The effects of Ca addition on the as-cast microstructure and mechanical properties of the Mg-5Zn-5Sn (mass fraction,%) alloy were investigated.The results indicate that an addition of 0.5%-1.5% (mass fraction) Ca to t...The effects of Ca addition on the as-cast microstructure and mechanical properties of the Mg-5Zn-5Sn (mass fraction,%) alloy were investigated.The results indicate that an addition of 0.5%-1.5% (mass fraction) Ca to the Mg-5Zn-5Sn alloy not only refines the as-cast microstructure of the alloy but also causes the formation of the primary and/or eutectic CaMgSn phases with high thermal stability;an increase in Ca amount from 0.5% to 1.5% (mass fraction) increases the amount and size of the CaMgSn phase.In addition,Ca addition to the Mg-5Zn-5Sn alloy improves not only the tensile properties at room temperature and 150 ℃ but also the creep properties.Among the Ca-containing Mg-5Zn-5Sn alloys,the one added 0.5% (mass fraction) Ca obtains the optimum ultimate tensile strength and elongation at room temperature and 150 ℃,however,the alloy added 1.5% (mass fraction) Ca exhibits the optimum yield strength and creep properties.展开更多
In this paper,a new method combining focused ion beam(FIB)and scanning electron microscope(SEM)Moirétechnique for the measurement of residual stress at micro scale is proposed.The FIB is employed to introduce str...In this paper,a new method combining focused ion beam(FIB)and scanning electron microscope(SEM)Moirétechnique for the measurement of residual stress at micro scale is proposed.The FIB is employed to introduce stress relief like the macro ring-core method and fabricate gratings with a frequency of 5000 lines/mm on the measured area of the sample surface.Three groups of gratings in different radial directions are manufactured in order to form a micro-scale strain rosette.After milling ring-core by FIB,the deformation incurred by relief of the stress will be recorded with the strain rosette.The displacement/strain field can be measured using SEM scanning Moiréwith random phase-shifting algorithm.In this study,the Nickel alloy GH4169 sample(which was processed by laser shock peening)is selected as a study object to determine its residual stress.The results showed that the components of the in-plane principal stresses were-359 MPa and-207 MPa,respectively,which show good agreement with the results obtained from the available literature.展开更多
基金Project(50725413) supported by the National Natural Science Foundation of ChinaProject (2007CB613704) supported by the National Basic Research Program of China Projects(2006AA4012-9-6,2007BB4400) supported by Chongqing Science and Technology Commission,China
文摘The effects of Ca addition on the as-cast microstructure and mechanical properties of the Mg-5Zn-5Sn (mass fraction,%) alloy were investigated.The results indicate that an addition of 0.5%-1.5% (mass fraction) Ca to the Mg-5Zn-5Sn alloy not only refines the as-cast microstructure of the alloy but also causes the formation of the primary and/or eutectic CaMgSn phases with high thermal stability;an increase in Ca amount from 0.5% to 1.5% (mass fraction) increases the amount and size of the CaMgSn phase.In addition,Ca addition to the Mg-5Zn-5Sn alloy improves not only the tensile properties at room temperature and 150 ℃ but also the creep properties.Among the Ca-containing Mg-5Zn-5Sn alloys,the one added 0.5% (mass fraction) Ca obtains the optimum ultimate tensile strength and elongation at room temperature and 150 ℃,however,the alloy added 1.5% (mass fraction) Ca exhibits the optimum yield strength and creep properties.
基金supported by the National Basic Research Program of China(Grant Nos.2010CB631005 and 2011CB606105)the National Natural Science Foundation of China(Grant Nos.90916010,11172151 and 11232008)+1 种基金Specialized Research Fund for the Doctoral Program of Higher Education(Grant No.20090002110048)Tsinghua University Initiative Scientific Research Program
文摘In this paper,a new method combining focused ion beam(FIB)and scanning electron microscope(SEM)Moirétechnique for the measurement of residual stress at micro scale is proposed.The FIB is employed to introduce stress relief like the macro ring-core method and fabricate gratings with a frequency of 5000 lines/mm on the measured area of the sample surface.Three groups of gratings in different radial directions are manufactured in order to form a micro-scale strain rosette.After milling ring-core by FIB,the deformation incurred by relief of the stress will be recorded with the strain rosette.The displacement/strain field can be measured using SEM scanning Moiréwith random phase-shifting algorithm.In this study,the Nickel alloy GH4169 sample(which was processed by laser shock peening)is selected as a study object to determine its residual stress.The results showed that the components of the in-plane principal stresses were-359 MPa and-207 MPa,respectively,which show good agreement with the results obtained from the available literature.