多束系统对12Cr-ODS钢辐照损伤协同效应的研究

室温下用不同种类的离子束对12Cr-ODS钢进行辐照。辐照前后12Cr-ODS钢的力学性能发生了明显变化,主要表现为辐照肿胀和辐照硬化,其中三束辐照下材料有最大的肿胀和最小的硬化。结合TEM照片对材料的辐照变化进行了分析。对材料进行拉曼光谱的测量,发现有碳析出现象,并且把碳峰的强度分布与辐照损伤分布进行了相互关联。本文为12Cr-ODS钢在实际反应堆中的应用积累了实验数据,明确了协同作用对核材料辐照损伤的影响。

多束质子辐照晶闸管的退火研究

研究了多束质子辐照对晶闸管开关特性和通态电压的影响，分析了退火机理，找出了最佳退火流程，获得了优良的通态电压与关断的时间（ＶＴＭ－Ｔｑ）的折衷关系。

关于多束质子辐照晶闸管的退火研究

作者研究了多束质子辐照对晶闸管开关特性和通态电压的影响 ,分析了退火机理 ,找出了最佳退火流程 ,获得了优良的通态电压与关断时间 (VTM～Tq)的折衷关系 .

Effect of electron beam irradiation on multi-walled carbon nanotubes

Multi-walled carbon nanotubes （MWCNTs） were irradiated with focused electron beams in a transmission electron microscope at room temperature. The results showed that carbon nanotubes had no obvious structural damages but only shell bending under 100 keV electron beam irradiation. However, when the electron energy increased to 200 keV, the nanotubes were damaged and amorphization, pits and gaps were detected. Furthermore, generating of carbon onions and welding between two MWCNTs occurred under 200 keV electron irradiation. It was easy to destroy the MWCNTs as the electron beams exceeded the displacement threshold energy that was calculated to be 83-110 keV. Conversely, the energy of electron beams below the threshold energy was not able to damage the tubes. The damage mechanism is sputtering and atom displacement.

核材料辐照损伤协同效应的研究

通过拉曼光谱、沟道背散射、原子力显微镜、透射电子显微镜、红外光谱等一系列测试手段对Zr O2,Si C和ODS钢三种核材料的多束辐照行为进行表征,研究离子束的协同效应对核材料辐照损伤的影响。Zr O2双束辐照肿胀和损伤是两个单束辐照的线性叠加,Si C双束同时辐照的拉曼光谱比双束先后辐照有更大的主峰半高宽的变化,ODS钢的三束辐照有最大的肿胀和硬化。综合分析得出双束同时辐照比先后辐照具有更明显的协同效应,三束辐照ODS钢的损伤最严重,比三个单束损伤之和大,Si离子与He,H的协同效应最明显。多束辐照能较好地模拟实际反应堆中的辐照环境。这些研究结果对于核材料在实际反应堆中的中子辐照行为具有一定的参考意义。