Various ordered mesoporous carbons （OMCs） have been prepared by evaporation-induced trieonstituent co-assembly method. Their mesostructural stability under different carbon content, aging time and acidity were conve...Various ordered mesoporous carbons （OMCs） have been prepared by evaporation-induced trieonstituent co-assembly method. Their mesostructural stability under different carbon content, aging time and acidity were conveniently monitored by X-ray diffraction, transmission electron microscopy, and N2 sorption isotherms techniques. The results show mesostruetural stability of OMCs is enhanced as the carbon content increases from 36% to 46%, further increasing carbon content deteriorates the mesostructural stability. Increasing aging time from 0.5 h to 5.0 h make the mesostructural stability go through an optimum （2.0 h） and gradually reduce framework shrinkage of the OMCs. Highly OMCs can only be obtained in the acidity range of 0.2-1.2 mol/L HC1, when the acidity is near the isoelectrie point of silica, the resulting OMCs have the best mesostructure stability. Under the optimum condition, the carbon content of 46%, aging time of 2.0 h, and 0.2 mol/L HCl, the resulting OMCs have the best mesostrueture stability and the highest BET surface areas of 2281 m2/g.展开更多
Amphiphilic dendritic poly（glutarnic acid）-b-polyphenylalanine copolymers were synthesized using generation 3 dendritic poly（glutamic acid） as the macroinitiator in the ring-opening polymerization of NCA-Phe. The ...Amphiphilic dendritic poly（glutarnic acid）-b-polyphenylalanine copolymers were synthesized using generation 3 dendritic poly（glutamic acid） as the macroinitiator in the ring-opening polymerization of NCA-Phe. The block copolymers self-assembled micelles with polyphenylalanine segments as core and dendritic poly（glutamic acid） segments as shell. The biocompatibility of the micelles was studied. The release of the anticancer drug doxorubicin from the micelles was investigated in vitro. The results showed that the sustaining release of the drug could last for 60 h. The micellar drug release system was efficient in inhibiting the proliferation of HepG2 liver cancer cells, 75% cancer cells were killed under appropriate in vitro incubation.展开更多
Block copolymers can yield a diverse array of nanostructures.Their assembly structures are influenced by their inherent structures,and the wide variety of structures that can be prepared especially becomes apparent wh...Block copolymers can yield a diverse array of nanostructures.Their assembly structures are influenced by their inherent structures,and the wide variety of structures that can be prepared especially becomes apparent when one considers the number of routes available to prepare block copolymer assemblies.Some examples include self-assembly,directed assembly,coupling,as well as hierarchical assembly,which can yield assemblies having even higher structural order.These assembly routes can also be complemented by processing techniques such as selective crosslinking and etching,the former technique leading to permanent structures,the latter towards sculpted and the combination of the two towards permanent sculpted structures.The combination of these pathways provides extremely versatile routes towards an exciting variety of architectures.This review will attempt to highlight destinations reached by LIU Guojun and coworkers following these pathways.展开更多
A kind of amphiphilic rod-coil diblock copolymer consisting both of tetraaniline(TAni)and polyethylene glycol(PEG)blocks,TAni-b-PEG,was synthesized.The diblock copolymer shows excellent electrochromic properties,espec...A kind of amphiphilic rod-coil diblock copolymer consisting both of tetraaniline(TAni)and polyethylene glycol(PEG)blocks,TAni-b-PEG,was synthesized.The diblock copolymer shows excellent electrochromic properties,especially,in switching time and coloration efficiency compared with tetraaniline.TAni-b-PEG is able to self-assemble into spherical structure,which is attributed to the formation of conducting channels and increase of ion-exchange capacity of TAni-b-PEG,implying that a block copolymer with electrochromic block and high ionic conductive block simultaneously possesses improving electrochromic properties.展开更多
Many technological applications require templates with nanoscale patterns.Block copolymer self-assembly is a method of choice for obtaining a large variety of such patterns,with greatest flexibility achieved when comb...Many technological applications require templates with nanoscale patterns.Block copolymer self-assembly is a method of choice for obtaining a large variety of such patterns,with greatest flexibility achieved when combined with a supramolecular approach.One of the ways to fabricate block copolymer templates is the Langmuir-Blodgett (LB) technique.Here,we briefly summarize recent work with LB films of polystyrene-poly(4-vinyl pyridine) (PS-P4VP) mixed with 3-n-pentade cylphenol (PDP),illustrating the different types of patterns possible and the principles governing them.One interesting pattern that can be easily achieved with this system is the so-called "nanostrand network",which,when used as a template for gold deposition,can produce double striped lines of gold.Here,we show how this pattern can be modified by acetone swelling to give rise to gold monolayer ribbons with internal structure.The results also suggest new insights into the early stages of morphology formation at the air/water interface.展开更多
基金This work was supported by the National Natural Science Foundation of China （No.20872135）.
文摘Various ordered mesoporous carbons （OMCs） have been prepared by evaporation-induced trieonstituent co-assembly method. Their mesostructural stability under different carbon content, aging time and acidity were conveniently monitored by X-ray diffraction, transmission electron microscopy, and N2 sorption isotherms techniques. The results show mesostruetural stability of OMCs is enhanced as the carbon content increases from 36% to 46%, further increasing carbon content deteriorates the mesostructural stability. Increasing aging time from 0.5 h to 5.0 h make the mesostructural stability go through an optimum （2.0 h） and gradually reduce framework shrinkage of the OMCs. Highly OMCs can only be obtained in the acidity range of 0.2-1.2 mol/L HC1, when the acidity is near the isoelectrie point of silica, the resulting OMCs have the best mesostructure stability. Under the optimum condition, the carbon content of 46%, aging time of 2.0 h, and 0.2 mol/L HCl, the resulting OMCs have the best mesostrueture stability and the highest BET surface areas of 2281 m2/g.
基金supported by the National Basic Research Program of China (973 Program,2011CB606206)National High-Tech Research & Development Program of China (863 Program,2007AA021801)+2 种基金National Natural Science Foundation of China (50633020 & 50830105)Sichuan Youth Science & Technology Foundation (07ZQ026-013)Open Fund of Engineering Research Center of Biomass Materials,Ministry of Education (2010LF4002)
文摘Amphiphilic dendritic poly（glutarnic acid）-b-polyphenylalanine copolymers were synthesized using generation 3 dendritic poly（glutamic acid） as the macroinitiator in the ring-opening polymerization of NCA-Phe. The block copolymers self-assembled micelles with polyphenylalanine segments as core and dendritic poly（glutamic acid） segments as shell. The biocompatibility of the micelles was studied. The release of the anticancer drug doxorubicin from the micelles was investigated in vitro. The results showed that the sustaining release of the drug could last for 60 h. The micellar drug release system was efficient in inhibiting the proliferation of HepG2 liver cancer cells, 75% cancer cells were killed under appropriate in vitro incubation.
基金Guojun Liu wishes to thank NSERC of Canada for a Tier 1 Canada Research Chair and for funding
文摘Block copolymers can yield a diverse array of nanostructures.Their assembly structures are influenced by their inherent structures,and the wide variety of structures that can be prepared especially becomes apparent when one considers the number of routes available to prepare block copolymer assemblies.Some examples include self-assembly,directed assembly,coupling,as well as hierarchical assembly,which can yield assemblies having even higher structural order.These assembly routes can also be complemented by processing techniques such as selective crosslinking and etching,the former technique leading to permanent structures,the latter towards sculpted and the combination of the two towards permanent sculpted structures.The combination of these pathways provides extremely versatile routes towards an exciting variety of architectures.This review will attempt to highlight destinations reached by LIU Guojun and coworkers following these pathways.
基金the National Natural Science Foundation of China(21174009,21574003)
文摘A kind of amphiphilic rod-coil diblock copolymer consisting both of tetraaniline(TAni)and polyethylene glycol(PEG)blocks,TAni-b-PEG,was synthesized.The diblock copolymer shows excellent electrochromic properties,especially,in switching time and coloration efficiency compared with tetraaniline.TAni-b-PEG is able to self-assemble into spherical structure,which is attributed to the formation of conducting channels and increase of ion-exchange capacity of TAni-b-PEG,implying that a block copolymer with electrochromic block and high ionic conductive block simultaneously possesses improving electrochromic properties.
基金supported by the Natural Sciences and Engineering Council of Canada (NSERC)the Fonds de recherches du Québec-Nature et Technologies (FQRNT)
文摘Many technological applications require templates with nanoscale patterns.Block copolymer self-assembly is a method of choice for obtaining a large variety of such patterns,with greatest flexibility achieved when combined with a supramolecular approach.One of the ways to fabricate block copolymer templates is the Langmuir-Blodgett (LB) technique.Here,we briefly summarize recent work with LB films of polystyrene-poly(4-vinyl pyridine) (PS-P4VP) mixed with 3-n-pentade cylphenol (PDP),illustrating the different types of patterns possible and the principles governing them.One interesting pattern that can be easily achieved with this system is the so-called "nanostrand network",which,when used as a template for gold deposition,can produce double striped lines of gold.Here,we show how this pattern can be modified by acetone swelling to give rise to gold monolayer ribbons with internal structure.The results also suggest new insights into the early stages of morphology formation at the air/water interface.