电偶腐蚀是腐蚀环境下异种材料连接结构的重要失效形式。采用浸泡腐蚀试验开展了异种材料连接结构在3.5%NaCl溶液中的腐蚀行为研究,并通过扫描电子显微镜(scanning electron microscopy,SEM)和材料拉伸实验对试样的腐蚀形貌观察和力学...电偶腐蚀是腐蚀环境下异种材料连接结构的重要失效形式。采用浸泡腐蚀试验开展了异种材料连接结构在3.5%NaCl溶液中的腐蚀行为研究,并通过扫描电子显微镜(scanning electron microscopy,SEM)和材料拉伸实验对试样的腐蚀形貌观察和力学性能测试,分析了长时腐蚀过程中异种材料连接结构的失效机理与性能弱化机制。研究结果表明,电偶因素和缝隙腐蚀因素联合作用使2A12铝合金的力学性能指标明显降低,但是对强度指标(屈服强度和断裂强度)的影响程度没有对塑性指标(延伸率和断面收缩率)的影响程度大。展开更多
One of the challenges for bimetal manufacturing is the joining process.Hence,transient liquid phase(TLP)bonding was performed between 304L stainless steel and Cp-Ti using an Ag-Cu interlayer with a thickness of 75μm ...One of the challenges for bimetal manufacturing is the joining process.Hence,transient liquid phase(TLP)bonding was performed between 304L stainless steel and Cp-Ti using an Ag-Cu interlayer with a thickness of 75μm for bonding time of 20,40,60,and 90 min.The bonding temperature of 860℃ was considered,which is under the β transus temperature of Cp-Ti.During TLP bonding,various intermetallic compounds(IMCs),including Ti_(5)Cr_(7)Fe_(17),(Cr,Fe)_(2)Ti,Ti(Cu,Fe),Ti_(2)(Cu,Ag),and Ti_(2)Cu from 304L toward Cp-Ti formed in the joint.Also,on the one side,with the increase in time,further diffusion of elements decreases the blocky IMCs such as Ti_(5)Cr_(7)Fe_(17),(Cr,Fe)_(2)Ti,Ti(Cu,Fe)in the 304L diffusion-affected zone(DAZ)and reaction zone,and on the other side,Ti_(2)(Cu,Ag)IMC transformed into fine morphology toward Cp-Ti DAZ.The microhardness test also demonstrated that the(Cr,Fe)_(2)Ti+Ti_(5)Cr_(7)Fe_(17) IMCs in the DAZ on the side of 304L have a hardness value of HV 564,making it the hardest phase.The maximum and minimum shear strength values are equal to 78.84 and 29.0 MPa,respectively.The cleavage pattern dominated fracture surfaces due to the formation of brittle phases in dissimilar joints.展开更多
A novel joining method,double-stage diffusion-brazing of an AZ31 magnesium alloy and a 304L austenitic stainless steel,was carried out using a pure copper interlayer.The solid-state diffusion bonding of 304L to copper...A novel joining method,double-stage diffusion-brazing of an AZ31 magnesium alloy and a 304L austenitic stainless steel,was carried out using a pure copper interlayer.The solid-state diffusion bonding of 304L to copper was conducted at 850 ℃ for 20 min followed by brazing to AZ31 at 520 ℃ and 495 ℃ for various time.Microstructural characteristics of the diffusion-brazed joints were investigated in detail.A defect free interface of Fe-Cu diffusion area appeared between the Cu alloy and the 304L steel.Cu-Mg reaction products were formed between AZ31 and Cu alloys.A layered structure including AZ31/Cu-Mg compounds/Cu/Fe-Cu diffusion layer/304L was present in the joint.With time prolonging,the reduction in the width of Cu layer was balanced by the increase in the width of Cu-Mg compounds zone.Microhardness peaks in the zone between AZ31 and Cu layer were attributed to the formation of Mg-Cu compounds in this zone.展开更多
In this study,the effect of varied loading ratio(mass of the explosive/mass of flyer plate)on the nature of interface,temperature and pressure developed in aluminum-steel explosive cladding is presented.Increase in th...In this study,the effect of varied loading ratio(mass of the explosive/mass of flyer plate)on the nature of interface,temperature and pressure developed in aluminum-steel explosive cladding is presented.Increase in the loading ratio,R,enhances the pressure developed,kinetic energy utilization and deformation work performed.Interfacial microstructures exhibit the formation of molten layer at few spots,owing to the increase in temperature beyond the melting point of parent alloy.The increase in temperature and the quantum of pressure developed were determined by numerical simulation performed in Ansys AUTODYN by employing smoothed particle hydrodynamics(SPH)method.The positioning of the experimental conditions on the weldability window is presented as well.展开更多
文摘电偶腐蚀是腐蚀环境下异种材料连接结构的重要失效形式。采用浸泡腐蚀试验开展了异种材料连接结构在3.5%NaCl溶液中的腐蚀行为研究,并通过扫描电子显微镜(scanning electron microscopy,SEM)和材料拉伸实验对试样的腐蚀形貌观察和力学性能测试,分析了长时腐蚀过程中异种材料连接结构的失效机理与性能弱化机制。研究结果表明,电偶因素和缝隙腐蚀因素联合作用使2A12铝合金的力学性能指标明显降低,但是对强度指标(屈服强度和断裂强度)的影响程度没有对塑性指标(延伸率和断面收缩率)的影响程度大。
文摘One of the challenges for bimetal manufacturing is the joining process.Hence,transient liquid phase(TLP)bonding was performed between 304L stainless steel and Cp-Ti using an Ag-Cu interlayer with a thickness of 75μm for bonding time of 20,40,60,and 90 min.The bonding temperature of 860℃ was considered,which is under the β transus temperature of Cp-Ti.During TLP bonding,various intermetallic compounds(IMCs),including Ti_(5)Cr_(7)Fe_(17),(Cr,Fe)_(2)Ti,Ti(Cu,Fe),Ti_(2)(Cu,Ag),and Ti_(2)Cu from 304L toward Cp-Ti formed in the joint.Also,on the one side,with the increase in time,further diffusion of elements decreases the blocky IMCs such as Ti_(5)Cr_(7)Fe_(17),(Cr,Fe)_(2)Ti,Ti(Cu,Fe)in the 304L diffusion-affected zone(DAZ)and reaction zone,and on the other side,Ti_(2)(Cu,Ag)IMC transformed into fine morphology toward Cp-Ti DAZ.The microhardness test also demonstrated that the(Cr,Fe)_(2)Ti+Ti_(5)Cr_(7)Fe_(17) IMCs in the DAZ on the side of 304L have a hardness value of HV 564,making it the hardest phase.The maximum and minimum shear strength values are equal to 78.84 and 29.0 MPa,respectively.The cleavage pattern dominated fracture surfaces due to the formation of brittle phases in dissimilar joints.
基金Project(51205428) supported by the National Natural Science Foundation of ChinaProject(CDJRC10130011) supported by the Fundamental Research Funds for the Central Universities,China
文摘A novel joining method,double-stage diffusion-brazing of an AZ31 magnesium alloy and a 304L austenitic stainless steel,was carried out using a pure copper interlayer.The solid-state diffusion bonding of 304L to copper was conducted at 850 ℃ for 20 min followed by brazing to AZ31 at 520 ℃ and 495 ℃ for various time.Microstructural characteristics of the diffusion-brazed joints were investigated in detail.A defect free interface of Fe-Cu diffusion area appeared between the Cu alloy and the 304L steel.Cu-Mg reaction products were formed between AZ31 and Cu alloys.A layered structure including AZ31/Cu-Mg compounds/Cu/Fe-Cu diffusion layer/304L was present in the joint.With time prolonging,the reduction in the width of Cu layer was balanced by the increase in the width of Cu-Mg compounds zone.Microhardness peaks in the zone between AZ31 and Cu layer were attributed to the formation of Mg-Cu compounds in this zone.
文摘In this study,the effect of varied loading ratio(mass of the explosive/mass of flyer plate)on the nature of interface,temperature and pressure developed in aluminum-steel explosive cladding is presented.Increase in the loading ratio,R,enhances the pressure developed,kinetic energy utilization and deformation work performed.Interfacial microstructures exhibit the formation of molten layer at few spots,owing to the increase in temperature beyond the melting point of parent alloy.The increase in temperature and the quantum of pressure developed were determined by numerical simulation performed in Ansys AUTODYN by employing smoothed particle hydrodynamics(SPH)method.The positioning of the experimental conditions on the weldability window is presented as well.