Activated carbon was fabricated by using oil asphalt as carbon source, KOH as activator. The samples were analyzed by N2 adsorption, scanning electron microscopy （SEM）. Cyclic voltammetry and galvanostatic charge-di...Activated carbon was fabricated by using oil asphalt as carbon source, KOH as activator. The samples were analyzed by N2 adsorption, scanning electron microscopy （SEM）. Cyclic voltammetry and galvanostatic charge-discharge were used to characterize the electrochemical performance of the samples. The results showed that the pore size was mainly in the range of 0.5-9.0 nm. Supercapacitors based on the sample AC （Activated carbon） have low ESR and excellent power property.展开更多
Activated carbon （AC） was fabricated by using phenolic resin as carbon source, silica gel as inorganic template, KOH as activator. The samples were analyzed by N2 adsorption, scanning electron microscopy （SEM）. Cy...Activated carbon （AC） was fabricated by using phenolic resin as carbon source, silica gel as inorganic template, KOH as activator. The samples were analyzed by N2 adsorption, scanning electron microscopy （SEM）. Cyclic voltammetry and galvanostatic charge-discharge were used to characterize the electrochemical performance of the samples. The results showed that the pore size was mainly in the range of 0.5 9.0 nm. Supercapacitors based on the sample AC-3 have low equivalent series resistanceb （ESR） and excellent power property.展开更多
文摘Activated carbon was fabricated by using oil asphalt as carbon source, KOH as activator. The samples were analyzed by N2 adsorption, scanning electron microscopy （SEM）. Cyclic voltammetry and galvanostatic charge-discharge were used to characterize the electrochemical performance of the samples. The results showed that the pore size was mainly in the range of 0.5-9.0 nm. Supercapacitors based on the sample AC （Activated carbon） have low ESR and excellent power property.
文摘Activated carbon （AC） was fabricated by using phenolic resin as carbon source, silica gel as inorganic template, KOH as activator. The samples were analyzed by N2 adsorption, scanning electron microscopy （SEM）. Cyclic voltammetry and galvanostatic charge-discharge were used to characterize the electrochemical performance of the samples. The results showed that the pore size was mainly in the range of 0.5 9.0 nm. Supercapacitors based on the sample AC-3 have low equivalent series resistanceb （ESR） and excellent power property.