IrO2-TiO2 thin films were prepared by atomic layer deposition using Ir（EtCp）（COD） and titanium isopropoxide （TTIP）. The resistivity of IrO2-TiO2 thin films can be easily controlled from 1 500 to 356.7 μΩ·...IrO2-TiO2 thin films were prepared by atomic layer deposition using Ir（EtCp）（COD） and titanium isopropoxide （TTIP）. The resistivity of IrO2-TiO2 thin films can be easily controlled from 1 500 to 356.7 μΩ·cm by the IrO2 intermixing ratio from 0.55 to 0.78 in the IrO2-TiO2 thin films. The low temperature coefficient of resistance（TCR） values can be obtained by adopting IrO2-TiO2 composite thin films. Moreover, the change in the resistivity of IrO2-TiO2 thin films was below 10% even after O2 annealing process at 600 ℃. The step stress test results show that IrO2-TiO2 films have better characteristics than conventional TaN08 heater resistor. Therefore, IrO2-TiO2 composite thin films can be used as a heater resistor material in thermal inkjet printhead.展开更多
Three-dimensional(3 D)printing has had a large impact on various fields,with fused deposition modeling(FDM)being the most versatile and cost-effective 3 D printing technology.However,FDM often requires sacrificial sup...Three-dimensional(3 D)printing has had a large impact on various fields,with fused deposition modeling(FDM)being the most versatile and cost-effective 3 D printing technology.However,FDM often requires sacrificial support structures,which significantly complicates the processing and increases the cost.Furthermore,poor layer-to-layer adhesion greatly affects the mechanical stability of 3D-printed objects.Here,we present a new Print-Healing strategy to address the aforementioned challenges.A polymer ink(Cu-DOU-CPU)with synergetic triple dynamic bonds was developed to have excellent printability and room-temperature self-healing ability.Objects with various shapes were printed using a simple compact 3D printer,and readily assembled into large sophisticated architectures via self-healing.Triple dynamic bonds induce strong binding between layers.Additionally,damaged printed objects can spontaneously heal,which significantly elongates their service life.This work paves a simple and powerful way to solve the key bottlenecks in FDM 3D printing,and will have diverse applications.展开更多
基金supported by a grant from the Fundamental R&D Program for Core Technology of Materials funded by the Ministry of Knowledge Economy, Republic of Koreasupported by Basic Science Research program through the National Research Foundation of Korea (NRF) funded by the Ministry of Education, Science and Technology (2010-0001-226)
文摘IrO2-TiO2 thin films were prepared by atomic layer deposition using Ir（EtCp）（COD） and titanium isopropoxide （TTIP）. The resistivity of IrO2-TiO2 thin films can be easily controlled from 1 500 to 356.7 μΩ·cm by the IrO2 intermixing ratio from 0.55 to 0.78 in the IrO2-TiO2 thin films. The low temperature coefficient of resistance（TCR） values can be obtained by adopting IrO2-TiO2 composite thin films. Moreover, the change in the resistivity of IrO2-TiO2 thin films was below 10% even after O2 annealing process at 600 ℃. The step stress test results show that IrO2-TiO2 films have better characteristics than conventional TaN08 heater resistor. Therefore, IrO2-TiO2 composite thin films can be used as a heater resistor material in thermal inkjet printhead.
基金supported by the National Natural Science Foundation of China(21991123,52073049 and 51703148)the Natural Science Foundation of Shanghai(20ZR1402500 and18ZR1401900)+4 种基金the Belt&Road Young Scientist Exchanges Project of Science and Technology Commission Foundation of Shanghai(20520741000)Shanghai Belt and Road Joint Laboratory of Advanced Fiber and Low-dimension Materials(Donghua University(DHU),18520750400)the Fundamental Research Funds for the Central UniversitiesDHU Distinguished Young Professor Program(LZA2019001)the Open Research Fund of Shanghai Center for High-performance Fibers and Composites and the Center for Civil Aviation Composites of Donghua University。
文摘Three-dimensional(3 D)printing has had a large impact on various fields,with fused deposition modeling(FDM)being the most versatile and cost-effective 3 D printing technology.However,FDM often requires sacrificial support structures,which significantly complicates the processing and increases the cost.Furthermore,poor layer-to-layer adhesion greatly affects the mechanical stability of 3D-printed objects.Here,we present a new Print-Healing strategy to address the aforementioned challenges.A polymer ink(Cu-DOU-CPU)with synergetic triple dynamic bonds was developed to have excellent printability and room-temperature self-healing ability.Objects with various shapes were printed using a simple compact 3D printer,and readily assembled into large sophisticated architectures via self-healing.Triple dynamic bonds induce strong binding between layers.Additionally,damaged printed objects can spontaneously heal,which significantly elongates their service life.This work paves a simple and powerful way to solve the key bottlenecks in FDM 3D printing,and will have diverse applications.