A series of die casting heat-resistant magnesium alloys based on Mg-Al system were developed for automotive application by adding Y and various amounts of Ca. The mechanical properties and microstructures of die casti...A series of die casting heat-resistant magnesium alloys based on Mg-Al system were developed for automotive application by adding Y and various amounts of Ca. The mechanical properties and microstructures of die casting AZ91 alloy with combined addition of Y and Ca were investigated by optical microscopy, scanning electronic microscopy, X-ray diffractometry and mechanical property test. The results show that the combined addition of Y and Ca can refine the as-die-cast microstructure, result in the formation of Al2Ca phase and Al2Y phase, and inhibit the precipitation of Mg17Al12 phase. The combined addition of Y and small amount of Ca has little influence on the ambient temperature tensile properties, but increasing the content of Ca can improve significantly the tensile strength at both ambient and elevated temperatures. It is found that for AZ91-1Y-xCa alloy, the hardness and the elevated temperature tensile strength increase, while the elongation decreases with increasing the addition of Ca. The mechanism of mechanical properties improvement caused by the combined addition of Y and Ca was also discussed.展开更多
The microstructure, physical and mechanical, and chemical properties of micro-arc calcium phosphate （CAP） coatings deposited under different process voltages in the range of 150-400 V on the commercially pure titani...The microstructure, physical and mechanical, and chemical properties of micro-arc calcium phosphate （CAP） coatings deposited under different process voltages in the range of 150-400 V on the commercially pure titanium （Ti） and Ti-40%Nb （Ti-40Nb） （mass fraction） alloy were investigated by the SEM, TEM, XRD and EDX methods. The coating thickness, roughness, and sizes of structural elements were measured and showed similar linear character depending on the process voltage for the coatings on both substrates. SEM results showed the porous morphology with spherical shape structural elements and rough surface relief of the coatings. XRD and TEM studies exhibited the amorphous structure of the CaP coating. With increasing the process voltage to 300-400 V, the crystalline phases, such as CaHPO4 and β-Ca2P207, were formed onto the coatings. The annealing leads to the formation of complex poly-phase structure with crystalline phases： CaTi4（PO4）6, β-Ca2P2O7, TiP2O7, TiNb（PO4）3, TiO2, NbO2, and Nb2O5. The applied voltage and process duration in the ranges of 200-250 V and 5-10 min, respectively, revealed the coating formed on Ti and Ti-40Nb with optimal properties： thickness of 40-70μm, porosity of 20%-25%, roughness （Ra） of 2.5-5.0 μm, adhesion strength of 15-30 MPa, and Ca/P mole ratio of 0.5-0.7.展开更多
基金Project(2008T142) supported by the Innovation Team Program of Liaoning Provincial Department of Education of China
文摘A series of die casting heat-resistant magnesium alloys based on Mg-Al system were developed for automotive application by adding Y and various amounts of Ca. The mechanical properties and microstructures of die casting AZ91 alloy with combined addition of Y and Ca were investigated by optical microscopy, scanning electronic microscopy, X-ray diffractometry and mechanical property test. The results show that the combined addition of Y and Ca can refine the as-die-cast microstructure, result in the formation of Al2Ca phase and Al2Y phase, and inhibit the precipitation of Mg17Al12 phase. The combined addition of Y and small amount of Ca has little influence on the ambient temperature tensile properties, but increasing the content of Ca can improve significantly the tensile strength at both ambient and elevated temperatures. It is found that for AZ91-1Y-xCa alloy, the hardness and the elevated temperature tensile strength increase, while the elongation decreases with increasing the addition of Ca. The mechanism of mechanical properties improvement caused by the combined addition of Y and Ca was also discussed.
基金Project(III.23.2.5)supported by the Fundamental Research Program of the Siberian Branch of Russian Academy of SciencesProject(15-03-07659)supported by the Russian Foundation for Basic Research+1 种基金Project(CR16-22)supported by the China and Russia on the Implementation of Inter-governmental ScientificTechnological Cooperation Projects of the Notice(NSC foreign word[2012]No.269)
文摘The microstructure, physical and mechanical, and chemical properties of micro-arc calcium phosphate （CAP） coatings deposited under different process voltages in the range of 150-400 V on the commercially pure titanium （Ti） and Ti-40%Nb （Ti-40Nb） （mass fraction） alloy were investigated by the SEM, TEM, XRD and EDX methods. The coating thickness, roughness, and sizes of structural elements were measured and showed similar linear character depending on the process voltage for the coatings on both substrates. SEM results showed the porous morphology with spherical shape structural elements and rough surface relief of the coatings. XRD and TEM studies exhibited the amorphous structure of the CaP coating. With increasing the process voltage to 300-400 V, the crystalline phases, such as CaHPO4 and β-Ca2P207, were formed onto the coatings. The annealing leads to the formation of complex poly-phase structure with crystalline phases： CaTi4（PO4）6, β-Ca2P2O7, TiP2O7, TiNb（PO4）3, TiO2, NbO2, and Nb2O5. The applied voltage and process duration in the ranges of 200-250 V and 5-10 min, respectively, revealed the coating formed on Ti and Ti-40Nb with optimal properties： thickness of 40-70μm, porosity of 20%-25%, roughness （Ra） of 2.5-5.0 μm, adhesion strength of 15-30 MPa, and Ca/P mole ratio of 0.5-0.7.