The ice melting performance of three types of deicers, including sodium chloride, calcium chloride and sodium acetate, were tested in laboratory under different temperature conditions, and their effects on asphalt mix...The ice melting performance of three types of deicers, including sodium chloride, calcium chloride and sodium acetate, were tested in laboratory under different temperature conditions, and their effects on asphalt mixture were evaluated from the point of the stripping resistance of asphalt mixture. Unsaturated Marshall samples were exposed to freeze-thaw cycling while immersed in the deicer solutions of different concentrations. After the freeze-thaw cycles, Cantabro tests were performed, and Cantabro loss was adopted to characterize the stripping resistance of asphalt mixture. The test results show that calcium chloride has the best comprehensive ice melting performance, and all deicers have detrimental effect on the stripping resistance of asphalt mixture at different degrees. The damage degree depends on deicer types and their concentration in the solution. Deicer solutions with about 2% concentration cause the greatest loss of stripping resistance due to serious freeze-thaw damage. Sodium acetate causes greater loss of stripping resistance than sodium chloride and calcium chloride at the same concentration.展开更多
基金The Specialized Research Fund for the Doctoral Program of Higher Education of China(No.20120092110053)
文摘The ice melting performance of three types of deicers, including sodium chloride, calcium chloride and sodium acetate, were tested in laboratory under different temperature conditions, and their effects on asphalt mixture were evaluated from the point of the stripping resistance of asphalt mixture. Unsaturated Marshall samples were exposed to freeze-thaw cycling while immersed in the deicer solutions of different concentrations. After the freeze-thaw cycles, Cantabro tests were performed, and Cantabro loss was adopted to characterize the stripping resistance of asphalt mixture. The test results show that calcium chloride has the best comprehensive ice melting performance, and all deicers have detrimental effect on the stripping resistance of asphalt mixture at different degrees. The damage degree depends on deicer types and their concentration in the solution. Deicer solutions with about 2% concentration cause the greatest loss of stripping resistance due to serious freeze-thaw damage. Sodium acetate causes greater loss of stripping resistance than sodium chloride and calcium chloride at the same concentration.