A friction stir welding window was developed for effective joining of AA2219 aluminium alloy. Joints were fabricated using different combination of process parameters such as rotational speed and welding speed. Based ...A friction stir welding window was developed for effective joining of AA2219 aluminium alloy. Joints were fabricated using different combination of process parameters such as rotational speed and welding speed. Based on macrostructural analysis, the friction stir welding window was constructed. The strength values of joints at different regions of friction stir welding window were analyzed using tensile properties, microstructural studies, and the fracture location of joints was correlated with the lowest hardness distribution profiles. These windows will act as reference maps for selecting appropriate friction stir welding process parameters to get good quality welds of AA2219 aluminium alloys.展开更多
The effects of vacuum assistance on the microstructure and mechanical properties of high pressure die cast A390alloy at different slow shot speeds were evaluated.Plate-shaped specimens of hypereutectic A390aluminum al...The effects of vacuum assistance on the microstructure and mechanical properties of high pressure die cast A390alloy at different slow shot speeds were evaluated.Plate-shaped specimens of hypereutectic A390aluminum alloy were produced on a TOYO BD?350V5cold chamber die casting machine incorporated with a self-improved TOYO vacuum system.According to the results,the vacuum pressure inside the die cavity increased linearly with the increasing slow shot speed at the beginning of mold filling.Meanwhile,tensile properties of vacuum die castings were deteriorated by the porosity content.In addition,the average primary silicon size decreased from23to14μm when the slow shot speed increased from0.05to0.2m/s,which has a binary functional relationship with the slow shot speed.After heat treatment,microstructural morphologies revealed that needle-shaped and thin-flaked eutectic silicon particles became rounded while Al2Cu dissolved intoα(Al)matrix.Furthermore,the fractography revealed that the fracture mechanism has evolved from brittle transgranular fracture to a fracture mode with many dimples after heat treatment.展开更多
文摘A friction stir welding window was developed for effective joining of AA2219 aluminium alloy. Joints were fabricated using different combination of process parameters such as rotational speed and welding speed. Based on macrostructural analysis, the friction stir welding window was constructed. The strength values of joints at different regions of friction stir welding window were analyzed using tensile properties, microstructural studies, and the fracture location of joints was correlated with the lowest hardness distribution profiles. These windows will act as reference maps for selecting appropriate friction stir welding process parameters to get good quality welds of AA2219 aluminium alloys.
基金Project(51775297)supported by the National Natural Science Foundation of ChinaProject(2015M580093)supported by the China Postdoctoral Science Foundation
文摘The effects of vacuum assistance on the microstructure and mechanical properties of high pressure die cast A390alloy at different slow shot speeds were evaluated.Plate-shaped specimens of hypereutectic A390aluminum alloy were produced on a TOYO BD?350V5cold chamber die casting machine incorporated with a self-improved TOYO vacuum system.According to the results,the vacuum pressure inside the die cavity increased linearly with the increasing slow shot speed at the beginning of mold filling.Meanwhile,tensile properties of vacuum die castings were deteriorated by the porosity content.In addition,the average primary silicon size decreased from23to14μm when the slow shot speed increased from0.05to0.2m/s,which has a binary functional relationship with the slow shot speed.After heat treatment,microstructural morphologies revealed that needle-shaped and thin-flaked eutectic silicon particles became rounded while Al2Cu dissolved intoα(Al)matrix.Furthermore,the fractography revealed that the fracture mechanism has evolved from brittle transgranular fracture to a fracture mode with many dimples after heat treatment.