Al-5Ti-1B master alloy was added into Mg-14Li-1Al(LA141)alloy and then LA141 sheets were prepared by extrusion and cold rolling.The effect of the addition level of Al-5Ti-1B master alloy on the grain size of LA141 all...Al-5Ti-1B master alloy was added into Mg-14Li-1Al(LA141)alloy and then LA141 sheets were prepared by extrusion and cold rolling.The effect of the addition level of Al-5Ti-1B master alloy on the grain size of LA141 alloy was investigated as well as the effects of the total reduction of cold rolling and the annealing temperature on microstructure,mechanical properties and plastic formability of the LA141 sheets.The results show that the optimal addition level of Al-5Ti-1B master alloy into LA141 alloy is 1.25%(mass fraction)and LA141 alloy has the finest grains.With the increase of the total reduction of cold rolling,the grains of the as-rolled LA141 sheets were flattened gradually.A proper anneal temperature of 200℃ is obtained for the cold rolled LA141 sheets. Under this condition,microstructure of the LA141 sheets consists of fine and uniform equiaxed grains and has higher Erichsen cupping index(IE).展开更多
AZ80 magnesium alloys were deformed at 200,250,300,350 and 400℃ with different deformation degree of 50%,75%, 83%,87%and 90%,respectively.The corrosion properties of different deformed AZ80 samples were studied by ga...AZ80 magnesium alloys were deformed at 200,250,300,350 and 400℃ with different deformation degree of 50%,75%, 83%,87%and 90%,respectively.The corrosion properties of different deformed AZ80 samples were studied by galvanic test in 3.5%NaCl solution.The results show that plastic deformation could improve the corrosion resistance of AZ80 alloy;and the corrosion rate of AZ80 deformed at 250℃ with the deformation degree of 83%was the lowest,which was 33%of the as-cast AZ80 alloy.Further studies of the microstructure show that the refined grain size and continuously distribution ofβphase around the grain boundary did have a positive effect on the improvement of corrosion resistance of AZ80 alloys.For AZ80 alloys,the smaller the grain size is,the more homogeneous the structure is,and the better the corrosion resistance is.展开更多
The microstructure and tensile properties of the Mg-1.0%Sn-xY(x=1.5%,3.0%,3.5%,atom fraction)alloys extruded indirectly at 350℃ were investigated by means of optical microscopy,scanning electron microscopy and tensil...The microstructure and tensile properties of the Mg-1.0%Sn-xY(x=1.5%,3.0%,3.5%,atom fraction)alloys extruded indirectly at 350℃ were investigated by means of optical microscopy,scanning electron microscopy and tensile test.The mean grain sizes ofα-Mg matrix in the three extruded alloys are 6,8 and 12μm,respectively,slightly increasing with the addition of Y. The relationship between microstructure and strength was discussed in detail.The results show that the addition of Y has little effect on the grain refinement of the as-extruded Mg-Sn based alloys above.The only MgSnY phase is detected in the Mg-Sn-1.5%Y alloy, and the Sn3Y5 phase in the Mg-Sn-3.5%Y alloy,whereas both of them simultaneously exist in the Mg-Sn-3.0%Y alloy.The particle shape of MgSnY and Sn3Y5 phase,inherited from the solidification,has little change before and after hot extrusion.Mg-Sn-3.0%Y alloy has the highest ultimate tensile strength(UTS),305 MPa,by over 50%compared with that of the other two alloys.展开更多
基金Project(50604020)supported by the National Natural Science Foundation of ChinaProject(2007CB613706)supported by the National Basic Research Program of ChinaProject(2009AA03Z507)supported by the National High-tech Research and Development Program of China
文摘Al-5Ti-1B master alloy was added into Mg-14Li-1Al(LA141)alloy and then LA141 sheets were prepared by extrusion and cold rolling.The effect of the addition level of Al-5Ti-1B master alloy on the grain size of LA141 alloy was investigated as well as the effects of the total reduction of cold rolling and the annealing temperature on microstructure,mechanical properties and plastic formability of the LA141 sheets.The results show that the optimal addition level of Al-5Ti-1B master alloy into LA141 alloy is 1.25%(mass fraction)and LA141 alloy has the finest grains.With the increase of the total reduction of cold rolling,the grains of the as-rolled LA141 sheets were flattened gradually.A proper anneal temperature of 200℃ is obtained for the cold rolled LA141 sheets. Under this condition,microstructure of the LA141 sheets consists of fine and uniform equiaxed grains and has higher Erichsen cupping index(IE).
基金Projects(50605059,50735005)supported by the National Natural Science Foundation of ChinaProject(2008062)supported by Shanxi Province Foundation for Returness
文摘AZ80 magnesium alloys were deformed at 200,250,300,350 and 400℃ with different deformation degree of 50%,75%, 83%,87%and 90%,respectively.The corrosion properties of different deformed AZ80 samples were studied by galvanic test in 3.5%NaCl solution.The results show that plastic deformation could improve the corrosion resistance of AZ80 alloy;and the corrosion rate of AZ80 deformed at 250℃ with the deformation degree of 83%was the lowest,which was 33%of the as-cast AZ80 alloy.Further studies of the microstructure show that the refined grain size and continuously distribution ofβphase around the grain boundary did have a positive effect on the improvement of corrosion resistance of AZ80 alloys.For AZ80 alloys,the smaller the grain size is,the more homogeneous the structure is,and the better the corrosion resistance is.
基金Project(2008S089)supported by the Key Laboratory Fund of Liaoning Province,ChinaProject(2007010303025)supported by Shenyang Talents Supporting ProgramProject(50731002)supported by the National Natural Science Foundation of China
文摘The microstructure and tensile properties of the Mg-1.0%Sn-xY(x=1.5%,3.0%,3.5%,atom fraction)alloys extruded indirectly at 350℃ were investigated by means of optical microscopy,scanning electron microscopy and tensile test.The mean grain sizes ofα-Mg matrix in the three extruded alloys are 6,8 and 12μm,respectively,slightly increasing with the addition of Y. The relationship between microstructure and strength was discussed in detail.The results show that the addition of Y has little effect on the grain refinement of the as-extruded Mg-Sn based alloys above.The only MgSnY phase is detected in the Mg-Sn-1.5%Y alloy, and the Sn3Y5 phase in the Mg-Sn-3.5%Y alloy,whereas both of them simultaneously exist in the Mg-Sn-3.0%Y alloy.The particle shape of MgSnY and Sn3Y5 phase,inherited from the solidification,has little change before and after hot extrusion.Mg-Sn-3.0%Y alloy has the highest ultimate tensile strength(UTS),305 MPa,by over 50%compared with that of the other two alloys.