The isothermal oxidation behavior of NiAl-31Cr-2.9Mo-0.1Hf-0.05Ho directional eutectic alloy was investigated with the help of scanning electron microscopy and X-ray diffraction.The results revealed that a continuous ...The isothermal oxidation behavior of NiAl-31Cr-2.9Mo-0.1Hf-0.05Ho directional eutectic alloy was investigated with the help of scanning electron microscopy and X-ray diffraction.The results revealed that a continuous Al2O3 scale was formed and owned excellent oxidation resistance in the temperature range of 900-1100°C.When the temperature was up to 1150°C,the continuous Al2O3 oxide film ruptured.Trace rare earth element Ho distributed uniformly in the alloy and relatively high level of Al in Cr（Mo）phase are beneficial to the formation of continuous and compact Al2O3 scale.During the oxidation,a phase transformation fromθ-Al2O3 toα-Al2O3 existed on the surface of oxidation film.It resulted in the abnormal oxidation mass gain happening when the alloy was oxidized at 1000°C or 1050°C.展开更多
Single-phase Ag2Al intermetallic nanoparticles, and Ag and Al metallic nanoparticles were synthesized by the flow-levitation （FL） method. Measurements of d-spacings from X-ray diffraction and electron diffraction co...Single-phase Ag2Al intermetallic nanoparticles, and Ag and Al metallic nanoparticles were synthesized by the flow-levitation （FL） method. Measurements of d-spacings from X-ray diffraction and electron diffraction confirmed that the intermetallic nanoparticles had the hexagonal Ag2Al structure. The morphology, crystal structure and chemical composition of Ag2Al nanoparticles were investigated by transmission electron microscopy, X-ray diffraction and induction-coupled plasma spectroscopy. A thin amorphous coating was formed around the particles when exposed to air. Based on the XPS measurements, the surface coating of the Ag2Al nanoparticles could most likely be aluminum oxide or silver aluminum oxide. Therefore, the single-phase nanocrystalline Ag2Al intermetallic compound particles can be produced by adjusting some experimental parameters in FL method.展开更多
基金Project(51101055)supported by the National Natural Science Foundation of China
文摘The isothermal oxidation behavior of NiAl-31Cr-2.9Mo-0.1Hf-0.05Ho directional eutectic alloy was investigated with the help of scanning electron microscopy and X-ray diffraction.The results revealed that a continuous Al2O3 scale was formed and owned excellent oxidation resistance in the temperature range of 900-1100°C.When the temperature was up to 1150°C,the continuous Al2O3 oxide film ruptured.Trace rare earth element Ho distributed uniformly in the alloy and relatively high level of Al in Cr（Mo）phase are beneficial to the formation of continuous and compact Al2O3 scale.During the oxidation,a phase transformation fromθ-Al2O3 toα-Al2O3 existed on the surface of oxidation film.It resulted in the abnormal oxidation mass gain happening when the alloy was oxidized at 1000°C or 1050°C.
基金Project (10804101) supported by the National Natural Science Foundation of China
文摘Single-phase Ag2Al intermetallic nanoparticles, and Ag and Al metallic nanoparticles were synthesized by the flow-levitation （FL） method. Measurements of d-spacings from X-ray diffraction and electron diffraction confirmed that the intermetallic nanoparticles had the hexagonal Ag2Al structure. The morphology, crystal structure and chemical composition of Ag2Al nanoparticles were investigated by transmission electron microscopy, X-ray diffraction and induction-coupled plasma spectroscopy. A thin amorphous coating was formed around the particles when exposed to air. Based on the XPS measurements, the surface coating of the Ag2Al nanoparticles could most likely be aluminum oxide or silver aluminum oxide. Therefore, the single-phase nanocrystalline Ag2Al intermetallic compound particles can be produced by adjusting some experimental parameters in FL method.