Through the shear tests on composite specimens using four different kinds of tack coat material （epoxy resin, SBS modified emulsified asphalt, SBS modified asphalt and H# bridge waterproof material）, the bond condit...Through the shear tests on composite specimens using four different kinds of tack coat material （epoxy resin, SBS modified emulsified asphalt, SBS modified asphalt and H# bridge waterproof material）, the bond condition between layers of porous asphalt pavement under traffic load, temperature variation and moisture situation is evaluated. The test results show that the bond strength decreases with the rise in temperature, and the relationship between shear strength and temperature can be expressed by a logarithm curve at a high reliability. Under the action of traffic load, the value of shear strength of the mixture right under the centre of the wheel track is smaller than that of other parts of the pavement. It is also found that some effects concerning moisture have comparative effects on the bonding of the two layers. Given all the results achieved during the study, it will be quite rewarding to make rational comparisons during selecting the sound type of tack coat.展开更多
In order to improve the mechanical properties and corrosion resistance of Mg alloys,the equal channel angular extrusion (ECAE)was employed to fabricate the Mg-5Gd-5Y/Mg-2Zn-1Gd(GW55/ZG21)laminated composites.After fab...In order to improve the mechanical properties and corrosion resistance of Mg alloys,the equal channel angular extrusion (ECAE)was employed to fabricate the Mg-5Gd-5Y/Mg-2Zn-1Gd(GW55/ZG21)laminated composites.After fabrication and annealing treatment,the microstructural evolution,phase constitution,microhardness,and bonding strength were investigated on the bonding interface zone of GW55/ZG21 laminated composites.The bonding interface zone of GW55/ZG21 laminated composites comprises a lot of Mg3(Y,Gd)2Zn3 particles along the bonding interface,some rod Mg24(Y,Gd)5 phases on GW55 side,and a precipitation free zone(PFZ)on ZG21 side.After annealing treatment,Mg3(Y,Gd)2Zn3 particles along the bonding interface increase, rod Mg24(Y,Gd)5 phases on GW55 side decrease,and PFZ is broadened.Meanwhile,the hardness on the bonding interface zone decreases and the bonding strength increases from 126 MPa to 162 MPa.展开更多
文摘Through the shear tests on composite specimens using four different kinds of tack coat material （epoxy resin, SBS modified emulsified asphalt, SBS modified asphalt and H# bridge waterproof material）, the bond condition between layers of porous asphalt pavement under traffic load, temperature variation and moisture situation is evaluated. The test results show that the bond strength decreases with the rise in temperature, and the relationship between shear strength and temperature can be expressed by a logarithm curve at a high reliability. Under the action of traffic load, the value of shear strength of the mixture right under the centre of the wheel track is smaller than that of other parts of the pavement. It is also found that some effects concerning moisture have comparative effects on the bonding of the two layers. Given all the results achieved during the study, it will be quite rewarding to make rational comparisons during selecting the sound type of tack coat.
基金Project(2007CB613704)supported by the National Basic Research Program of ChinaProject(50874100)supported by the National Natural Science Foundation of China
文摘In order to improve the mechanical properties and corrosion resistance of Mg alloys,the equal channel angular extrusion (ECAE)was employed to fabricate the Mg-5Gd-5Y/Mg-2Zn-1Gd(GW55/ZG21)laminated composites.After fabrication and annealing treatment,the microstructural evolution,phase constitution,microhardness,and bonding strength were investigated on the bonding interface zone of GW55/ZG21 laminated composites.The bonding interface zone of GW55/ZG21 laminated composites comprises a lot of Mg3(Y,Gd)2Zn3 particles along the bonding interface,some rod Mg24(Y,Gd)5 phases on GW55 side,and a precipitation free zone(PFZ)on ZG21 side.After annealing treatment,Mg3(Y,Gd)2Zn3 particles along the bonding interface increase, rod Mg24(Y,Gd)5 phases on GW55 side decrease,and PFZ is broadened.Meanwhile,the hardness on the bonding interface zone decreases and the bonding strength increases from 126 MPa to 162 MPa.