The amplitude-dependent and temperature-dependent low frequency damping capacities of magnesium with 99.96% purity were studied by a dynamic mechanical analyzer. The pure magnesium alloys include CPM1 and CPM2 casting...The amplitude-dependent and temperature-dependent low frequency damping capacities of magnesium with 99.96% purity were studied by a dynamic mechanical analyzer. The pure magnesium alloys include CPM1 and CPM2 castings having textures of columnar grains which extraordinarily influence the damping behaviours. The commercial pure magnesium alloy CPM was re-melted to obtain equiaxed grains, which could remove the effect of texture orientation on the damping behaviours of these pure magnesium alloys. The results of strain amplitude-dependent damping spectrums of these pure magnesium alloys show that the pure magnesium with equiaxed grains possesses the highest damping capacity. In temperature-dependent damping plot for all these three pure magnesium alloys, there are two damping peaks P1 and P2 located at 80 and 230 °C, respectively. These two damping peaks are considered to be caused by the interaction between dislocation and point defects, and the movement of grain boundaries, respectively.展开更多
The microstructure and mechanical properties of Mg-10.1Gd-3.74Y-0.25Zr （mass fraction, %） alloy （GW104 alloy） cast by metal mould casting （MMC） and lost foam casting （LFC） were evaluated, respectively. It is r...The microstructure and mechanical properties of Mg-10.1Gd-3.74Y-0.25Zr （mass fraction, %） alloy （GW104 alloy） cast by metal mould casting （MMC） and lost foam casting （LFC） were evaluated, respectively. It is revealed that different forming modes do not influence the phase composition of as-cast alloy. In the as-cast specimens, the microstructures are similar and composed of α-Mg solid solution, eutectic compound of α-Mg＋Mg 24 （Gd, Y） 5 and cuboid-shaped Mg 5 （Gd, Y） phase; whereas the average grain size of the alloy produced by metal mould casting is smaller than that by lost foam casting. The eutectic compound of the alloy is completely dissolved after solution treatment at 525 ℃for 6 h, while the Mg 5 （Gd, Y） phase still exists after solution treatment. After peak-ageing, the lost foam cast alloy exhibits the maximum ultimate tensile strength of 285 MPa, and metal mould cast specimen 325 MPa at room temperature, while the tensile yield strengths of them are comparable. It can be concluded that GW104 alloy cast by lost foam casting possesses similar microstructure and evidently lower mechanical strength compared with metal mould cast alloy, due to slow solidification rate and proneness to form shrinkage porosities during lost foam casting process.展开更多
Mg-6Al-0.3Mn-xY(x=0,0.3,0.6 and 0.9,mass fraction,%) magnesium alloys were prepared by casting and hot rolling process.The influence of yttrium on microstructure and tensile mechanical properties of the AM60 magnesium...Mg-6Al-0.3Mn-xY(x=0,0.3,0.6 and 0.9,mass fraction,%) magnesium alloys were prepared by casting and hot rolling process.The influence of yttrium on microstructure and tensile mechanical properties of the AM60 magnesium alloy was investigated.The results reveal that with increasing the yttrium content,Al2Y precipitates form and the grain size is reduced.The ultimate strength,yield strength and elongation at room temperature are 192 MPa,62 MPa and 12.6%,respectively,for the as-cast Mg-6Al-0.3Mn-0.9Y alloy.All these properties are improved obviously by hot rolling,and the values are up to 303 MPa,255 MPa and 17.1%,respectively,for the rolled Mg-6Al-0.3Mn-0.9Y alloy.The improvement of mechanical properties is attributed to continuous dynamic recrystallization and the existence of highly thermal stable Al2Y precipitate which impedes the movement of dislocation effectively.展开更多
Through the research on stress metamorphism character of the II1 coal seam in Ludian gliding structure, the stress effecting factors of metamorphism and hydrocarbon generation process of tectonic coal were studied. It...Through the research on stress metamorphism character of the II1 coal seam in Ludian gliding structure, the stress effecting factors of metamorphism and hydrocarbon generation process of tectonic coal were studied. It is shown that different tectonic stress has different coal evolution effects. Compared with tensional stress, compressive stress, which has apparent anisotropic characteristics, has greater stimulative effect against the increase of coal metamorphic degree, the abscission of functional group and side chains of basic structural unit, and the formation of gas primarily composed of methane.展开更多
To investigate the seismic behavior of autoclaved aerated concrete load-bearing masonry wall(AACLMW), a piece of control block wall without constructional measures and five pieces of block walls with different constru...To investigate the seismic behavior of autoclaved aerated concrete load-bearing masonry wall(AACLMW), a piece of control block wall without constructional measures and five pieces of block walls with different constructional measures were tested under low reversed cyclic loading which imitated low to moderate earthquake force. The seismic behavior of AACLMW with different constructional measures in terms of failure mode, hysteretic curve, deformation capacity and displacement ductility was studied and compared with that without constructional measures. The experimental results indicate that the constructional measures comprising constructional columns and horizontal concrete strips are effective for improving the seismic behavior of AACLMW. The study in this paper can provide a reliable experimental basis for further analysis and engineering application of AACLMW in the future.展开更多
In-situ titanium matrix composites with N content of 0. 045-0. 27 wt% have been produced by a easting method. The microstructure and mechanical properties of as-cast materials have been observed and tested. The result...In-situ titanium matrix composites with N content of 0. 045-0. 27 wt% have been produced by a easting method. The microstructure and mechanical properties of as-cast materials have been observed and tested. The results show that when N content in Ti-6Al alloy is between 0. 045 wt% and 0. 27 wt%, the reinforcement is a compound of Ti, Al and N, and volume fraction of reinforcements increases with an increase of N content. The hardness, compressive strength and elastic modulus are all higher than that of the matrix alloy. With the increase of N content, the compressive strength, the hardness and the elastic modulus increase. Fracture surface analysis has also shown that the matrix alloy fractures in a ductile model and the composites fracture in a cleavage brittle model with characteristics of dimple and cleavage surface.展开更多
基金Project (50801017) supported by the National Natural Science Foundation of Chinaproject (20080440843) supported by Postdoctoral Science Foundation, ChinaProject (HIT.NSRIF.2009028) supported by the Natural Scientific Research Innovation Foundation of Harbin Institute of Technology, China
文摘The amplitude-dependent and temperature-dependent low frequency damping capacities of magnesium with 99.96% purity were studied by a dynamic mechanical analyzer. The pure magnesium alloys include CPM1 and CPM2 castings having textures of columnar grains which extraordinarily influence the damping behaviours. The commercial pure magnesium alloy CPM was re-melted to obtain equiaxed grains, which could remove the effect of texture orientation on the damping behaviours of these pure magnesium alloys. The results of strain amplitude-dependent damping spectrums of these pure magnesium alloys show that the pure magnesium with equiaxed grains possesses the highest damping capacity. In temperature-dependent damping plot for all these three pure magnesium alloys, there are two damping peaks P1 and P2 located at 80 and 230 °C, respectively. These two damping peaks are considered to be caused by the interaction between dislocation and point defects, and the movement of grain boundaries, respectively.
基金Project(2007CB613704)supported by the National Basic Research Program of China
文摘The microstructure and mechanical properties of Mg-10.1Gd-3.74Y-0.25Zr （mass fraction, %） alloy （GW104 alloy） cast by metal mould casting （MMC） and lost foam casting （LFC） were evaluated, respectively. It is revealed that different forming modes do not influence the phase composition of as-cast alloy. In the as-cast specimens, the microstructures are similar and composed of α-Mg solid solution, eutectic compound of α-Mg＋Mg 24 （Gd, Y） 5 and cuboid-shaped Mg 5 （Gd, Y） phase; whereas the average grain size of the alloy produced by metal mould casting is smaller than that by lost foam casting. The eutectic compound of the alloy is completely dissolved after solution treatment at 525 ℃for 6 h, while the Mg 5 （Gd, Y） phase still exists after solution treatment. After peak-ageing, the lost foam cast alloy exhibits the maximum ultimate tensile strength of 285 MPa, and metal mould cast specimen 325 MPa at room temperature, while the tensile yield strengths of them are comparable. It can be concluded that GW104 alloy cast by lost foam casting possesses similar microstructure and evidently lower mechanical strength compared with metal mould cast alloy, due to slow solidification rate and proneness to form shrinkage porosities during lost foam casting process.
基金Projects(2006BA104B04-1,2006BAE04B07-3) supported by the National Science and Technology Supporting Program of ChinaProject (2007KZ05) supported by the Science and Technology Supporting Program of Changchun City, ChinaProject supported by "985 Program" of Jilin University,China
文摘Mg-6Al-0.3Mn-xY(x=0,0.3,0.6 and 0.9,mass fraction,%) magnesium alloys were prepared by casting and hot rolling process.The influence of yttrium on microstructure and tensile mechanical properties of the AM60 magnesium alloy was investigated.The results reveal that with increasing the yttrium content,Al2Y precipitates form and the grain size is reduced.The ultimate strength,yield strength and elongation at room temperature are 192 MPa,62 MPa and 12.6%,respectively,for the as-cast Mg-6Al-0.3Mn-0.9Y alloy.All these properties are improved obviously by hot rolling,and the values are up to 303 MPa,255 MPa and 17.1%,respectively,for the rolled Mg-6Al-0.3Mn-0.9Y alloy.The improvement of mechanical properties is attributed to continuous dynamic recrystallization and the existence of highly thermal stable Al2Y precipitate which impedes the movement of dislocation effectively.
文摘Through the research on stress metamorphism character of the II1 coal seam in Ludian gliding structure, the stress effecting factors of metamorphism and hydrocarbon generation process of tectonic coal were studied. It is shown that different tectonic stress has different coal evolution effects. Compared with tensional stress, compressive stress, which has apparent anisotropic characteristics, has greater stimulative effect against the increase of coal metamorphic degree, the abscission of functional group and side chains of basic structural unit, and the formation of gas primarily composed of methane.
基金Supported by Science and Technology Development Program of Tianjin(No.033112311)
文摘To investigate the seismic behavior of autoclaved aerated concrete load-bearing masonry wall(AACLMW), a piece of control block wall without constructional measures and five pieces of block walls with different constructional measures were tested under low reversed cyclic loading which imitated low to moderate earthquake force. The seismic behavior of AACLMW with different constructional measures in terms of failure mode, hysteretic curve, deformation capacity and displacement ductility was studied and compared with that without constructional measures. The experimental results indicate that the constructional measures comprising constructional columns and horizontal concrete strips are effective for improving the seismic behavior of AACLMW. The study in this paper can provide a reliable experimental basis for further analysis and engineering application of AACLMW in the future.
文摘In-situ titanium matrix composites with N content of 0. 045-0. 27 wt% have been produced by a easting method. The microstructure and mechanical properties of as-cast materials have been observed and tested. The results show that when N content in Ti-6Al alloy is between 0. 045 wt% and 0. 27 wt%, the reinforcement is a compound of Ti, Al and N, and volume fraction of reinforcements increases with an increase of N content. The hardness, compressive strength and elastic modulus are all higher than that of the matrix alloy. With the increase of N content, the compressive strength, the hardness and the elastic modulus increase. Fracture surface analysis has also shown that the matrix alloy fractures in a ductile model and the composites fracture in a cleavage brittle model with characteristics of dimple and cleavage surface.