Mg-Al-Zn alloy thin strips were prepared by vertical twin-roll casting.Effects of Al and Ca on the microstructure and the surface defects of the thin strips were investigated.The results show that with the increase of...Mg-Al-Zn alloy thin strips were prepared by vertical twin-roll casting.Effects of Al and Ca on the microstructure and the surface defects of the thin strips were investigated.The results show that with the increase of Al content,the quantity of surface cracks of the thin strips increases rapidly and their locations are moved to the center of the thin strips.The alloy melts with more than 0.10%Ca(mass fraction)stick on the roller and a poor surface quality of the thin strips appears.With the increase of Al content,the microstructure of the thin strips evolves from singleα-Mg phase,characterized by the uniform and equiaxed recrystallization grains, to the combination of dendriticα-Mg with Al supersaturatedα-Mg.The minor addition of Ca can obviously refine the grains of Mg-3Al-1Zn thin strip because the formation of Al2Ca and the finest grains are obtained by adding 0.08%Ca.展开更多
文摘在传统微带线结构基础上利用阶跃阻抗并联短截线SISS(Step-Impedance Shunt Stubs)的带阻及慢波抑制特性,提出了一种新的基于SISS缺陷微带线结构S-DMS(SISS Defected Microstrip Structure),利用该结构设计制作了具有谐波抑制功能的双通带滤波器。采用HFSS进行仿真优化,在此基础上进行了实物加工,获得了通带中心频率为3.5 GHz,8.5 GHz,插入损耗分别为0.45 d B,2.7 d B,3 d B带宽分别是550 MHz,260 MHz,带外最大抑制小于-40 d B的实测结果,与仿真结果相当吻合。结果表明该双通带滤波器具有良好的谐波抑制能力、小带内衰减和宽且深的阻带特性。
基金Project(50604020)supported by the National Natural Science Foundation of ChinaProject(2007CB613706)supported by the National Basic Research Program of China+1 种基金Project(2009AA03Z507)supported by the National High-tech Research and Development Program of ChinaProject(CSTC2008AA4028)supported by Key Program of Chongqing Science and Technology Commission,China
文摘Mg-Al-Zn alloy thin strips were prepared by vertical twin-roll casting.Effects of Al and Ca on the microstructure and the surface defects of the thin strips were investigated.The results show that with the increase of Al content,the quantity of surface cracks of the thin strips increases rapidly and their locations are moved to the center of the thin strips.The alloy melts with more than 0.10%Ca(mass fraction)stick on the roller and a poor surface quality of the thin strips appears.With the increase of Al content,the microstructure of the thin strips evolves from singleα-Mg phase,characterized by the uniform and equiaxed recrystallization grains, to the combination of dendriticα-Mg with Al supersaturatedα-Mg.The minor addition of Ca can obviously refine the grains of Mg-3Al-1Zn thin strip because the formation of Al2Ca and the finest grains are obtained by adding 0.08%Ca.