制备了添加少量B2O3和P2O5后的Fe2O3 CaO SiO2体系铁磁微晶玻璃,并进行了微观结构分析、XRD分析、磁性检测以及生理模拟液的浸泡实验.实验结果表明,制备的微晶玻璃材料同时具备磁性和生物活性这两种重要性能.不经过核化处理在1000℃晶...制备了添加少量B2O3和P2O5后的Fe2O3 CaO SiO2体系铁磁微晶玻璃,并进行了微观结构分析、XRD分析、磁性检测以及生理模拟液的浸泡实验.实验结果表明,制备的微晶玻璃材料同时具备磁性和生物活性这两种重要性能.不经过核化处理在1000℃晶化2h后能够获得较理想的磁铁矿主晶相和硅灰石次晶相均匀致密分布的微观组织,所得微晶玻璃具有最佳的磁性能.铁含量提高能够增加微晶玻璃的磁性,然而会抑制微晶玻璃表面羟基磷灰石的形成,从而降低其生物活性.展开更多
Three water-soluble β-alanine C 60 adducts with different addition numbers, C 60(NHCH 2CH 2COONa) nH n(n=1,5,9), were synthesized. The products were characterized by FTIR, 1H NMR and elemental analysis. The antioxida...Three water-soluble β-alanine C 60 adducts with different addition numbers, C 60(NHCH 2CH 2COONa) nH n(n=1,5,9), were synthesized. The products were characterized by FTIR, 1H NMR and elemental analysis. The antioxidant activity of these C 60 adducts as the quencher for superoxide anion radical O -· 2 was evaluated by chemiluminescence in the system of pyrogallol-luminol. The results indicate that the three C 60 derivatives are all excellent quencher for superoxide anion radical O -· 2. The concentrations of 50% inhibition are 252, 140, 112 μmol/L respectively. This high efficiency should be attributed to many factors such as the numbers of remaining double bonds, donor effect of amino group and steric effect. However, the above results also suggest the effect of the adducted β-alanine groups is predominated in this system.展开更多
The complex [Cd(tren)(meim)](ClO4)2 was synthesized and characterized by elemental analysis, IR and X-ray single-crystal diffraction. The compound crystallizes in monoclinic system, space group P21/m with a=0.786 8(2)...The complex [Cd(tren)(meim)](ClO4)2 was synthesized and characterized by elemental analysis, IR and X-ray single-crystal diffraction. The compound crystallizes in monoclinic system, space group P21/m with a=0.786 8(2) nm, b=0.834 2(2) nm, c=1.496 2(4) nm, Mr=538.64, Z=2, F(000)=542, Dc=1.822 g·cm-3, T=298(2) K, μ=1.435 mm-1 and λ=0.071 073 nm. The structure was refined to R=0.045 8 and wR=0.123 1 for 1 489 observed reflections with I>2σ(I). The complex was valued for its antimicrobial activity against bacterial strands using the agar diffusion method. It was found to be active against the four test bacterial organisms. CCDC: 600198.展开更多
文摘制备了添加少量B2O3和P2O5后的Fe2O3 CaO SiO2体系铁磁微晶玻璃,并进行了微观结构分析、XRD分析、磁性检测以及生理模拟液的浸泡实验.实验结果表明,制备的微晶玻璃材料同时具备磁性和生物活性这两种重要性能.不经过核化处理在1000℃晶化2h后能够获得较理想的磁铁矿主晶相和硅灰石次晶相均匀致密分布的微观组织,所得微晶玻璃具有最佳的磁性能.铁含量提高能够增加微晶玻璃的磁性,然而会抑制微晶玻璃表面羟基磷灰石的形成,从而降低其生物活性.
文摘Three water-soluble β-alanine C 60 adducts with different addition numbers, C 60(NHCH 2CH 2COONa) nH n(n=1,5,9), were synthesized. The products were characterized by FTIR, 1H NMR and elemental analysis. The antioxidant activity of these C 60 adducts as the quencher for superoxide anion radical O -· 2 was evaluated by chemiluminescence in the system of pyrogallol-luminol. The results indicate that the three C 60 derivatives are all excellent quencher for superoxide anion radical O -· 2. The concentrations of 50% inhibition are 252, 140, 112 μmol/L respectively. This high efficiency should be attributed to many factors such as the numbers of remaining double bonds, donor effect of amino group and steric effect. However, the above results also suggest the effect of the adducted β-alanine groups is predominated in this system.
文摘The complex [Cd(tren)(meim)](ClO4)2 was synthesized and characterized by elemental analysis, IR and X-ray single-crystal diffraction. The compound crystallizes in monoclinic system, space group P21/m with a=0.786 8(2) nm, b=0.834 2(2) nm, c=1.496 2(4) nm, Mr=538.64, Z=2, F(000)=542, Dc=1.822 g·cm-3, T=298(2) K, μ=1.435 mm-1 and λ=0.071 073 nm. The structure was refined to R=0.045 8 and wR=0.123 1 for 1 489 observed reflections with I>2σ(I). The complex was valued for its antimicrobial activity against bacterial strands using the agar diffusion method. It was found to be active against the four test bacterial organisms. CCDC: 600198.