Titanium alloys play an important role in aerospace and other fields.However,after precision forging and cold rolling process,some defects will appear on the subsurface of titanium alloy bars,thus reducing the surface...Titanium alloys play an important role in aerospace and other fields.However,after precision forging and cold rolling process,some defects will appear on the subsurface of titanium alloy bars,thus reducing the surface quality and precision of turning process.This study aimed at exploring the effect of crack defects on TC4 cutting.Firstly,the finite element cutting simulation model of TC4 material with crack defects was established in ABAQUS.Then,the cutting parameters such as cutting force,stress concentration,chip morphology,residual stress were obtained by changing the variables such as the size and height of crack defects.Finally,the turning experiment was carried out on centerless lathe.The results show that the cutting force changes abruptly when the defect position is located on the cutting path,the maximal stress occurs at the tip of the defect,and the mutation of stress value is more serious with the increase of defect size;the buckling deformation of chip morphology occurs and becomes less serious with the increase of the distance between the defect position and the workpiece surface;the surface residual stress near the defect is related to the stress when the tool is close to the defect,the larger defect size and the closer to the machined surface,the greater the residual stress.Therefore,under certain processing conditions,the TC4 material should avoid large size defects or increase the distance between defects and the machined surface,so as to obtain better and stable surface quality.展开更多
In order to study and analyze the stability of engineering rock mass under non-uniform triaxial stress and obtain the evolution mechanism of the whole process of fracture,a series of conventional triaxial compression ...In order to study and analyze the stability of engineering rock mass under non-uniform triaxial stress and obtain the evolution mechanism of the whole process of fracture,a series of conventional triaxial compression tests and three-dimensional numerical simulation tests were carried out on hollow granite specimens with different diameters.The bearing capacity of hollow cylindrical specimen is analyzed based on elasticity.The results show that:1)Under low confining pressure,the tensile strain near the hole of the hollow cylindrical specimen is obvious,and the specimen deformation near the hole is significant.At the initial stage of loading,the compressive stress and compressive strain of the specimen are widely distributed.With the progress of loading,the number of microelements subjected to tensile strain gradually increases,and even spreads throughout the specimen;2)Under conventional triaxial compression,the cracking position of hollow cylinder specimens is concentrated in the upper and lower parts,and the final fracture mode is generally compressive shear failure.The final fracture mode of complete specimen is generally tensile fracture.Under high confining pressure,the tensile cracks of the sample are concentrated in the upper and lower parts and are not connected,while the cracks of the upper and lower parts of the intact sample will expand and connect to form a fracture surface;3)In addition,the tensile crack widths of intact and hollow cylindrical specimens under low confining pressure are larger than those under high confining pressure.展开更多
An aluminum-based in-situ composites reinforced with Mg2Si and Si particles were produced by centrifugal casting A1-20Si-5Mg alloy. The microstructure of the composites was examined, and the effects of temperature on ...An aluminum-based in-situ composites reinforced with Mg2Si and Si particles were produced by centrifugal casting A1-20Si-5Mg alloy. The microstructure of the composites was examined, and the effects of temperature on fracture behavior of the composite were investigated. The results show that the average fraction of primary Si and Mg2Si particles in the composites is as high as 38%, and ultimate tensile strengths （UTS） of the composites first increase then decrease with the increase of test temperature. Microstructures of broken specimens show that both the particle fracture and the interface debonding affect the fracture behavior of the composites, and the interface debonding becomes the dominant fracture mechanism with increasing test temperature. Comparative results indicate that rich particles in the composites and excellent interface strength play great roles in enhancing tensile property by preventing the movement of dislocations.展开更多
In order to improve the in vitro fertilization rate of bovine, the effects of different sperm capacitation methods on fertilization were investigated. Total two treatments were designed： two-time centrifugation （C）...In order to improve the in vitro fertilization rate of bovine, the effects of different sperm capacitation methods on fertilization were investigated. Total two treatments were designed： two-time centrifugation （C）, and one-time centrifugation and swim-up method （CS）. The results showed that the cleavage rate in the C treatment group was （75.6±4.5）%, which showed no difference compared with that （（76.4±1.9）%） in the CS treatment group （P〉0.05）; there was also no significant dif- ference in blastocyst rate between the two treatment groups （（35.7±4.1）% vs. （36.3± 2.7）%, P〉0.05）. However, the CS treatment significantly saved the capacitation time in vitro.展开更多
基金supported by Key Research and Development Program of Shaanxi Province(No.2023-YBGY-386)Natural Science and Technology Fund General Program of Shaanxi Province(No.2021JM-599).
文摘Titanium alloys play an important role in aerospace and other fields.However,after precision forging and cold rolling process,some defects will appear on the subsurface of titanium alloy bars,thus reducing the surface quality and precision of turning process.This study aimed at exploring the effect of crack defects on TC4 cutting.Firstly,the finite element cutting simulation model of TC4 material with crack defects was established in ABAQUS.Then,the cutting parameters such as cutting force,stress concentration,chip morphology,residual stress were obtained by changing the variables such as the size and height of crack defects.Finally,the turning experiment was carried out on centerless lathe.The results show that the cutting force changes abruptly when the defect position is located on the cutting path,the maximal stress occurs at the tip of the defect,and the mutation of stress value is more serious with the increase of defect size;the buckling deformation of chip morphology occurs and becomes less serious with the increase of the distance between the defect position and the workpiece surface;the surface residual stress near the defect is related to the stress when the tool is close to the defect,the larger defect size and the closer to the machined surface,the greater the residual stress.Therefore,under certain processing conditions,the TC4 material should avoid large size defects or increase the distance between defects and the machined surface,so as to obtain better and stable surface quality.
基金Projects(52074116,51804113)supported by the National Natural Science Foundation of China。
文摘In order to study and analyze the stability of engineering rock mass under non-uniform triaxial stress and obtain the evolution mechanism of the whole process of fracture,a series of conventional triaxial compression tests and three-dimensional numerical simulation tests were carried out on hollow granite specimens with different diameters.The bearing capacity of hollow cylindrical specimen is analyzed based on elasticity.The results show that:1)Under low confining pressure,the tensile strain near the hole of the hollow cylindrical specimen is obvious,and the specimen deformation near the hole is significant.At the initial stage of loading,the compressive stress and compressive strain of the specimen are widely distributed.With the progress of loading,the number of microelements subjected to tensile strain gradually increases,and even spreads throughout the specimen;2)Under conventional triaxial compression,the cracking position of hollow cylinder specimens is concentrated in the upper and lower parts,and the final fracture mode is generally compressive shear failure.The final fracture mode of complete specimen is generally tensile fracture.Under high confining pressure,the tensile cracks of the sample are concentrated in the upper and lower parts and are not connected,while the cracks of the upper and lower parts of the intact sample will expand and connect to form a fracture surface;3)In addition,the tensile crack widths of intact and hollow cylindrical specimens under low confining pressure are larger than those under high confining pressure.
基金Project(51174244) supported by the National Natural Science Foundation of ChinaProject(CDJZR11130005) supported by the Fundamental Research Funds for the Central Universities,China
文摘An aluminum-based in-situ composites reinforced with Mg2Si and Si particles were produced by centrifugal casting A1-20Si-5Mg alloy. The microstructure of the composites was examined, and the effects of temperature on fracture behavior of the composite were investigated. The results show that the average fraction of primary Si and Mg2Si particles in the composites is as high as 38%, and ultimate tensile strengths （UTS） of the composites first increase then decrease with the increase of test temperature. Microstructures of broken specimens show that both the particle fracture and the interface debonding affect the fracture behavior of the composites, and the interface debonding becomes the dominant fracture mechanism with increasing test temperature. Comparative results indicate that rich particles in the composites and excellent interface strength play great roles in enhancing tensile property by preventing the movement of dislocations.
基金Supported by Earmarked Fund for China Agriculture(Beef and Yak)Research System(NYCYTX-38)Key Agriculture Research and Development Program of Qiqihar(NYGG-201524)~~
文摘In order to improve the in vitro fertilization rate of bovine, the effects of different sperm capacitation methods on fertilization were investigated. Total two treatments were designed： two-time centrifugation （C）, and one-time centrifugation and swim-up method （CS）. The results showed that the cleavage rate in the C treatment group was （75.6±4.5）%, which showed no difference compared with that （（76.4±1.9）%） in the CS treatment group （P〉0.05）; there was also no significant dif- ference in blastocyst rate between the two treatment groups （（35.7±4.1）% vs. （36.3± 2.7）%, P〉0.05）. However, the CS treatment significantly saved the capacitation time in vitro.