Advanced run-out table cooling technology based on ultra fast cooling and laminar cooling in hot strip mill

In order to meet the severe requirements of market and reduce production costs of high quality steels,advanced run-out table cooling based on ultra fast cooling(UFC) and laminar cooling(LC) was proposed and applied to industrial production.Cooling mechanism of UFC and LC was introduced first,and then the control system and control models were described.By using UFC and LC,low-cost Q345B strips had been produced in a large scale,and industrial trials of producing low-cost dual phase strips were completed successfully.Application results show that the ultra fast cooling is uniform along the strip width and length,and does not affect the flatness of strips.The run-out table cooling system runs stably with a high precision,and makes it possible for the user to develop more high quality steels with low costs.

FeTiP相在高强IF钢热轧过程中析出行为的研究

利用电阻炉、Gleeble热模拟试验机和透射电镜,分析了高强IF钢中FeTiP相在热轧过程的析出行为。结果表明,高强IF钢连铸坯中心位置存在少量的FeTiP相析出物,但经过加热和长时间保温,析出物可完全回溶;在热轧过程中,轧制温度范围内的应变诱导析出物主要为TiS相、Ti4C2S2相和TiC相,难以捕捉到明显的FeTiP相存在;FeTiP相的析出主要发生于带钢卷取过程,层冷冷速对FeTiP相和P元素在晶界析出有重要的影响,当层冷冷速为10℃/s时,晶界处易发现棒状和蠕虫状的FeTiP相析出物,同时析出物中的P含量明显升高。因此,可以采取扩大带钢终轧和卷取的温差以及提高层冷冷速等方法来控制热轧带钢晶界处FeTiP相析出物,以利于改变高强IF钢的韧脆转变温度以及提高其深冲性能。