Microstructure and properties of high-fraction graphite nanoflakes/6061Al matrix composites fabricated via spark plasma sintering

30-50 wt.%graphite nanoflakes(GNFs)/6061Al matrix composites were fabricated via spark plasma sintering(SPS)at 610℃.The effects of the sintering pressure and GNF content on the microstructure and properties of the composites were investigated.The results indicated that interfacial reactions were inhibited during SPS because no Al4C3 was detected.Moreover,the agglomeration of the GNFs increased,and the distribution orientation of the GNFs decreased with increasing the GNF content.The relative density,bending strength,and coefficient of thermal expansion(CTE)of the composites decreased,while the thermal conductivity(TC)in the X−Y direction increased.As the sintering pressure increased,the GNFs deagglomerated and were distributed preferentially in the X−Y direction,which increased the relative density,bending strength and TC,and decreased the CTE of the composites.The 50wt.%GNFs/6061Al matrix composite sintered at 610℃ under 55 MPa demonstrated the best performance,i.e.,bending strength of 72 MPa,TC and CTE(RT−100℃)of 254 W/(m·K)and 8.5×10^(−6)K^(−1)in the X−Y direction,and 55 W/(m·K)and 9.7×10^(−6)K^(−1)in the Z direction,respectively.

Effects of graphene nanoplates on microstructures and mechanical properties of NSA-TIG welded AZ31 magnesium alloy joints

The effects of graphene nanoplates(GNPs)on the microstructures and mechanical properties of nanoparticlesstrengthening activating tungsten inert gas arc welding(NSA-TIG)welded AZ31magnesium alloy joints were investigated.It wasfound that compared with those of activating TIG(A-TIG),and obvious refinement ofα-Mg grains was achieved and the finestα-Mggrains of fusion zone of NSA-TIG joints were obtained in the welded joints with TiO2+GNPs flux coating.In addition,thepenetrations of joints coated by TiO2+GNPs flux were similar to those coated by the TiO2+SiCp flux.However,the welded jointswith TiO2+GNPs flux coating showed better mechanical properties(i.e.,ultimate tensile strength and microhardness)than those withTiO2+SiCp flux coating.Moreover,the generation of necking only occurred in the welded joints with TiO2+GNPs flux.

Electron transfer from sulfate-reducing bacteria biofilm promoted by reduced graphene sheets

Reduced graphene sheets (RGSs) mediate electron transfer between sulfate-reducing bacteria (SRB) and solid electrodes, and promote the development of microbial fuel cells (MFC). We have investigated RSG-promoted electron transfer between SRB and a glassy carbon (GC) electrode. The RGSs were produced at high yield by a chemical sequence involving graphite oxidation, ultrasonic exfoliation of nanosheets, and N2H4 reduction. Cyclic voltammetric testing showed that the characteristic anodic peaks (around 0.3 V) might arise from the combination of bacterial membrane surface cytochrome c3 and the metabolic products of SRB. After 6 d, another anodic wave gradually increased to a maximum current peak and a third anodic signal became visible at around 0 V. The enhancements of two characteristic anodic peaks suggest that RSGs mediate electron-transfer kinetics between bacteria and the solid electrode. Manipulation of these recently-discovered electron-transport mechanisms will lead to significant advances in MFC engineering.

确定变质岩区褶皱构造形态的几种方法及其理论分析

本文根据作者多年研究和实践,提出确定变质岩区褶皱构造形态的3种技术和方法:1.微片石法,2.钩状褶皱法,3.构造透镜体法。它们的理论依据是构造置换。这些方法无论在实际上,还是在理论上都是能成立的。应用这些方法能获得较好的效果。