研究了采用ZGA351大孔强碱性阴离子交换树脂从粗钨酸铵溶液中吸附分离钼的工艺方法,考察了树脂型号、料液硫含量、料液陈化时间、料液陈化温度、料液pH值、吸附流速、吸附温度对树脂吸附分离钼效果的影响。结果表明:使用100 mL ZGA351...研究了采用ZGA351大孔强碱性阴离子交换树脂从粗钨酸铵溶液中吸附分离钼的工艺方法,考察了树脂型号、料液硫含量、料液陈化时间、料液陈化温度、料液pH值、吸附流速、吸附温度对树脂吸附分离钼效果的影响。结果表明:使用100 mL ZGA351树脂进行动态吸附试验,在料液硫含量为理论量1.1倍、料液陈化时间48 h、料液陈化温度40℃、料液pH值10.0、吸附流速15 mL/h、吸附温度40℃的最优条件下,料液钨损失率仅为0.54%,树脂钼穿透容量为107.77 g/L_(湿树脂),相比目前工业生产应用的HBDM-1树脂钼穿透容量提高了3.15倍。另外,重复试验稳定性良好,ZGA351树脂吸附后得到的纯钨酸铵溶液平均钼钨比为0.88×10^(-4),满足工业生产APT产品用纯钨酸铵溶液钼钨比小于2×10^(-4)的需求。综合而言,采用强碱性阴离子交换树脂从粗钨酸铵溶液中分离钼具有钼穿透容量高、钨损失率低、钨钼分离效率高等优势,为工业化应用提供了一种有效技术参考。展开更多
Refined soybean oil and lard were interesterified in the presence of a basic anion exchange resin as heterogeneous catalyst. The structural composition of the interesterification products was determined by 1,3 specifi...Refined soybean oil and lard were interesterified in the presence of a basic anion exchange resin as heterogeneous catalyst. The structural composition of the interesterification products was determined by 1,3 specific lipase hydrolysis method followed by chromotographic analysis. The influences of the acidity of reactants, reaction time and reaction temperature on the interesterfication have been investigated. The experimental results showed that a mixture of 60% soybean oil and 40% lard(in mass ratio) with acid value of 0 116 was found to have remarkable interesterification at 50℃, for 150 min by using 10% basic anion exchange resin as a catalyst. The melting point of the final product was 37 6 ℃.展开更多
文摘Refined soybean oil and lard were interesterified in the presence of a basic anion exchange resin as heterogeneous catalyst. The structural composition of the interesterification products was determined by 1,3 specific lipase hydrolysis method followed by chromotographic analysis. The influences of the acidity of reactants, reaction time and reaction temperature on the interesterfication have been investigated. The experimental results showed that a mixture of 60% soybean oil and 40% lard(in mass ratio) with acid value of 0 116 was found to have remarkable interesterification at 50℃, for 150 min by using 10% basic anion exchange resin as a catalyst. The melting point of the final product was 37 6 ℃.