The crystallographic structures and magnetic properties of a Zn0.95Co0.05O thin film deposited on a C-sapphire substrate using a dual-beam pulsed laser deposition method were characterized. It was shown from crystallo...The crystallographic structures and magnetic properties of a Zn0.95Co0.05O thin film deposited on a C-sapphire substrate using a dual-beam pulsed laser deposition method were characterized. It was shown from crystallographic analysis that the film belongs to the wurtzite structure with the C-axis aligned with that of the substrate. Magnetic hysteresis loops were observed till up to room temperature. A small peak around 55 K was noticed on the magnetization vs. temperature curve. The corresponding temperature of the small peak is close to that of ‘the abnormal peak’ reported by X.M. Zhang et al. From the results obtained, no correlation was found between the abnormal peak and the quantum effects. The magnetic behaviors in the Zn0.95Co0.05O film cannot be explained by the ferromagnetism in diluted magnetic semiconductors. The magnetic mechanisms in ZnO-based diluted magnetic semiconductors are also discussed.展开更多
基金Supported by the National Natural Science Foundation of China under Grant No 10674040 and the Natural Science Foundation of Hebei Province under Grant No A2007000227.
基金Supported by the Hangzhou Dianzi University Fund (Grant No. KYF091506003)funds from State Key Lab of Silicon Materials, Zhejiang University (Grant No. 2000603)
文摘The crystallographic structures and magnetic properties of a Zn0.95Co0.05O thin film deposited on a C-sapphire substrate using a dual-beam pulsed laser deposition method were characterized. It was shown from crystallographic analysis that the film belongs to the wurtzite structure with the C-axis aligned with that of the substrate. Magnetic hysteresis loops were observed till up to room temperature. A small peak around 55 K was noticed on the magnetization vs. temperature curve. The corresponding temperature of the small peak is close to that of ‘the abnormal peak’ reported by X.M. Zhang et al. From the results obtained, no correlation was found between the abnormal peak and the quantum effects. The magnetic behaviors in the Zn0.95Co0.05O film cannot be explained by the ferromagnetism in diluted magnetic semiconductors. The magnetic mechanisms in ZnO-based diluted magnetic semiconductors are also discussed.