been manufactured by the method of powder metallurgy.Electrolytic copper powders and atomized copper powders are used as matrix material.Methylcellulose and paraffin are used as porogen.The influence of porogen type and copper powder morphology on the property of copper porous materials is investigated as well.The results show that copper porous materials with paraffin as porogen have lower porosity and permeability compared with materials using methylcellulose as porogen,due to the different pore-forming mechanisms.The pore forming mechanism of methylcellulose is thermal decomposition,while the pore forming mechanism of paraffin is melting–evaporation.The morphology of copper powders affects the contact state between adjacent powders,which further influence the sintering shrinkage.The porous materials using arborescent copper powders as matrix have lower porosity,smaller pore size and lower permeability,compared with materials with atomized copper powders as matrix.
文摘This paper introduces the classification, properties and application of porous ceramic materials, reviewed preparation of porous ceramics. Taking fly ash and red mud as the main raw material to generate porous ceramics, the paper study the influence of different proportions of raw materials, sintering temperature, porosity of porous ceramic sample rate, bending strength, and microstructure. The results show that, fly ash and red mud proportioning and sintering temperature are the main factors that influence the structure and properties of samples. The4#sample is a kind of high porosity and high strength quality of porous ceramics.