In the continuous casting production of medium carbon steel (whose mass fraction of carbon is 0.09 % to 0.16 %) and high strength low alloy steel (whose mass fraction of Mn is 0.90 % to 1.40 %), flecks occurring the m...In the continuous casting production of medium carbon steel (whose mass fraction of carbon is 0.09 % to 0.16 %) and high strength low alloy steel (whose mass fraction of Mn is 0.90 % to 1.40 %), flecks occurring the most often are usually longitudinal and star cracks. In additional to the employment of a galvanized plate mould, two kinds of fluxes with special properties were studied and used to harmonize the conflicts between the function of heat transfer and lubrication. An industrial application revealed that the crystallizing temperature (Tc) and crystal ratio (R) of fluxes have a crucible effect on impeding the occurrence of above defects on a slab surface. In the case of slab section (180 to 240) mm(1000 to 1400) mm and casting speed Vc of (0.7 to 1.2) m/min, the optimized parameters of fluxes are Tc of (1170 to 1190) ℃, R of 80 % to 95 % for medium carbon steel, and Tc of (1100 to 1150) ℃, plus R of 40 % to 60 % for high strength low alloy steel.展开更多
The hardening curve for sheet metal can be determined from the load-displacement curve of tensile specimen with rectangular cross-section. Therefore,uniaxial compression test on cylinder specimen made from laminated s...The hardening curve for sheet metal can be determined from the load-displacement curve of tensile specimen with rectangular cross-section. Therefore,uniaxial compression test on cylinder specimen made from laminated sample is put forward. Considering the influence of anisotropy on hardening properties and the stress state in popular forming process,plane strain compression test on cubic specimen made from laminated sample was advanced. Results show that the deformation range of hardening curves obtained from the presented methods is wide,which meets the need for the application in sheet metal forming processes. In view of the characteristics of methods presented in the paper and the stress strain state of various forming processes,the adaptability of the two methods presented in this paper is given.展开更多
文摘In the continuous casting production of medium carbon steel (whose mass fraction of carbon is 0.09 % to 0.16 %) and high strength low alloy steel (whose mass fraction of Mn is 0.90 % to 1.40 %), flecks occurring the most often are usually longitudinal and star cracks. In additional to the employment of a galvanized plate mould, two kinds of fluxes with special properties were studied and used to harmonize the conflicts between the function of heat transfer and lubrication. An industrial application revealed that the crystallizing temperature (Tc) and crystal ratio (R) of fluxes have a crucible effect on impeding the occurrence of above defects on a slab surface. In the case of slab section (180 to 240) mm(1000 to 1400) mm and casting speed Vc of (0.7 to 1.2) m/min, the optimized parameters of fluxes are Tc of (1170 to 1190) ℃, R of 80 % to 95 % for medium carbon steel, and Tc of (1100 to 1150) ℃, plus R of 40 % to 60 % for high strength low alloy steel.
文摘The hardening curve for sheet metal can be determined from the load-displacement curve of tensile specimen with rectangular cross-section. Therefore,uniaxial compression test on cylinder specimen made from laminated sample is put forward. Considering the influence of anisotropy on hardening properties and the stress state in popular forming process,plane strain compression test on cubic specimen made from laminated sample was advanced. Results show that the deformation range of hardening curves obtained from the presented methods is wide,which meets the need for the application in sheet metal forming processes. In view of the characteristics of methods presented in the paper and the stress strain state of various forming processes,the adaptability of the two methods presented in this paper is given.