The effect of cold plastic deformation between solution treatment and artificial aging on the age-hardening response and mechanical properties of alloy was investigated by micro-hardness test,tensile test,optical micr...The effect of cold plastic deformation between solution treatment and artificial aging on the age-hardening response and mechanical properties of alloy was investigated by micro-hardness test,tensile test,optical microscopy（OM） and TEM observation.After solution treatment at 420 ℃ for 1 h,three kinds of pre-deformation strains,i.e.0,5% and 10%,were applied to extruded ZM61 bars.Age-hardening curves show that pre-deformation can significantly accelerate the precipitation kinetics and increase peak-hardness value;however,as pre-deformation strain rises from 5% to 10%,there is no gain in peak hardness value.The room temperature（RT） tensile properties demonstrate that increasing the pre-deformation degree can enhance the yield strength（YS） and ultimate tensile strength（UTS） but moderately reduce elongation（EL）;furthermore,the enhancement of YS is larger than that of UTS.No twin can be observed in 5% pre-deformed microstructure;however,a large number of twins are activated after 10% pre-deformation.The peak-aged TEM microstructure shows that pre-deformation can increase the number density of rod-shaped β 1 ＇ precipitates which play a key role in strengthening ZM61 alloy.展开更多
The influences of high temperature pre-straining (HT-PS) on the natural aging and bake hardening of Al?Mg?Si alloys were investigated by Vickers microhardness measurements, differential scanning calorimetry (DSC) anal...The influences of high temperature pre-straining (HT-PS) on the natural aging and bake hardening of Al?Mg?Si alloys were investigated by Vickers microhardness measurements, differential scanning calorimetry (DSC) analysis and transmission electron microscopy (TEM) characterization. The results show that pre-straining at 170 °C immediately after quenching can effectively resolve the rather high T4 temper hardness caused by the conventional room temperature (RT) pre-straining treatment, and give a better bake hardening response (BHR) after paint-bake cycle. HT-PS 7% at 170 °C for 10 min is chosen as the optimum process as it provides lower T4 temper hardness and better BHR. The simultaneous introduction of dislocations and Cluster (2) can significantly suppress the natural aging and promote the precipitation of β″ phase, and reduce the effects of deformation hardening by dynamic recovery.展开更多
An as-solution treated Mg-6Gd-1Y-0.4Zr alloy was processed by low temperature thermo-mechanical treatments （LT-TMT）, including cold tension with various strains followed by aging at 200 °C to peak hardness. The...An as-solution treated Mg-6Gd-1Y-0.4Zr alloy was processed by low temperature thermo-mechanical treatments （LT-TMT）, including cold tension with various strains followed by aging at 200 °C to peak hardness. The results show that the precipitation kinetics of the alloy experienced LT-TMT is greatly accelerated and the aging time to peak hardness is greatly decreased with increasing tensile strain. The tensile yield strength, ultimate tensile strength and elongation at room temperature of the alloy after cold tension with strain of 10% and peak aging at 200 °C are 251 MPa, 296 MPa and 8%, respectively, which are superior to the commercial heat-resistant WE54 alloy, although the latter has a higher rare earth element content.展开更多
基金Project(2007CB613700) supported by the National Basic Research Program of ChinaProject(50725413) supported by the National Natural Science Foundation of China+2 种基金Project(CDJXS11132228) supported by the Fundamental Research Funds for the Central Universities,ChinaProjects(2010DFR50010,2008DFR50040) supported by International Cooperation Program,ChinaProjects (CSTC2009AB4008,2010CSTC-HDLS) supported by Chongqing Sci & Tech Program,China
文摘The effect of cold plastic deformation between solution treatment and artificial aging on the age-hardening response and mechanical properties of alloy was investigated by micro-hardness test,tensile test,optical microscopy（OM） and TEM observation.After solution treatment at 420 ℃ for 1 h,three kinds of pre-deformation strains,i.e.0,5% and 10%,were applied to extruded ZM61 bars.Age-hardening curves show that pre-deformation can significantly accelerate the precipitation kinetics and increase peak-hardness value;however,as pre-deformation strain rises from 5% to 10%,there is no gain in peak hardness value.The room temperature（RT） tensile properties demonstrate that increasing the pre-deformation degree can enhance the yield strength（YS） and ultimate tensile strength（UTS） but moderately reduce elongation（EL）;furthermore,the enhancement of YS is larger than that of UTS.No twin can be observed in 5% pre-deformed microstructure;however,a large number of twins are activated after 10% pre-deformation.The peak-aged TEM microstructure shows that pre-deformation can increase the number density of rod-shaped β 1 ＇ precipitates which play a key role in strengthening ZM61 alloy.
基金Project(2014DFA51270)supported by the International Science and Technology Cooperation Program of ChinaProject(51421001)supported by the Foundation for Innovative Research Groups of the National Natural Science Foundation of China
文摘The influences of high temperature pre-straining (HT-PS) on the natural aging and bake hardening of Al?Mg?Si alloys were investigated by Vickers microhardness measurements, differential scanning calorimetry (DSC) analysis and transmission electron microscopy (TEM) characterization. The results show that pre-straining at 170 °C immediately after quenching can effectively resolve the rather high T4 temper hardness caused by the conventional room temperature (RT) pre-straining treatment, and give a better bake hardening response (BHR) after paint-bake cycle. HT-PS 7% at 170 °C for 10 min is chosen as the optimum process as it provides lower T4 temper hardness and better BHR. The simultaneous introduction of dislocations and Cluster (2) can significantly suppress the natural aging and promote the precipitation of β″ phase, and reduce the effects of deformation hardening by dynamic recovery.
基金Projects(50971089,51171113,51001072)supported by the National Natural Science Foundation of ChinaProjects(2012M511089,20090460615,201003267)supported by the Postdoctoral Science Foundation of China
文摘An as-solution treated Mg-6Gd-1Y-0.4Zr alloy was processed by low temperature thermo-mechanical treatments （LT-TMT）, including cold tension with various strains followed by aging at 200 °C to peak hardness. The results show that the precipitation kinetics of the alloy experienced LT-TMT is greatly accelerated and the aging time to peak hardness is greatly decreased with increasing tensile strain. The tensile yield strength, ultimate tensile strength and elongation at room temperature of the alloy after cold tension with strain of 10% and peak aging at 200 °C are 251 MPa, 296 MPa and 8%, respectively, which are superior to the commercial heat-resistant WE54 alloy, although the latter has a higher rare earth element content.