Bridgman-type directional solidification experiments were conducted for Ti-46Al-8Nb （mole fraction, %） alloy. The effects of the growth rate and the diameter on the microstructure, phase transition and hardness of t...Bridgman-type directional solidification experiments were conducted for Ti-46Al-8Nb （mole fraction, %） alloy. The effects of the growth rate and the diameter on the microstructure, phase transition and hardness of the alloy were investigated. The results show that with the increase of the growth rate and the decrease of the diameter, the fullyβphase solidification changes to the peritectic solidification, and the final microstructure is composed of theα2/γlamellar structure and a multiphase microstructure （B2 phase,α2/γlamellar structure） respectively, which can be attributed to the solute enrichment resulting from the decreasing diffusion and convection ability. The occurrence of peritectic reaction at high growth rate promotes the solute segregation heavily and the coarse lamellar spacing in Al-and Nb-rich region, which greatly decreases the hardness values and leads to the discontinuity of the hardness curves with the increase of the growth rate. Comparatively, the Ti-46Al-8Nb alloy has lower hardness values than the other applied TiAl-based alloys in previous studies.展开更多
基金Projects(51071062,51274077,51271068)supported by the National Natural Science Foundation of ChinaProject(2011-P03)supported by Open Fund of State Key Laboratory of Mold and Die Technology of Huazhong University of Science and Technology+1 种基金Project(HIT.NSRIF.2013002)supported by the Fundamental Research Funds for the Central Universities,ChinaProject(2011CB605504)supported by the National Basic Research Program of China
文摘Bridgman-type directional solidification experiments were conducted for Ti-46Al-8Nb （mole fraction, %） alloy. The effects of the growth rate and the diameter on the microstructure, phase transition and hardness of the alloy were investigated. The results show that with the increase of the growth rate and the decrease of the diameter, the fullyβphase solidification changes to the peritectic solidification, and the final microstructure is composed of theα2/γlamellar structure and a multiphase microstructure （B2 phase,α2/γlamellar structure） respectively, which can be attributed to the solute enrichment resulting from the decreasing diffusion and convection ability. The occurrence of peritectic reaction at high growth rate promotes the solute segregation heavily and the coarse lamellar spacing in Al-and Nb-rich region, which greatly decreases the hardness values and leads to the discontinuity of the hardness curves with the increase of the growth rate. Comparatively, the Ti-46Al-8Nb alloy has lower hardness values than the other applied TiAl-based alloys in previous studies.