AIM:To analyze constructive and biomechanical properties of different quality ratio material impregnated decalcified bone matrix (DBM) with bone cement (BC).M ETHODS:The DBM particles and the materials impregnated 0 m...AIM:To analyze constructive and biomechanical properties of different quality ratio material impregnated decalcified bone matrix (DBM) with bone cement (BC).M ETHODS:The DBM particles and the materials impregnated 0 mg/g, 300 mg/g and 400 mg/g mass ratio DBM particles with BC were made according to the methods of Uris t et al.The compound material constructions were observed by scanning electron m icroscope and the biomechanical properties were measured by Instron mechanics te sting-machine.RESULTS:The DBM particles with irregular gaps existing within int erspace were connected with BC by the multipoint mode in the compound material. The ultimate compressive strength were 0 mg/g DBM in (59.3±2.2) MPa, 300 mg/g i n (27.1±1.8) MPa, 400 mg/g in (19.3±1.6) MPa.The ultimate bending strength wer e 0 mg/g in (54.3±3.7) MPa, 300 mg/g in (18.5±1.1) MPa, 400 mg/g in (13.3±1.4 ) MPa.CONCLUSION:The materials of DBM impregnated with BC had perfect plastic pr operty with much more irregular gaps existing within interspace.The materials co uld provide abundant biomechanical support.展开更多
文摘AIM:To analyze constructive and biomechanical properties of different quality ratio material impregnated decalcified bone matrix (DBM) with bone cement (BC).M ETHODS:The DBM particles and the materials impregnated 0 mg/g, 300 mg/g and 400 mg/g mass ratio DBM particles with BC were made according to the methods of Uris t et al.The compound material constructions were observed by scanning electron m icroscope and the biomechanical properties were measured by Instron mechanics te sting-machine.RESULTS:The DBM particles with irregular gaps existing within int erspace were connected with BC by the multipoint mode in the compound material. The ultimate compressive strength were 0 mg/g DBM in (59.3±2.2) MPa, 300 mg/g i n (27.1±1.8) MPa, 400 mg/g in (19.3±1.6) MPa.The ultimate bending strength wer e 0 mg/g in (54.3±3.7) MPa, 300 mg/g in (18.5±1.1) MPa, 400 mg/g in (13.3±1.4 ) MPa.CONCLUSION:The materials of DBM impregnated with BC had perfect plastic pr operty with much more irregular gaps existing within interspace.The materials co uld provide abundant biomechanical support.