Major defects in forming of conical cups are wrinkles and rupture.Hydrodynamic deep drawing assisted by radial pressure（HDDRP） is a sheet hydroforming process for production of shell cups in one step.In this work,pr...Major defects in forming of conical cups are wrinkles and rupture.Hydrodynamic deep drawing assisted by radial pressure（HDDRP） is a sheet hydroforming process for production of shell cups in one step.In this work,process window diagrams（PWDs） for Al1050-O,pure copper and DIN 1623 St14 steel are obtained for HDDRP process.The PWD is determined to provide a quick assessment of part producibility for sheet hydroforming process.Finite element method is used for this purpose considering the process parameters including pressure path,and the blank material and its thickness.Numerical results are validated by experiments.It is shown that the sheets with less initial thickness and higher strength show better formability and uniformity of thickness distribution on final product.The results demonstrate that the obtained PWD can predict appropriate forming area and probability of rupture or wrinkling occurrence under different pressure loading paths.展开更多
A friction stir welding window was developed for effective joining of AA2219 aluminium alloy. Joints were fabricated using different combination of process parameters such as rotational speed and welding speed. Based ...A friction stir welding window was developed for effective joining of AA2219 aluminium alloy. Joints were fabricated using different combination of process parameters such as rotational speed and welding speed. Based on macrostructural analysis, the friction stir welding window was constructed. The strength values of joints at different regions of friction stir welding window were analyzed using tensile properties, microstructural studies, and the fracture location of joints was correlated with the lowest hardness distribution profiles. These windows will act as reference maps for selecting appropriate friction stir welding process parameters to get good quality welds of AA2219 aluminium alloys.展开更多
The stretch forming and the deep-drawing processes were carried out at 300 and 673 K to determine the safe forming and fracture limits of IN625 alloy.The experimentally obtained strain-based fracture forming limit dia...The stretch forming and the deep-drawing processes were carried out at 300 and 673 K to determine the safe forming and fracture limits of IN625 alloy.The experimentally obtained strain-based fracture forming limit diagram(FFLD)was transformed into a stress-based(σ-FFLD)and effective plastic strain(EPS)vs triaxiality(η)plot to remove the excess dependency of fracture limits over the strains.For the prediction of fracture limits,seven different damage models were calibrated.The Oh model displayed the best ability to predict the fracture locus with the least absolute error.Though the experimentally obtained fracture limits have only been used for the numerical analysis,none of the considered damage models predicted the fracture strains over the entire considered range of stress triaxiality(0.33<η<0.66).The deep drawing process window helped to determine wrinkling,safe and fracture zones while drawing the cylindrical cups under different temperature and lubricating conditions.Further,the highest drawing ratio of 2 was achieved at 673 K under the lubricating condition.All the numerically predicted results of both stretch forming and deep drawing processes using the Hill 1948 anisotropic yielding function were found to be good within the acceptable range of error.展开更多
Friction stir spot welding technique was used to join dissimilar combinations of aluminium alloy(Al5052)with copperalloy(C27200)and friction stir spot welding windows such as tool rotational speed–dwell time and tool...Friction stir spot welding technique was used to join dissimilar combinations of aluminium alloy(Al5052)with copperalloy(C27200)and friction stir spot welding windows such as tool rotational speed–dwell time and tool rotational speed?plungedepth diagrams for effective joining of these materials were developed.Using a central composite design model,empirical relationswere developed to predict the changes in tensile shear failure load values and interface hardness of the joints with three processparameters such as tool rotational speed,plunge depth and dwell time.The adequacy of the developed model was verified usingANOVA analysis at95%confidence level.Response surface methodology was used to optimize the developed model to maximizetensile strength and minimize interface hardness.A high tensile shear failure load value of3850N and low interface hardness valueof HV81was observed for joints made under optimum conditions,and validation experiments confirmed the high predictability ofthe developed model with error less than2%.The operating windows developed shall act as reference maps for future designengineers in choosing appropriate friction stir spot welding process parameter values to obtain good joints.展开更多
文摘Major defects in forming of conical cups are wrinkles and rupture.Hydrodynamic deep drawing assisted by radial pressure（HDDRP） is a sheet hydroforming process for production of shell cups in one step.In this work,process window diagrams（PWDs） for Al1050-O,pure copper and DIN 1623 St14 steel are obtained for HDDRP process.The PWD is determined to provide a quick assessment of part producibility for sheet hydroforming process.Finite element method is used for this purpose considering the process parameters including pressure path,and the blank material and its thickness.Numerical results are validated by experiments.It is shown that the sheets with less initial thickness and higher strength show better formability and uniformity of thickness distribution on final product.The results demonstrate that the obtained PWD can predict appropriate forming area and probability of rupture or wrinkling occurrence under different pressure loading paths.
文摘A friction stir welding window was developed for effective joining of AA2219 aluminium alloy. Joints were fabricated using different combination of process parameters such as rotational speed and welding speed. Based on macrostructural analysis, the friction stir welding window was constructed. The strength values of joints at different regions of friction stir welding window were analyzed using tensile properties, microstructural studies, and the fracture location of joints was correlated with the lowest hardness distribution profiles. These windows will act as reference maps for selecting appropriate friction stir welding process parameters to get good quality welds of AA2219 aluminium alloys.
基金Science and Engineering Research Board,Government of India(ECR/2016/001402)BITS-Pilani,Hyderabad Campus。
文摘The stretch forming and the deep-drawing processes were carried out at 300 and 673 K to determine the safe forming and fracture limits of IN625 alloy.The experimentally obtained strain-based fracture forming limit diagram(FFLD)was transformed into a stress-based(σ-FFLD)and effective plastic strain(EPS)vs triaxiality(η)plot to remove the excess dependency of fracture limits over the strains.For the prediction of fracture limits,seven different damage models were calibrated.The Oh model displayed the best ability to predict the fracture locus with the least absolute error.Though the experimentally obtained fracture limits have only been used for the numerical analysis,none of the considered damage models predicted the fracture strains over the entire considered range of stress triaxiality(0.33<η<0.66).The deep drawing process window helped to determine wrinkling,safe and fracture zones while drawing the cylindrical cups under different temperature and lubricating conditions.Further,the highest drawing ratio of 2 was achieved at 673 K under the lubricating condition.All the numerically predicted results of both stretch forming and deep drawing processes using the Hill 1948 anisotropic yielding function were found to be good within the acceptable range of error.
文摘Friction stir spot welding technique was used to join dissimilar combinations of aluminium alloy(Al5052)with copperalloy(C27200)and friction stir spot welding windows such as tool rotational speed–dwell time and tool rotational speed?plungedepth diagrams for effective joining of these materials were developed.Using a central composite design model,empirical relationswere developed to predict the changes in tensile shear failure load values and interface hardness of the joints with three processparameters such as tool rotational speed,plunge depth and dwell time.The adequacy of the developed model was verified usingANOVA analysis at95%confidence level.Response surface methodology was used to optimize the developed model to maximizetensile strength and minimize interface hardness.A high tensile shear failure load value of3850N and low interface hardness valueof HV81was observed for joints made under optimum conditions,and validation experiments confirmed the high predictability ofthe developed model with error less than2%.The operating windows developed shall act as reference maps for future designengineers in choosing appropriate friction stir spot welding process parameter values to obtain good joints.